L11 Product datasheet L11 Standard range Material mixed cellular polyurethane Static range of use Color beige P25 2.5 Standard dimensions on stock Thickness 12.5 mm with L11 12 25 mm with L11 25 Rolls Stripes 1.5 m wide, 5. m long max. 1.5 m wide, up to 5. m long Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term, infrequent loads) Compression load up to.11 N/mm² up to.16 N/mm 2 up to.5 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity.25.17 N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity.15.38 N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.28 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 1.6% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength.31 N/mm 2 DIN EN ISO 1798* Elongation at break 22% DIN EN ISO 1798* Tear strength 1.2 N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.7 [-].8 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 14 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 34% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 49% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
2 L11 Product datasheet Load deflection curve.2.18.16.14.12.1.8 12 mm 25 mm 37 mm 5 mm.11 N/mm 2 Control of the deflection of L11 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature..6.4.2 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ].4.3 4 Hz 1 Hz e Lastbereich Measurement of the modulus of elasticity of L11 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513..2 Quasistatic.1.4.8.12.16.2.11 N/mm
L11 Natural frequency.2.16.12 12 mm Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of L11 based on a stiff subgrade..8 25 mm 37 mm.11 N/mm 2.4 5 mm 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency Disturbing frequency [Hz] 1 9 8 7 6-4 db/99% -35 db/98% -3 db/97% -25 db/94% -2 db/9% -15 db/82% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of L11 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 5 4-1 db/69% -5 db/44% 3 db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ L11 Creep behavior % of the thickness] Relative deflection 4 3 2 Increase of the deformation of APSOPUR L11 under the same constant compressive load..11 N/mm 2 1.7 N/mm 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com
L18 Product datasheet L18 Standard range Material mixed cellular polyurethane Static range of use Color lavander P25 2.5 Standard dimensions on stock Thickness 12.5 mm with L18 12 25 mm with L18 25 Rolls Stripes 1.5 m wide, 5. m long max. 1.5 m wide, up to 5. m long Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term, infrequent loads) Compression load up to.18 N/mm² up to.28 N/mm 2 up to.8 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity.5.25 N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity.25.55 N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.25 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 2.% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength.4 N/mm 2 DIN EN ISO 1798* Elongation at break 22% DIN EN ISO 1798* Tear strength 2. N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.7 [-].8 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 22 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 35% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 61% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
L18 Product datasheet Load deflection curve.35.3.25 12 mm 25 mm 37 mm 5 mm Control of the deflection of L18 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature..2.15.1.18 N/mm².5 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ].7.6.5.4 4 Hz 1 Hz Measurement of the modulus of elasticity of L18 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513..3 Quasistatic.2.1 N/mm 2.18.5.1.15.2.25.3.35
L18 Natural frequency.35.3.25.2 12 mm Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of L18 based on a stiff subgrade..15 25 mm 37 mm.18 N/mm 2.1 5 mm.5 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency Disturbing frequency [Hz] 1 9 8 7 6-4 db/99% -35 db/98% -3 db/97% -25 db/94% -2 db/9% -15 db/82% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of L18 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 5 4 3-1 db/69% -5 db/44% db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ L18 Creep behavior % of the thickness] 4 3 Increase of the deformation of APSOPUR L18 under the same constant compressive load. Relative deflection 2 1.18 N/mm 2.9 N/mm 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com
L28 Product datasheet L28 Standard range Material mixed cellular polyurethane Static range of use Color green P25 2.5 Standard dimensions on stock Thickness 12.5 mm with L28 12 25 mm with L28 25 Rolls Stripes 1.5 m wide, 5. m long max. 1.5 m wide, up to 5. m long Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term, infrequent loads) Compression load up to.28 N/mm 2 up to.4 N/mm 2 up to.9 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity.8.5 N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity.35.75 N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.22 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 2.3% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength.5 N/mm 2 DIN EN ISO 1798* Elongation at break 18% DIN EN ISO 1798* Tear strength 2.1 N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.7 [-].8 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 39 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 47% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 69% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
