INTRODUCTION TO ION IMPLANTATION Dr. Lynn Fuller, Dr. Renan Turkman Dr Robert Pearson

Similar documents
How To Implant Anneal Ion Beam

Principles of Ion Implant

Semiconductor doping. Si solar Cell

Graduate Student Presentations

Conductivity of silicon can be changed several orders of magnitude by introducing impurity atoms in silicon crystal lattice.

Vacuum Evaporation Recap

Etching Etch Definitions Isotropic Etching: same in all direction Anisotropic Etching: direction sensitive Selectivity: etch rate difference between

Solar Photovoltaic (PV) Cells

ELEC 3908, Physical Electronics, Lecture 15. BJT Structure and Fabrication

Lezioni di Tecnologie e Materiali per l Elettronica

Introduction to VLSI Fabrication Technologies. Emanuele Baravelli

Lecture#20 Ion Implant for ULSI

A Plasma Doping Process for 3D FinFET Source/ Drain Extensions

Damage-free, All-dry Via Etch Resist and Residue Removal Processes

AN900 APPLICATION NOTE

Lecture 12. Physical Vapor Deposition: Evaporation and Sputtering Reading: Chapter 12. ECE Dr. Alan Doolittle

Solid State Detectors = Semi-Conductor based Detectors

Module 7 Wet and Dry Etching. Class Notes

Coating Technology: Evaporation Vs Sputtering

Advanced VLSI Design CMOS Processing Technology

Lecture 030 DSM CMOS Technology (3/24/10) Page 030-1

Sheet Resistance = R (L/W) = R N L

Chapter 11 PVD and Metallization

Dry Etching and Reactive Ion Etching (RIE)

Secondary Ion Mass Spectrometry

Chapter 5: Diffusion. 5.1 Steady-State Diffusion

Chapter 5. Second Edition ( 2001 McGraw-Hill) 5.6 Doped GaAs. Solution

Contamination. Cleanroom. Cleanroom for micro and nano fabrication. Particle Contamination and Yield in Semiconductors.

Improved Contact Formation for Large Area Solar Cells Using the Alternative Seed Layer (ASL) Process

Chemical Sputtering. von Kohlenstoff durch Wasserstoff. W. Jacob

Figure Process flow from starting material to polished wafer.

Fabrication and Characterization of N- and P-Type a-si:h Thin Film Transistors

h e l p s y o u C O N T R O L

Ion Beam Sputtering: Practical Applications to Electron Microscopy

MOS (metal-oxidesemiconductor) 李 2003/12/19

Results Overview Wafer Edge Film Removal using Laser

ISOTROPIC ETCHING OF THE SILICON NITRIDE AFTER FIELD OXIDATION.

ELG4126: Photovoltaic Materials. Based Partially on Renewable and Efficient Electric Power System, Gilbert M. Masters, Wiely

Electron Beam and Sputter Deposition Choosing Process Parameters

III. Wet and Dry Etching

Modification of Pd-H 2 and Pd-D 2 thin films processed by He-Ne laser

The MOSFET Transistor

Understanding the p-n Junction by Dr. Alistair Sproul Senior Lecturer in Photovoltaics The Key Centre for Photovoltaic Engineering, UNSW

Study of tungsten oxidation in O 2 /H 2 /N 2 downstream plasma

Types of Epitaxy. Homoepitaxy. Heteroepitaxy

CRYSTAL DEFECTS: Point defects

Implementation Of High-k/Metal Gates In High-Volume Manufacturing

Short overview of TEUFEL-project

Coating Thickness and Composition Analysis by Micro-EDXRF

Wafer Manufacturing. Reading Assignments: Plummer, Chap 3.1~3.4

The Physics of Energy sources Renewable sources of energy. Solar Energy

High power picosecond lasers enable higher efficiency solar cells.

