A COMPARISON OF METHODS FOR THE EXTRACTION OF SMECTITES FROM CALCAREOUS ROCKS BY ACID DISSOLUTION TECHNIQUES

Transcription

1 Clay Minerals (1992) 27, A COMPARSON OF METHODS FOR THE EXTRACTON OF SMECTTES FROM CALCAREOUS ROCKS BY ACD DSSOLUTON TECHNQUES R. J. COOK Postgraduate Research nstitute for Sedimentology, The University, PO Box 227, Whiteknights, Reading RG6 2AB, UK (Received 5 March 1991; revised 30 May 1991) ABSTRACT: Four methods of extracting clays from calcite-rich samples were compared: (i) sodium acetate buffer solution; (ii) lithium acetate buffer solution; (iii) hydrochloric acid; (iv) liquid cation-exchange acid. The methods were tested on mixtures consisting of 80% calcite, 10% quartz and 10% hectorite. Potassium had previously been exchanged on to the interlayer sites of the clay. XRD traces of the extracted clays appeared identical with those of the original clays except for a sharpening of the 001 reflection. The bulk chemistry of the clay was unchanged except by the HC extraction, which appeared to cause a stripping of the octahedral cations. With all of the methods the exchangeable cation content was altered; the sodium acetate method, for example, retained only 17% of the original exchangeable K +, the other methods all retaining <10%. Clay minerals are usually separated from carbonate rocks by acid dissolution (Ray et al., 1957; Ostrom, 1961; Peterson, 1961; Jackson, 1969). Previous workers have examined X-ray diffraction (XRD) patterns of the clays for consequential changes, but not their structural chemistry and interlayer chemistry. The interlayer chemistry may be greatly affected by the release of Ca 2+ and Mg 2+ from the carbonate during dissolution since divalent cations are preferentially taken up by clays (Carroll, 1959). Cations produced from the dissolution of carbonate can interfere with cation exchange capacity and elemental analyses (Eslinger & Pevear, 1988). t is thus desirable to know how any clay extraction techniques may affect not only XRD characteristics but also structural and interlayer chemistry. This paper compares four techniques for the extraction of smectites from calcareous rocks using acid solutions and compares the XRD traces, the structural chemistry and the interlayer chemistry of the clays. EXPERMENTAL TECHNQUES Starting materials n order to compare the methods it had to be possible to refer the resultant clay composition to the original. For this reason the experiments were carried out on synthetic mixtures consisting of 80% calcite, 10% quartz and 10% hectorite. The XRD pattern and the chemical composition of the hectorite had been predetermined. Hectorite [(l/2ca, Na)y(Mg6_yLiy)SisO20(OH)4 ], a trioetahedral smectite, was chosen as the most susceptible of the smectite clays to acid attack (Ostrom, 1961). The hectorite was a The Mineralogical Society