L28 Product datasheet Load deflection curve.5.4.3.2 12 mm 25 mm 37 mm 5 mm.28 N/mm 2 Control of the deflection of L28 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature..1 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ] 1.8.6 4 Hz 1 Hz Quasistatic Measurement of the modulus of elasticity of L28 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513..4.2.1.2.3.4.5.28 N/mm 2
L28 Natural frequency.5.4.3 12 mm Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of L28 based on a stiff subgrade..2 25 mm 37 mm.28 N/mm 2.1 5 mm 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency [Hz] Disturbing frequency 1 9 8 7-4 db/99% -35 db/98% -3 db/97% -25 db/94% -2 db/9% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of L28 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 6-15 db/82% 5 4-1 db/69% -5 db/44% 3 db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ L28 Creep behavior % of the thickness] Relative deflection 4 3 2 Increase of the deformation of APSOPUR L28 under the same constant compressive load..28 N/m 2 1.14 N/m 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com
L42 Product datasheet L42 Standard range Material mixed cellular polyurethane Static range of use Color yellow P25 2.5 Standard dimensions on stock Thickness 12.5 mm with L42 12 25 mm with L42 25 Rolls Stripes 1.5 m wide, 5. m long max. 1.5 m wide, up to 5. m long Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term, infrequent loads) Compression load up to.42 N/mm² up to.62 N/mm 2 up to 1.2 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity.21.8 N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity.6 1.5 N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.2 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 3.2% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength.9 N/mm 2 DIN EN ISO 1798* Elongation at break 21% DIN EN ISO 1798* Tear strength 4.5 N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.7 [-].8 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 63 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 38% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 7% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
L42 Product datasheet Load deflection curve.8.7.6.5 12 mm 25 mm 37 mm 5 mm Control of the deflection of L42 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature..4.3.42 N/mm 2.2.1 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ] 1.5 1.2.9 4 Hz 1 Hz Quasistatic Measurement of the modulus of elasticity of L42 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513..6.3.1.2.3.4.5.6.7.8.42 N/mm 2
L42 Natural frequency.8.7.6.5 12 mm Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of L42 based on a stiff subgrade..4.3 25 mm 37 mm.42 N/mm 2.2 5 mm.1 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency [Hz] Disturbing frequency 1 9 8 7 6-4 db/99% -35 db/98% -3 db/97 % -25 db/94 % -2 db/9 % -15 db/82% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of L42 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 5 4 3-1 db/69% -5 db/44% db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ L42 Creep behavior % of the thickness] 4 3 Increase of the deformation of APSOPUR L42 under the same constant compressive load. Relative deflection 2.42 N/mm 2 1.21 N/mm 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com
L55 Product datasheet L55 Standard range Material mixed cellular polyurethane Static range of use Color light blue P25 2.5 Standard dimensions on stock Thickness 12.5 mm with L55 12 25 mm with L55 25 Rolls Stripes 1.5 m wide, 5. m long max. 1.5 m wide, up to 5. m long Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term, infrequent loads) Compression load up to.55 N/mm² up to.8 N/mm 2 up to 2 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity.28.75 N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity.68 1.25 N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.18 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 3.4% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength 1.2 N/mm 2 DIN EN ISO 1798* Elongation at break 24% DIN EN ISO 1798* Tear strength 4.8 N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.6 [-].75 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 82 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 44% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 72% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
L55 Product datasheet Load deflection curve.1.8.6 12 mm 25 mm 37 mm 5 mm,55 N/mm 2 Control of the deflection of L55 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature..4.2 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ] 2 1 4 Hz 1 Hz Measurement of the modulus of elasticity of L55 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513. Quasistatic.2.4.6.8.1.55 N/mm 2
L55 Natural frequency.1.8.6 12 mm Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of L55 based on a stiff subgrade..4 25 mm.55 N/mm 2 37 mm.2 5 mm 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency [Hz] Disturbing frequency 1 9 8 7 6-4 db/99% -35 db/98% -3 db/97% -25 db/94% -2 db/9% -15 db/82% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of L55 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 5 4 3-1 db/69% -5 db/44% db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ L55 Creep behavior % of the thickness] 4 3 Increase of the deformation of APSOPUR L55 under the same constant compressive load. Relative deflection 2.55 N/mm 2 1.28 N/mm 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com