Neuere Entwicklungen zur Herstellung optischer Schichten durch reaktive. Wolfgang Hentsch, Dr. Reinhard Fendler. FHR Anlagenbau GmbH

. Tutorial #3 Building Complex Targets

Modification of Graphene Films by Laser-Generated High Energy Particles

Chapter 2 The Study on Polycrystalline Pentacene Thin Film Transistors

VLSI Fabrication Process

Process simulation. Maria Concetta Allia

Lecture 2 - Semiconductor Physics (I) September 13, 2005

Silicon, the test mass substrate of tomorrow? Jerome Degallaix The Next Detectors for Gravitational Wave Astronomy Beijing

How To Analyze Plasma With An Inductively Coupled Plasma Mass Spectrometer

OLED display. Ying Cao

NEUTRON TRANSMUTATION DOPED (NTD) SILICON FOR HIGH POWER ELECTRONICS

Lecture 11. Etching Techniques Reading: Chapter 11. ECE Dr. Alan Doolittle

TOF FUNDAMENTALS TUTORIAL

Sample Exercise 12.1 Calculating Packing Efficiency

Fabrication and Manufacturing (Basics) Batch processes

Cathode Ray Tube. Introduction. Functional principle

CONTENTS. Preface Energy bands of a crystal (intuitive approach)

Silicon Sensors for CMS Tracker at High-Luminosity Environment - Challenges in particle detection -

Radiation Enhanced Diffusion of Nickel in Silicon Diodes

3. Diodes and Diode Circuits. 3. Diodes and Diode Circuits TLT-8016 Basic Analog Circuits 2005/2006 1

Spectroscopic Ellipsometry:

A Remote Plasma Sputter Process for High Rate Web Coating of Low Temperature Plastic Film with High Quality Thin Film Metals and Insulators

The HEMP Thruster - An Alternative to Conventional Ion Sources?

13C NMR Spectroscopy

The Periodic Table: Periodic trends

Nanometer-scale imaging and metrology, nano-fabrication with the Orion Helium Ion Microscope

Development of New Inkjet Head Applying MEMS Technology and Thin Film Actuator

Displays. Cathode Ray Tube. Semiconductor Elements. Basic applications. Oscilloscope TV Old monitors. 2009, Associate Professor PhD. T.

The Focused Ion Beam Scanning Electron Microscope: A tool for sample preparation, two and three dimensional imaging. Jacob R.

Characteristic curves of a solar cell

Modern Physics Laboratory e/m with Teltron Deflection Tube

PHOTOELECTRIC EFFECT AND DUAL NATURE OF MATTER AND RADIATIONS

Low-cost Printed Electronic Nose Gas Sensors for Distributed Environmental Monitoring

FUNDAMENTAL PROPERTIES OF SOLAR CELLS

Defect Engineering in Semiconductors

Ultra-High Density Phase-Change Storage and Memory

Wafer-based silicon PV technology Status, innovations and outlook

Solid-State Physics: The Theory of Semiconductors (Ch ) SteveSekula, 30 March 2010 (created 29 March 2010)

Silicon-On-Glass MEMS. Design. Handbook

Defects Introduction. Bonding + Structure + Defects. Properties

FEATURE ARTICLE. Figure 1: Current vs. Forward Voltage Curves for Silicon Schottky Diodes with High, Medium, Low and ZBD Barrier Heights

For Touch Panel and LCD Sputtering/PECVD/ Wet Processing

Etching and Pattern Transfer (1) OUTLINE J / 3.155J -- Spring Term 2005 Lecture 12 - Etch and Pattern Transfer I (Wet Etch) 1.

Photovoltaics photo volt Photovoltaic Cells Crystalline Silicon Cells Photovoltaic Systems

Photolithography. Class: Figure Various ways in which dust particles can interfere with photomask patterns.

SEMICONDUCTOR I: Doping, semiconductor statistics (REF: Sze, McKelvey, and Kittel)

Chapter 7-1. Definition of ALD

Transcription:

Ion Implantation ROCHESTER INSTITUTE OF TECHNOLOGY MICROELECTRONIC ENGINEERING INTRODUCTION TO ION IMPLANTATION Dr. Lynn Fuller, Dr. Renan Turkman Dr Robert Pearson Webpage: http://people.rit.edu/lffeee 82 Lomb Memorial Drive Rochester, NY 14623-5604 Tel (585) 475-2035 Fax (585) 475-5041 Email: Lynn.Fuller@rit.edu Department webpage: http://www.microe.rit.edu 1-20-12 implant.ppt Page 1

VARIAN 400 & 120-10 ION IMPLANTERS Varian 120-10 Varian 400 Page 2

VARIAN 350 D ION IMPLANTER (4 AND 6 WAFERS) Page 3

OUTLINE Principles of Ion Implantation Generate a focused beam of ions to be implanted (B +, P + or As + ) Accelerate the ions Scan the ion beam over the wafer Implant dose Ion Implantation Equipment Plasma source and ion extraction Ion selection Accelerating column End station Low and high (beam) current implanters Page 4

