Molybdenum Etchants Study Surajit Sutar University of Notre Dame

Similar documents
Photolithography. Class: Figure Various ways in which dust particles can interfere with photomask patterns.

Dry Etching and Reactive Ion Etching (RIE)

Lecture 11. Etching Techniques Reading: Chapter 11. ECE Dr. Alan Doolittle

Etching Etch Definitions Isotropic Etching: same in all direction Anisotropic Etching: direction sensitive Selectivity: etch rate difference between

III. Wet and Dry Etching

Module 7 Wet and Dry Etching. Class Notes

Conductivity of silicon can be changed several orders of magnitude by introducing impurity atoms in silicon crystal lattice.

MICROPOSIT LOL 1000 AND 2000 LIFTOFF LAYERS For Microlithography Applications

Chemical Reactions During Wet-Etching Process of LSMO/PZT/LSMO-Structured Device Fabrication

JePPIX Course Processing Wet and dry etching processes. Huub Ambrosius

Demonstration of sub-4 nm nanoimprint lithography using a template fabricated by helium ion beam lithography

ELEC 3908, Physical Electronics, Lecture 15. BJT Structure and Fabrication

ISOTROPIC ETCHING OF THE SILICON NITRIDE AFTER FIELD OXIDATION.

Contamination. Cleanroom. Cleanroom for micro and nano fabrication. Particle Contamination and Yield in Semiconductors.

Introduction to VLSI Fabrication Technologies. Emanuele Baravelli

Types of Epitaxy. Homoepitaxy. Heteroepitaxy

Electron Beam and Sputter Deposition Choosing Process Parameters

Study of Surface Reaction and Gas Phase Chemistries in High Density C 4 F 8 /O 2 /Ar and C 4 F 8 /O 2 /Ar/CH 2 F 2 Plasma for Contact Hole Etching

EE-527: MicroFabrication

Coating Technology: Evaporation Vs Sputtering

Dependence of the thickness and composition of the HfO 2 /Si interface layer on annealing

Damage-free, All-dry Via Etch Resist and Residue Removal Processes

Advanced VLSI Design CMOS Processing Technology

Dry Film Photoresist & Material Solutions for 3D/TSV

Safety, Cleaning, and Chemical Disposal Procedures

T.M.M. TEKNIKER MICROMACHINING

Microstockage d énergie Les dernières avancées. S. Martin (CEA-LITEN / LCMS Grenoble)

Micro-Power Generation

Resists, Developers and Removers

Grad Student Presentation Topics PHGN/CHEN/MLGN 435/535: Interdisciplinary Silicon Processing Laboratory

1. PECVD in ORGANOSILICON FED PLASMAS

Sheet Resistance = R (L/W) = R N L

h e l p s y o u C O N T R O L

Chapter 6 Metal Films and Filters

Semiconductor doping. Si solar Cell

What is optical lithography? The optical system Production process Future and limits of optical lithography References. Optical lithography

Photolithography (source: Wikipedia)

A Remote Plasma Sputter Process for High Rate Web Coating of Low Temperature Plastic Film with High Quality Thin Film Metals and Insulators

Study of tungsten oxidation in O 2 /H 2 /N 2 downstream plasma

Observation of Long Transients in the Electrical Characterization of Thin Film BST Capacitors

Supporting Online Material for

Lezioni di Tecnologie e Materiali per l Elettronica

Implementation Of High-k/Metal Gates In High-Volume Manufacturing

Sandia Agile MEMS Prototyping, Layout Tools, Education and Services Program

Processing Procedures for CYCLOTENE 4000 Series Photo BCB Resins DS2100 Puddle Develop Process

THE USE OF OZONATED HF SOLUTIONS FOR POLYSILICON STRIPPING

Graduate Student Presentations

IMA. Reaktives Ionenätzen für die Herstellung vertikaler, mikromechanisch aktuierbarer, optischer Bauelemente. Sören Irmer

Results Overview Wafer Edge Film Removal using Laser

Etching and Pattern Transfer (1) OUTLINE J / 3.155J -- Spring Term 2005 Lecture 12 - Etch and Pattern Transfer I (Wet Etch) 1.