H11 Product datasheet H11 Standard range Material mixed cellular polyurethane Static range of use Color pink P25 2.5 Standard dimensions on stock Thickness 12.5 mm with H11 12 25 mm with H11 25 Plates 1.5 m long, special lenghts available 1. m wide Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term, infrequent loads) Compression load up to.11 N/mm² up to.16 N/mm 2 up to 3 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity.65 1.5 N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity 1.2 2. N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.17 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 3.9% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength 1.5 N/mm 2 DIN EN ISO 1798* Elongation at break 22% DIN EN ISO 1798* Tear strength 6. N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.7 [-].8 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 17 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 57% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 68% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
1. H11 Product datasheet Load deflection curve.2.16.12.8 12 mm 25 mm 37 mm 5 mm.11 N/mm 2 Control of the deflection of H11 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature..4 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ] 3 2 Quasistatic 4 Hz 1 Hz Measurement of the modulus of elasticity of H11 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513. 1.4.8.12.16.2 1 N/mm 2
H11 Natural frequency.2.16.12 12 mm Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of H11 based on a stiff subgrade..8 25 mm 37 mm.11 N/mm 2.4 5 mm 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency [Hz] Disturbing frequency 1 9 8 7 6-4 db/99% -35 db/98% -3 db/97% -25 db/94% -2 db/9% -15 db/82% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of H11 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 5 4 3-1 db/69% -5 db/44% db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ H11 Creep behavior % of the thickness] 4 3 Increase of the deformation of APSOPUR H11 under the same constant compressive load. Relative deflection 2.11 N/mm 2 1.55 N/mm 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com
H22 Product datasheet H22 Standard range Material mixed cellular polyurethane Static range of use Color dark green P25 2.5 Standard dimensions on stock Thickness 12.5 mm with H22 12 25 mm with H22 25 Plates 1.5 m long, special lenghts available 1. m wide Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term, infrequent loads) Compression load up to.22 N/mm² up to.32 N/mm 2 up to 4 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity 1.7 2.5 N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity 2.2 3.7 N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.15 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 4.2% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength 2.4 N/mm 2 DIN EN ISO 1798* Elongation at break 24% DIN EN ISO 1798* Tear strength 9.3 N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.7 [-].8 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 33 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 6% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 61% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
H22 Product datasheet Load deflection curve.4.3 25 mm 12 mm 37 mm 5 mm Control of the deflection of H22 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature..2.22 N/mm 2.1 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ] 5 4 3 4 Hz 1 Hz Quasistatic Measurement of the modulus of elasticity of H22 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513. 2 1.22 N/mm 2.15.3.45
H22 Natural frequency.4.3 25 mm 12 mm Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of H22 based on a stiff subgrade..2 37 mm.22 N/mm 2 5 mm.1 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency Disturbing frequency [Hz] 1 9 8 7 6-4 db/99% -35 db/98% -3 db/97% -25 db/94% -2 db/9% -15 db/82% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of H22 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 5 4 3-1 db/69% -5 db/44% db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ H22 Creep behavior % of the thickness] 4 3 Increase of the deformation of APSOPUR H22 under the same constant compressive load. Relative deflection 2.22 N/mm 2 1.11 N/mm 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com
H3 Product datasheet H3 Standard range Material mixed cellular polyurethane Static range of use Color light orange P25 2.5 Standard dimensions on stock Thickness 12.5 mm with H3 12 25 mm with H3 25 Plates 1.5 m long, special lenghts available 1. m wide Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term. infrequent loads) Compression load up to.3 N/mm² up to.42 N/mm 2 up to 4.5 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity 3.6 5. N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity 5.1 6.3 N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.14 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 4.4% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength 2.9 N/mm 2 DIN EN ISO 1798* Elongation at break 21% DIN EN ISO 1798* Tear strength 14.1 N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.6 [-].7 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 62 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 58% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 5% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