OUTLINE Implanted Dopant Profiles Dopant ion-substrate interactions Post implant anneal Dopant concentration profiles Implanted Dopant Profiles (continued) Channeling Implanting through thin film layers (e.g. oxide) Masking against ion implants Page 5

INTRODUCTION Ion implant is used to put specific amounts of n-type and p-type dopants (Dose) into a semiconductor. The dose is accurately measured during implantation giving outstanding control and repeatability. Specific regions can be implanted using a variety of masking materials including photoresist. Ion implantation is basically a low temperature process. Ion implant can deliver lower doses than chemical doping (predeposit). Dose can be as low as 10 11 /cm 2 In today's advanced integrated circuits ion implantation is used for all doping applications. (with a few exceptions) Page 6

BASICS F = qe + q ( v x B ) Example 1: Example 2: vy + v v B w/m2 + vx + Page 7

GENERATION OF A DOPANT GAS PLASMA Source Gas Molecule + e Dopant Ion + (Other Atoms, Molecules and/or Radicals) + e + e Example : Boron Trifluoride as B source BF 3 + e B + + F 2 + F + e + e Other dissociative ionizations result in the generation of B 10+,F +, BF 2 + The dopant ion sources commonly used in silicon processing are boron trifluoride BF 3, phosphine PH 3, arsenic pentafluoride AsF 5, arsine AsH 3. Page 8

PLASMA SOURCE AND ION EXTRACTION BF3 Gas feed Solenoid N BF3 e B+ e BF2+ Plasma Chamber mt level pressure M v 2 / 2 = q Vext (positive) ions Arc Voltage To pump S V extraction ( variable, typically ~30 KV ) ν = 2qVext m v 19 ( 2)( 1.6x10 ) ( 30, 000) 27 ( 11)( 1.67x10 ) = = 7.23x10 5 m s Page 9

TYPICAL SOURCE SET UP Pressure 30mT Extraction Voltage 33 KV Extraction Current 0.8 ma Arc Voltage 2000 V Arc Current 50 ma Filament Current 150 A Filament Voltage 20 V Solenoid Current 3.0 A Source Cabinet for Varian 120-10 Page 10

NIELSEN-TYPE GASEOUS SOURCE Solenoid Magnet (wraps around) neutrals Gas inlet + e - + Filament Extraction Outlet + + Velocity - v Anode Electrons boil off the filament and ionize the gas. Solenoid make electrons follow a spiral path increasing ionization Page 11

SELECTION OF THE IONS TO BE IMPLANTED The ions are extracted from the source and analyzed in a magnetic field. The Lorentz force makes the ions take a curved path with a radius of curvature that depends on the mass of each ionic species. By adjusting the magnetic field strength, only the selected ions will enter the accelerating column. Ions Extracted from Source N S Light Ions Heavy Ions Analyzing Magnet Selected Ions Page 12

ION SELECTION - ANALYZING MAGNET Lorentz = Centripetal Force force q (ν xb) = M ν 2 / R R=M ν / q B ν = 2qVext m B Magnetic Field v : ion velocity R: radius of curvature R Resolving Aperture Selected ions Heavier ions Mass to charge ratio, M / q of the selected ions: M /q = R 2 B 2 / (2 Vext) R is fixed, B and Vext are variable Page 13

MAGNETIC SCAN COIL IN VARIAN 120-10 Scan Magnet to give X-scan Analyzing Magnet for mass spectrometer (Ion Selection) Page 14

PH 3 GAS SPECTRUM 100 Phosphorus - 31 Hydrogen - 1 P 31+ Beam Current (ma) PH + PH + 2 PH + 3 1 2 3 12 18 31 62 Ion Atomic Mass Units (AMU) Page 15

BF 3 GAS SPECTRUM 100 Boron - 11 Fluorine - 19 BF 2 + Beam Current (ma) B 10+ B 11+ B10 (F) + 2 F + BF + 1011 19 30 48 49 Ion Atomic Mass Units (AMU) Page 16

ACCELERATING COLUMN µτ level pressure E field Resolving Aperture Vacc Column length = 3 Ground Final Kinetic Energy of the Ion = q ( V ext + V acc ) Example: V ext = 30 KV V acc = 70 KV Energy of the Ion= E= 100 KeV Page 17