Solar Photovoltaic (PV) Cells

Silicon-On-Glass MEMS. Design. Handbook

2. Deposition process

Electroplating with Photoresist Masks

LOR and PMGI Resists. Figure 1: SFG2 w/tok Resist 80 nm line. Figure 2: PMGI w/spr um line. Figure 3: LOR 30B w/spr

AN900 APPLICATION NOTE

A Plasma Doping Process for 3D FinFET Source/ Drain Extensions

OPTIMIZING OF THERMAL EVAPORATION PROCESS COMPARED TO MAGNETRON SPUTTERING FOR FABRICATION OF TITANIA QUANTUM DOTS

CRYSTAL DEFECTS: Point defects

MOS (metal-oxidesemiconductor) 李 2003/12/19

Lithography Part I September, 5 th 2013

Bachelor Project. Nano-stenciling for fabrication of metal nanoparticles. Nano-stenciling for fabrication of metal nanoparticles

Chapter 6. Solution, Acids and Bases

Facility Rates & Expense Caps

How To Make A Plasma Control System

Design of inductors and modeling of relevant field intensity

Fabrication and Manufacturing (Basics) Batch processes

MEMS Processes from CMP

Design and Simulation of MEMS Vibration Sensor for Launch Vehicles

... complement Information for Processing

Vacuum Evaporation Recap

Spectroscopic Ellipsometry:

Concepts and principles of optical lithography

Deposition Overview for Microsytems

FLEXIBLE CIRCUITS MANUFACTURING

Basic Properties and Application of Auto Enamels

CHAPTER 5. OVERVIEW OF THE MANUFACTURING PROCESS

IBS - Ion Beam Services

Supporting information

Silica Over-Saturation, Precipitation, Prevention and Remediation In Hot Water Systems Edited By Dave Peairs, Cal Water, Technical Director

ACTIVATION ENERGY: AN ELEMENTARY STUDY IN THE MATRIX ISOTROPIC ETCHER.

Optimization of Photosensitive Polyimide Process for Cost Effective Packaging

Revised: June 6, 2007

Neuere Entwicklungen zur Herstellung optischer Schichten durch reaktive. Wolfgang Hentsch, Dr. Reinhard Fendler. FHR Anlagenbau GmbH

Processing Procedures for BCB Adhesion

Lecture 12. Physical Vapor Deposition: Evaporation and Sputtering Reading: Chapter 12. ECE Dr. Alan Doolittle

For Touch Panel and LCD Sputtering/PECVD/ Wet Processing

How compact discs are made

Advanced materials & solutions for high h temperatures

Rapid Prototyping and Development of Microfluidic and BioMEMS Devices

SFxxx-S PID Test Report (Potential Induced Degradation) TUV Rheinland Japan. ARC Product Management Ver. 1

COMPARISON OF TEXTURE IN COPPER AND ALUMINUM THIN FILMS DETERMINED BY XRD AND EBSD *

The New PVD HI3-Technology: Latest Developments and Potential for Coining Dies.

Mask Cleaning Processes and Challenges

Chapter 2 The Study on Polycrystalline Pentacene Thin Film Transistors

BROADBAND PHOTOCURRENT ENHANCEMENT IN LONGWAVE INFRARED QUANTUM DOT PHOTODETECTORS BY SUB-WAVELENGTH SURFACE GRATINGS

Study on Wet Etching of AAO Template

Study of plasma-induced damage of porous ultralow-k dielectric films during photoresist stripping

Single Sided Wet Etching for Texturing, Thinning, and Packaging Applications

THIN FILM MATERIALS TECHNOLOGY

Transcription:

The purpose of this Molybdenum etching study is to find a Molybdenum metallization process without involving a Lift-Off. Molybdenum, a refractory metal, when evaporated by an E-beam, causes a significant rise in the temperature of the evaporation chamber. This could present problems during the subsequent Lift-Off due to the possible baking of the photoresist during evaporation. An alternative process would be to deposit Molybdenum all over the surface of the wafer, pattern the Molybdenum surface in a photolithography process, and then to etch off Molybdenum where not needed. This process requires suitable and preferably selective etchants for Molybdenum. Preparation of the samples: Molybdenum was deposited on Si and InAs (PEDI-90, top InAsP removed) wafers. The wafers were patterned using AZ5214E photoresist. Samples like these were then treated with the etchant and were step-profiled to get the etch depth after removing the photoresist. The metal deposited varied in thickness. Could be taken between 700 and 1000 A 0. A brown Molybdenum oxide layer is usually formed in exposure to air. That could have affected the Molybdenum thickness and subsequent etching too. Etchants studied: 1. x HF: x H 2 O a. 1 HF: 1 H 2 O b. 1 HF: 5 H 2 O No etching was observed in 1 minute 2. x HF: x H 2 O 2 : x H 2 O No etching was observed in 5 minutes. All the compositions give a very rough surface. The etching is not uniform. The places most etched are dark (probably oxide), and at other places Molybdenum becomes fragmented. The average surface roughness is very high. The samples were soaked in HCl (both concentrated and diluted) to remove the brown oxide film. But 3 hours of soaking yielded nothing. The etchant seemed to attack both InAs and Si.