H3 Product datasheet Load deflection curve.6.5.4.3 12 mm 25 mm 37 mm 5 mm.3 N/mm 2 Control of the deflection of H3 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature..2.1 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ] 1 8 6 Quasistatic 4 Hz 1 Hz Measurement of the modulus of elasticity of H3 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513. 4 2.3 N/mm 2.2.4.6
H3 Natural frequency.6.5.4.3 12 mm 25 mm 37 mm.3 N/mm 2 Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of H3 based on a stiff subgrade..2 5 mm.1 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency [Hz] Disturbing frequency 1 9 8 7 6-4 db/99% -35 db/98% -3 db/97% -25 db/94% -2 db/9% -15 db/82% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of H3 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 5 4 3-1 db/69% -5 db/44% db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ H3 Creep behavior % of the thickness] Relative deflection 4 3 2 Increase of the deformation of APSOPUR H3 under the same constant compressive load..3 N/mm 2 1.15 N/mm 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com
H45 Product datasheet H45 Standard range Material mixed cellular polyurethane Static range of use Color dark blue P25 2.5 Standard dimensions on stock Thickness 12.5 mm with H45 12 25 mm with H45 25 Plates 1.5 m long, special lenghts available 1. m wide Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term, infrequent loads) Compression load up to.45 N/mm² up to.62 N/mm 2 up to 5 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity 4.2 5.7 N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity 6.8 1. N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.12 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 6.2% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength 3.6 N/mm 2 DIN EN ISO 1798* Elongation at break 23% DIN EN ISO 1798* Tear strength 18.5 N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.6 [-].7 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 84 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 58% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 44% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
H45 Product datasheet Load deflection curve.9.8.7.6.5 12 mm 25 mm 37 mm 5 mm Control of the deflection of H45 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature..4.45 N/mm 2.3.2.1 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ] 12 8 4 Hz 1 Hz Quasistatic Measurement of the modulus of elasticity of H45 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513. 4.45 N/mm 2.1.2.3.4.5.6.7.8.9
H45 Natural frequency.9.8.7.6.5 25 mm 12 mm Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of H45 based on a stiff subgrade..4.3 37 mm 5 mm.45 N/mm 2.2.1 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency [Hz] Disturbing frequency 1 9 8 7 6-4 db/99% -35 db/98% -3 db/97% -25 db/94% -2 db/9% -15 db/82% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of H45 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 5 4 3-1 db/69% -5 db/44% db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ H45 Creep behavior % of the thickness] 4 3 Increase of the deformation of APSOPUR H45 under the same constant compressive load. Relative deflection 2.45 N/mm 2 1.225 N/mm 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com
H6 Product datasheet H6 Standard range Material mixed cellular polyurethane Static range of use Color red P25 2.5 Standard dimensions on stock Thickness 12.5 mm with H6 12 25 mm with H6 25 Plates 1.5 m long, special lenghts available 1. m wide Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term, infrequent loads) Compression load up to.6 N/mm² up to.85 N/mm 2 up to 6 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity 5.5 7.8 N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity 7.9 13. N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.11 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 4.8% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength 4. N/mm 2 DIN EN ISO 1798* Elongation at break 21% DIN EN ISO 1798* Tear strength 19 N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.6 [-].7 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 15 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 59% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 39% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
H6 Product datasheet Load deflection curve 1.2 1.8.6 12 mm 25 mm 37 mm 5 mm.6 N/mm 2 Control of the deflection of H6 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature. Form factor q = 2.5.4.2 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ] 16 12 8 4 Hz 1 Hz Quasistatic Measurement of the modulus of elasticity of H6 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513. Form factor q = 2.5 4.6 N/mm 2.2.4.6.8 1 1.2