ACCELERATION OF THE IONS An acceleration voltage is applied across the column giving the ions their final kinetic energy. This voltage should be adjustable. This shows 14 equal acceleration plates. If the desired acceleration was 70KeV each section would contribute 5000 volts for example. Page 18

VARIAN 400 ACCELERATION HARDWARE Page 19

BF2 IMPLANTS Boron mass = 11 Fluorine mass = 19 BF2 mass = 49 The energy divides by mass so 100 KeV BF2 is equivalent to 22.4 KeV B11 implant BF2 peak is larger than B11 peak giving more current and shorter time for large dose implants BF2 can give shallow implants BF2 reduces channeling (explained in following pages) Page 20

SCANNING THE BEAM Scanning of the beam The focused ion beam is scanned over the wafer in a highly controlled manner in order to achieve uniform doping. Either the wafer or the beam could be stationary. Y Scan Patterns X Page 21

ELECTROSTATIC BEAM SCANNING I) Electrostatic scanning (low/medium beam current implanters. I < 1mA) V y Vertical Scan Vx Si wafer This type of implanter is suitable for low dose implants. The beam current is adjusted to result in t=10 sec./wafer. With scan frequencies in the 100 Hz range, good implant uniformity is achieved with reasonable throughput. Horizontal Scan Page 22

MECHANICAL BEAM SCANNING Mechanical Scanning (high beam current implanters. I > 1 ma ) Stationary Ion Beam Beam Size = 20 cm 2 Excellent wafer cooling needed. Substantial load/unload time. 15-25 wafers /disc. Excellent throughput for high dose implants. Si wafer Rotating Disc ( 1200 rpm ) Page 23

MECHANICAL SCAN END STATION Page 24

IMPLANT DOSE The implant dose φ is the number of ions implanted per unit area (cm2) of the wafer. If a beam current I is scanned for a time t, the total implanted charge Q = ( I x t ). For a dose φ,the total number of implanted ions is (Scan area A s x φ ). Since each ion is singly positively charged, this corresponds to a total charge of (q x A s x φ ). Q= It = q A s φ => φ = Dose = I t / ( q A s ) ions/cm 2 Page 25

ION IMPLANT BEAM CURRENT SET UP XL Faraday Cup Beam Current I in µa Scanning Ion Beam XL Scan Position XR I Current Integrator - XR Wafer Holder Specimen Current Detector I + To Dose Counter and Comparator Page 26

END STATION DOSE MEASUREMENT secondary electrons wafer ion beam Idt = q =A s q φ back plate DOSE MONITORING V Faraday cup ( - 100 V ) V suppression ( - 500 V ) I - + To Dose Counter And Comparator Integrator Page 27

VARIAN 120-10 END STATION Page 28

COMPLETE SYSTEM Page 29

DOPANT ION-SUBSTRATE INTERACTIONS Upon entering the substrate, the ion slows down due to nuclear and electronic stopping. Nuclear stopping : Nuclear stopping is due to the energy transfer from the ion to Si nuclei. The interaction may be strong enough to displace the Si atom from its site ( only 15 ev needed to displace one Si atom ). The displaced Si atom may even have enough kinetic energy to displace several other Si atoms. Arsenic and Phosphorous ions lose their energy mostly by nuclear stopping. They cause substantial Si crystal damage when the implant dose exceeds 5E13/cm 2. Page 30

DOPANT ION-SUBSTRATE INTERACTIONS Silicon ( represents a Si atom ) Incident ion Ion at rest Projected Range R p Electronic stopping is due to the energy transfer from the ion to the electrons of the host Si crystal. Boron ions lose their energy mostly by electronic stopping. Electronic stopping does not cause crystal damage. Page 31

POST IMPLANT ANNEAL The damaged crystal needs to be restored. This is typically achieved by 900 C, 30 min. furnace anneals or 1150 C, 30 sec. rapid thermal anneals. The interstitial dopant ions become substitutional, thus donating carriers. The interstitial (displaced) silicon atoms become substitutional,thus removing the defects that trap carriers and/or affect their mobility. During the post implant anneal, dopant ions diffuse deeper into silicon. This must be minimized to maintain shallow junctions. Page 32

ISOCHRONAL ANNEALING OF BORON P hall is the free hole content (holes/cm2) determined by Hall measurements P Hall Trend: higher the dose, the more disorder, thus the higher the final temperature required for full activation Page 33