a. 1 HF: 2 H 2 O 2 b. 1 HF: 2 H 2 O 2 : 5 H 2 O 20 1.24 µm 30 2.354 µm c. 1 HF: 2 H 2 O 2 : 10 H 2 O 10 337.3 nm 10 211.1 nm d. 1 HF: 1 H 2 O 2 e. 1 HF: 1 H 2 O 2 : 1 H 2 O f. 1 HF: 1 H 2 O 2 : 5 H 2 O 20 75.8 nm 40 92.3 nm Surface Roughness 20 22 Å 40 Å 40 242 Å 30 Å 100 2179 Å 400 Å 240 5993 Å 200 Å Time (minutes) Surface Roughness 2 5.6 nm 3.1 nm 5 450 nm 61.4 nm 10 1400 nm 3192 nm

g. 1 HF: 1 H 2 O 2 : 10 H 2 O Time (minutes) h. 1 HF: 1 H 2 O 2 : 25 H 2 O 15 1.15 µm Time (minutes) i. 1 HF: 1 H 2 O 2 : 50 H 2 O 25 713 nm Time (minutes) j. 1 HF: 1 H 2 O 2 : 200 H 2 O 20 0 nm Time (minutes) Surface Roughness 90 (on Si) 785.7 nm 79.2 nm 90 (on InAs) 5.25 µm IT DOES ATTACK InAs!!

2. 15 NH 4 OH: 10 H 2 O 2 : 100 H 2 O 100 Etching Rate for Molybdenum on Si (nm) 80 60 40 20 15 NH 4 OH : 10 H 2 O 2 : 100 H 2 O Molybdenum thickness 70-100 nm 0 0 50 100 150 200 The Molybdenum thickness could have been 70-100 nm. After 3 minutes, there were places where the photoresist (5214E) seemed to have been worn off at the edges of features. It means either the etchant attacks the PR or the etching is isotropic. The etching reaction is marked with brown film being formed at the places etched. 1 HNO 3 : 1 H 2 SO 4 : 3 H 2 O Doesn t seem to attack Silicon. But attacks InAs rapidly (from both the top and bottom of the sample). Takes off around 80 nm of Molybdenum in 10 seconds. 1 HNO 3 : 10 H 2 O No etching was observed after 20 minutes of treatment. 1 HNO 3 : 1 HCl: 1 H 2 O Attacks InAs rapidly after etching Molybdenum.

Straight H 2 O 2 (nm) 350 300 250 200 150 100 Molybdenum Etch with H 2 O 2 Si Substrate Molybdenum 50 y = -1.5357 + 2.6704x R= 0.9759 0 0 50 100 150 200 250 2ss1013etch2 The etching was done with Photoresist (5214E) as an etch mask, and it was observed that for longer etch times (greater than 3 minutes), the molybdenum under the photoresist was etched at the edges. It suggests adhesion problems between Molybdenum and the photoresist or H 2 O 2 attacking the photoresist. Also, the etch rate depends upon the strength of the H 2 O 2 (the actual percentage of H 2 O 2 in the solution).

Reactive Ion Etching (RIE) with CF 4 and O 2 (nm) 800 700 600 500 400 300 200 100 CF 4 /O 2 RIE Etch Molybdenum y = -1.5336 + 0.7342x R= 0.98509 y = -133.74 + 1.8718x R= 0.99222 y = -276.17 + 2.7907x R= 0.97966 RIE Etch 26 sccm CF, 5 sccm O, 4 2 60 mt, 100 W, ~210 V DC bias Si substrate Molybdenum PECVD grown SiO 0 2 0 50 100 150 200 250 300 350 400 Etch 2ss1013etch1 The etch rate as found from the above figure is approximately 18.71 Å/s. The etchant doesn t attack InAs, but with the DC bias ~ 200 V, it is expected to damage the surface and introduce defects. Conclusions: 1. The mineral acid etchants (HNO 3, H 2 SO 4 etc) are found to have high etch rates, but they attack InAs and possibly, other III-IV compounds. 2. The NH 4 OH etchant and the H 2 O 2 etchant can be used with a photoresist (5214E) etch mask for shorter etch times (< 3 minutes). For longer etches, SiO 2 can be used as an etch mask. Note: NH 4 OH could attack InAs if the ph of the solution is low. 3. The RIE with CF 4 and O 2 etches Si and SiO 2. It could introduce defects in InAs. 4. After etching, usually a thin brown oxide film is formed on the surface. This could be taken off by treatment with diluted HCl.