H6 Natural frequency 1.2 1.8.6 25 mm 37 mm 12 mm.6 N/mm 2 Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of H6 based on a stiff subgrade. Form factor q = 2.5.4 5 mm.2 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency [Hz] Disturbing frequency 1 9 8 7 6-4 db/99% -35 db/98% -3 db/97% -25 db/94% -2 db/9% -15 db/82% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of H6 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 5 4 3-1 db/69% -5 db/44% db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ H6 Creep behavior % of the thickness] 4 3 Increase of the deformation of APSOPUR H6 under the same constant compressive load. Form factor q = 2.5 Relative deflection 2.6 N/mm 2 1.3 N/mm 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com
H85 Product datasheet H85 Standard range Material mixed cellular polyurethane Static range of use Color brown P25 2.5 Standard dimensions on stock Thickness 12.5 mm with H85 12 25 mm with H85 25 Plates 1.5 m long, special lenghts available 1. m wide Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term, infrequent loads) Compression load up to.85 N/mm² up to 1.2 N/mm 2 up to 7 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity 8.3 9.6 N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity 11. 16.5 N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.1 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 7.9% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength 4.6 N/mm 2 DIN EN ISO 1798* Elongation at break 23% DIN EN ISO 1798* Tear strength 2 N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.6 [-].75 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 1241 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 58% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 35% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
H85 Product datasheet Load deflection curve 1.5 1.2 12 mm 25 mm 37 mm 5 mm Control of the deflection of H85 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature..9.85 N/mm 2 Form factor q = 2.5.6.3 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ] 2 16 12 3 Hz 1 Hz Quasistatic Measurement of the modulus of elasticity of H85 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513. Form factor q = 2.5 8 4.3.6.9 1.2 1.5.85 N/mm 2
H85 Natural frequency 1.5 1.2.9.6 25 mm 37 mm 5 mm 12 mm.85 N/mm 2 Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of H85 based on a stiff subgrade. Form factor q = 2.5.3 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency [Hz] Disturbing frequency 1 9 8 7 6-4 db/99% -35 db/98% -3 db/97% -25 db/94% -2 db/9% -15 db/82% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of H85 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 5 4 3-1 db/69% -5 db/44% db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ H85 Creep behavior % of the thickness] 4 3 Increase of the deformation of APSOPUR H85 under the same constant compressive load. Form factor q = 2.5 Relative deflection 2.85 N/mm 2 1.45 N/mm 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com
P25 Product datasheet P25 Standard range Material mixed cellular polyurethane Static range of use Color orange P25 2.5 Standard dimensions on stock Thickness 12.5 mm with P25 12 25 mm with P25 25 Plates 1.5 m long, special lenghts available 1. m wide Other dimensions (also thickness) as well as stamped and molded parts on request H85 H6 H45 H3 H22.85.6.45.3.22 H11.11 Area of application Static range of use (static loads) Operating (static plus loads) Load peaks (short term, infrequent loads) Compression load up to 2.5 N/mm² up to 3.5 N/mm 2 up to 8 N/mm 2 L55 L42 L28 L18 L11.55.42.28.18.11.1.1.1 1 1 Static load [N/mm 2 ] Material properties Test methods Comment Static modulus of elasticity 25.5 31.3 N/mm 2 EN 826* tangent modulus, see chart modulus of elasticity Dynamic modulus of elasticity 41. 16. N/mm 2 DIN 53513 depending on the frequency, static load and thickness, see chart modulus of elasticity Mechanical loss factor.9 [-] DIN 53513* depending on the load, the amplitude and the frequency Compression set 8.6% DIN EN ISO 1856* measured 3 minutes after unloading, 5% deformation, 23 C, 72 hours Tensile strength 6.9 N/mm 2 DIN EN ISO 1798* Elongation at break 19% DIN EN ISO 1798* Tear strength 34.5 N/mm DIN ISO 34-1* Fire behavior B2 [-] E [-] Coefficient of friction.5 [-].6 [-] DIN 412 DIN EN 1351 normal flammable steel (dry) concrete (dry) Compression strength 364 kpa DIN EN ISO 3386-2* compressive strength 25% deformation, sample h = 25 mm Rebound resilience 55% DIN EN ISO 837* depending on thickness, sample h = 25 mm Strength reduction 2% DIN EN 1494 depending on thickness, sample h = 25 mm * Tests according to respective standards
P25 Product datasheet Load deflection curve 5. 4. 3. 12 mm 25 mm 37 mm 5 mm 2.5 N/mm 2 Control of the deflection of P25 between two flat steel plates, according to DIN EN 826. Recording of the 3 rd loading. Loading time 2 secondes. Testing at room temperature. Form factor q = 1.25 2. 1.. 1 2 3 4 5 6 7 8 9 1 Deflection [mm] Modulus of elasticity Modulus of elasticity [ N/m m 2 ] 18 15 12 Measurement of the modulus of elasticity of P25 due to sinusoidal excitation with a constant medium load, oscillating range ±.25 mm. Quasistatic modulus of elasticity as a tangent modulus taken from the load deflection curve. Test according to DIN 53513. Form factor q = 1.25 9 6 3 3 Hz 1 Hz Quasistatic 2.5 N/mm 2. 1. 2. 3. 4. 5.