ISOCHRONAL ANNEALING OF PHOSPHOROUS N Hall is the free electron content. Note that heavy dose Phosphorous implants can be annealed easier than the lesser dose implants N Hall Page 34

ION IMPLANT EQUATIONS Gaussian Implant Profile N -(X-Rp) N(x) = exp [ 2 ] 2π Rp 2 Rp 2 After Anneal Rp = Range Rp = Straggle N 2π Rp 2 -(X-Rp) 2 2( Rp 2 +Dt) N(x) = exp [ ] + 2Dt } I N = Dose = mqa dt From Curves concentration cm -3 Ni N peak = N p Rp where D is diffusion constant at the anneal temperature t is time of anneal after implant after anneal at 950 C, 15 min xi Approximation used in Vt calculations C background Approximation N = Ni xi x Page 35

ION IMPLANT RANGE 1 Projected Range, Rp,(um) 10-1 B P As 10-2 Sb 10 100 Implantation Energy (KeV) Page 36

ION IMPLANT STANDARD DEVIATION Standard Deviation, Rp,(um) 0.1 0.01 B P As Sb 0.001 10 100 Implantation Energy (KeV) 1,000 Page 37

CALCULATIONS Using the equations on the previous pages: Find: Xj sheet Rho implant time surface conc. average doping Page 38

ACTUAL PROFILES ARE NOT GAUSSIAN Light ions such as boron, are more effectively scattered backwards more ions to come to rest on the surface-side of Rp Heavy Ions, such as Arsenic, scatter more in forward direction the amount of dopant on the deeper side will be higher. Impurity concentration in atoms/cm 3 10 21 10 20 10 19 10 18 Boron Implanted into Silicon 30keV Simple Gaussian 100keV 300keV 800keV 10 17 0 0.2 0.4 0.6 0.8 1.0 1.2 1.4 1.6 1.8 2.0 Depth in µm Page 39

VT ADJUST IMPLANT Assume that the total implant is shallow (within W dmax ) +/- Vt = q Dose*/Cox where Dose* is the dose that is added to the Si Boron gives + shift Phosphorous gives - shift Cox is gate oxide capacitance/cm 2 Cox = εoεr / Xox Example: To shift +1.0 volts implant Boron through 1000 Å kooi oxide at an energy to place the peak of the implant at the oxide/silicon interface. Let Xox= 200 Å. Dose = Vt Cox /q =(1.0)(3.9)(8.85E-14)/(1.6E-19)(200E-8)=1.08E12 ions/cm 2 but multiply by 2 since ½ goes into silicon and ½ in Kooi oxide so dose setting on the implanter is 2.16E12 ions/cm 2 Page 40

CHANNELING Origin : the crystalline nature of the host substrate (110) (100) (111) Relative degree of openness of the silicon crystal for ions moving in <111>, <100> and <110> directions unchanneled ion: α > α cr α : entrance angle channeled ion: α < α cr Channeling process Page 41

CHANNELING ION PROFILES C(x) cm -3 Without Channeling With Channeling C background The implanted dose C(x) dx is about the same with or without channeling. But µ along the channeled profile is higher than µ along the unchanneled profile. Since the sheet resistance R s is defined as: R s = [ q µ(x) C(x)dx ] -1 = [q µ C(x)dx] -1 (where µ is the average effective mobility) R s is smaller in regions where channeling occurs. x Page 42

CHANNELING IS NON UNIFORM ACROSS THE WAFER Due to beam scan angle β s and/or the wafer flex angle β f, the entrance angle of ions varies across the wafer. The resulting channeling variations cause the sheet resistance to vary across the wafer. These R s variations can be as much as 25 % across a wafer. As the extent of local channeling is difficult to control, channeling must be prevented. BEAM BEAM β s Wafer β f Wafer Page 43

PREVENTING CHANNELING Channeling does not occur if there is significant implant damage that turns the implanted layer into an amorphous one. Heavy ions like P 31 and As 75 at large doses do not show channeling. Light ions and/or low dose implants are prone to channeling. In such instances, channeling can be prevented by: 1) Implanting through a thin amorphous layer (e.g. oxide). 2) Tilting and twisting the wafer to close crystal openness as seen by the ion beam. 3) Implanting heavy, but electrically inactive species like Si or Ar prior to the actual dopant implant. The pre-implant implant turns the wafer surface into an amorphous layer. Page 44

Ion Implantation CHANNELING Implanting Through Thin Films In addition to channeling prevention, implanting through a thin film layer (e.g. few 100 A of SiO 2 ) offers the following advantages: 1) It prevents photoresist residues/deposits from reaching the silicon surface. The resist residues deposited on the thin film can subsequently be etched away with that film (e.g. SiO 2 dipped in B.O.E.) resist oxide Silicon Wafer resist deposit resist 2) It prevents excessive evaporation (out-gassing) of volatile species (e.g. As) during implant damage anneals. Page 45

MASKING AGAINST ION IMPLANTS Various thin films can be used to mask against ion implants : resist, oxide, nitride, polysilicon, etc. The most widely used combination is resist over the oxide. 1 to 1.5 µm thick resist blocks most of the ion implants encountered in silicon processing.silicon dioxide slows down the ions at about the same rate as silicon does. Silicon nitride is a much stronger barrier to ions than silicon. Implant Doping RESIST O X I D E Dopant Density Wafer Background Doping SILICON Page 46

MASKING WITH PHOTORESIST, POLY, AND OXIDE B11, Dose = 2 E15, E = 50 KeV 6000 Å Field Oxide P-well N-well N-type Substrate 10 ohm-cm Page 47

IMPLANT MASKING THICKNESS CALCULATOR 11/20/04 IMPLANT MASK CALCULATOR Lance Barron Dr. Lynn Fuller Enter 1 - Yes 0 - No in white boxes DOPANT SPECIES MASK TYPE ENERGY B11 1 Resist 0 40 KeV BF2 0 Poly 1 P31 0 Oxide 0 Nitride 0 Thickness to Mask >1E15/cm3 Surface Concentration 2961.954 Angstroms Page 48

RESIST DAMAGE AT HIGH IMPLANT CURRENTS BF2 Implant at 80 µa in Varian 400 without a water cooled chuck Note: Varian 350D can do implants up to 300 µa with no photoresist damage because of wafer cooling Page 49

ION IMPLANT VS. CHEMICAL SOURCE PREDEPOSIT Advantages of Ion Implant Low dose introduction of dopants is possible. In chemical source predeposits dose values less than 5E13/cm 2 are not achievable. Ion implant dose control is possible down to 1E11/cm 2. High dose introduction is not limited to solid solubility limit values. Dose control is very precise at all levels. Excellent doping uniformity is achieved across the wafer and from wafer to wafer. Done in high vacuum, it is a very clean process step (except for out gassing resist particulates due to excessive local power input ). Drawbacks of Ion Implant It requires very expensive equipment ( $1M or more). At high dose values, implant throughput is less than in the case of chemical source predep. Page 50

LECTURE REVIEW Principles of Ion Implantation The implant depth controlled by the energy E of the ions Dopant density primarily controlled by the implant dose Ion Implantation equipment Low current implanters High current implanters Implanted Dopant Profiles Nuclear stopping and implant damage Post implant anneal Gaussian doping profiles Channeling and its prevention Thin film coverage of the wafer surface Advantages and Drawbacks of Ion Implantation Page 51

REFERENCES 1. Silicon Processing for the VLSI Era Volume I, S. Wolf and R.N. Tauber, Lattic Press, Sunset Beach, CA, 1986. 2. The Science and Engineering of Microelectronic Fabrication, S.A. Campbell, Oxford University Press, New York, NY, 1996. 3. VLSI Technology, Edited by S.M. Sze, McGraw-Hill Book Company, 1983. Page 52

HOMEWORK ION IMPLANT 1: The implant depth is controlled by the a) beam size b) acceleration voltage c) beam current d) implant time 2: The volume density of implanted dopants is controlled by the a) plasma density b) beam size and implant time c) implant time only d) beam current and implant time 3: In using low current implanters that process one wafer at a time, the optimal implant time per wafer (i.e. best uniformity / throughput compromise) a) 1 s b) 10 s c) 50 s d) 100 s 4: True or false? Channeling is a serious problem when implanting AS 75 ions at a dose Φ = 5x10 15 /cm 2. 5: In CMOS processing, threshold adjust doping can be made by a) chemical source predep only b) ion implant only c) either chemical source predep or ion implant. 6: Calculate the implant dose and energy needed to make the pmos Vt of -1 volt for the following device parameters. N+ Poly gate, 250 Å gate oxide, 2E16 cm-3 substrate doping, Nss=3.4E11. Page 53