P25 Natural frequency 5. 4. 3. 25 mm 12 mm Natural frequency of a single-degree-offreedom system consisting of a fixed mass and an elastic bearing consisting of P25 based on a stiff subgrade. Form factor q = 1.25 2. 1. 37 mm 5 mm 2.5 N/mm 2. 5 1 15 2 25 Natural frequency of the system [Hz] Vibration isolation efficiency [Hz] Disturbing frequency 1 9 8 7 6-4 db/99% -35 db/98% -3 db/97% -25 db/94% -2 db/9% -15 db/82% Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of P25 based on a stiff subgrade. Parameter: transmission in db, isolation rate in %. 5 4 3-1 db/69% -5 db/44% db/% 2 1 5 1 15 2 25 Natural frequency of the system [Hz]
[ P25 Creep behavior % of the thickness] 4 3 Increase of the deformation of APSOPUR P25 under the same constant compressive load. Form factor q = 1.25 Relative deflection 2 1 2.5 N/mm 2 1.25 N/mm 2 1 1 1 1 1 1 Load duration [h] Status January 214 All information and data is based on our current knowledge. The data can be applied for calculations and as guidelines, are subject to typical manufacturing tolerances and are not guaranteed. We reserve the right to amend the data. Further characteristic values on request. Switzerland Angst + Pfister AG Thurgauerstrasse 66, Postfach, CH-852 Zürich Phone +41 ()44 36 61 11 Fax +41 ()44 32 18 71, ch@angst-pfister.com Angst + Pfister SA Chemin de la Papeterie 1, CH-129 Versoix Phone +41 ()22 979 28 Fax +41 ()22 979 28 78, ch@angst-pfister.com the Online Shop of Angst + Pfister www.apsoparts.com France Angst + Pfister SA Boîte postale 5115, 33, rue des Chardonnerets ZAC Paris Nord ll, FR-9595 Roissy CDG CEDEX Phone +33 ()1 48 63 2 8 Fax +33 ()1 48 63 26 9, fr@angst-pfister.com Germany Angst + Pfister GmbH Schulze-Delitzsch-Strasse 38, DE-7565 Stuttgart Phone +49 ()711 48 999 2- Fax +49 ()711 48 999 2-69, de@angst-pfister.com Austria Angst + Pfister Ges.m.b.H. Floridsdorfer Hauptstrasse 1/E, AT-121 Wien Phone +43 ()1 258 46 1- Fax +43 ()1 258 46 1-98, at@angst-pfister.com Italy Angst + Pfister S.p.A. Via Montefeltro 4, IT-2156 Milano Phone +39 2 387.1 Fax +39 2 387.1, it@angst-pfister.com Netherlands Angst + Pfister B.V. Boerhaavelaan 19, NL-2713 HA Zoetermeer Phone +31 ()79 32 37 Fax +31 ()79 32 3799, nl@angst-pfister.com Belgium Angst + Pfister N.V. S.A. Bedrijvencentrum Waasland Industriepark-West 75 BE-91 Sint-Niklaas Phone +32 ()3 778 128 Fax +32 ()3 777 8398, be@angst-pfister.com China Angst + Pfister Trade (Shanghai) Co. Ltd. Rm 142, West Tower, Zhong Rong Hengrui Building No. 56 Zhangyang Road, CN-Shanghai 2122 Phone +86 21 5169 5 5 Fax +86 21 5835 8618, cn@angst-pfister.com Turkey Laspar Angst + Pfister Advanced Industrial Solutions A.Ş. Dosab Gonca Sok. No:1, TR-16245 Bursa Phone +9 224 261 26 21 Fax +9 224 261 26 2 www.laspargroup.com, info@laspargroup.com