2 74 R. J. Cook standard clay supplied by Source Clay Mineral Repository, Department of Geology, University of Missouri, USA. The clay was initially saturated with K + by washing with 1 M KC1 solution twice for 30 min and then overnight (Bain & Smith, 1987). The clays were then washed with distilled water to remove any residual KC1. The washings were monitored by the use of AgC1 solution, which produces a cloudy white precipitate if C1 ions are present. f this washing is too vigorous exchangeable cations may be stripped off (Bain & Smith, 1987). Extraction methods' n each extraction (performed in duplicate) 5 g of sample was used. Repeated wetting and drying of the samples was avoided as this can affect the clay structure (Chaussidon, 1962). Sodium acetate (NaOAc) buffer solution (after Jackson, 1969). Sodium acetate solution (1 M) was used to buffer acetic acid at ph 5.0. The leaching solution was added 50 ml at a time and when the solution was spent it was separated off by centrifugation and a further 50 ml added. n all, 300 ml of leaching solution was required. The process took two days at room temperature with constant stirring for completion, completion being the dissolution of all the calcite present in the sample as indicated by the lack of effervescence on adding concentrated HC1 to a small fraction of the treated sample. At the end of the process the solid was washed carefully with distilled water to remove any residual leaching solution, and the clays were finally separated by sedimentation. Lithium acetate (LiOAc) buffer solution (after Peterson, 1961). Lithium acetate solution (1 M) was used to buffer acetic acid at ph 4.5. Lithium was chosen as this is one of the ions least likely to replace other cations already in the clay structure (Peterson, 1961). The leaching solution (300 ml) was added in one operation ensuring that the cations released by carbonate dissolution would be kept in low concentration and thus have less effect (Peterson, 1961). This process was also completed in two days at room temperature with constant Stirring, and the clay was washed and separated as above. Hydrochloric acid. Hydrochloric acid is generally employed for dissolution purposes when dealing with dolomites or coarse-grained calcites (Eslinger & Pevear, 1988). The method was used to compare strong-acid and weak-acid methods. Eighty ml of 10% HC1 were added to the sample. Dissolution was complete after one hour at room temperature with constant stirring. The solids were then washed to remove residual HC1 and the clays separated by sedimentation. Liquid cation-exchange acid. This method was devised in an attept to counter the effect of the cations released by the carbonate dissolution exchanging on to clay interlayer sites, on the basis that the cation-exchange acid removed the released cations from the solution and thus lessened their effect on the interlayer chemistry of the clay. The experiment is shown schematically in Fig. 1. An aqueous-phase leaching solution, consisting of acetic acid buffered at ph 6.5 by NaOAc, was added (200 ml) followed by an equal volume of an organic phase containing the cation-exchange acid. The organic phase consisted of the cation-exchange acid dissolved in ethyl-ether in the ratio 5% wt/vol of acid to solvent. Ethyl-ether was chosen as the solvent as it is partially soluble in water and water is partially soluble in it, thereby allowing exchange between the two phases to occur readily. The cation-exchange acid chosen was pentadecafluorooctanoic acid RCOzH

3 Smectite extraction from calcareous rocks 75 ~o~..c~.+. o-~ / / -~, Organic phase OH OH 1 Sample Fro. 1. Schematic diagram for cation exchange method. (R = (CF2)6CF3). This acid is selective towards Ca 2+ and Mg 2+ (Coleman et al., 1962) which are major elements in carbonates. The general reactions of this process are: CaCO3 + 2H + > H20 + CO 2 q- Ca 2+ (1) 2RfOzH(org) + CaZ+(aq) < > 2H+(aq) + ((RfO2-)2CaZ+}(org) (2) Equation (2) shows the exchange of Ca 2+ across the interface for 2H + lost by the dissolution process in equation (1). n this way the aqueous leaching solution remains relatively undepleted during the process, unlike the other methods. The process took 8 h to complete, with constant stirring. The sample was then carefully washed and the clay separated by sedimentation. Preparation of samples for analysis The initial clay, a clay sample washed with deionized water for 0.5 h, and the extracted clays were allowed to air-dry and each separated into four subsamples. Two orientated-clay tiles were made for each of the clay samples for XRD analysis using a Philips PWl710 diffractometer and Cu-Kolradiation. For one tile per sample an air-dried trace was run from 2-20~ For the second tile, successive traces were run from 2-14~ after allowing the tile to air-dry, after glycollation for 4 h, and after heating at 375~ for 1 h. The bulk chemistry of the clay was determined by electron microprobe analysis and by wet chemical methods. For the former, the clays were mounted on carbon-coated A1 stubs and analysed chemically using a JEOL JSM-840 SEM fitted with a Link Systems energydispersive X-ray spectrometer. The clay coating on the stub was 2 mm thick to prevent penetration of the incident electron beam to the A1 stub itself. The wet chemical method was used for the determination of Li which cannot be detected by the energy-dispersive X-ray spectrometer. The extracted clays were dissolved in HF and the solution analysed by inductively-coupled plasma (CP) spectroscopy. The exchangeable K + content of the clays was determined by washing the clays for

4 76 R. J. Cook 3 days with 1 M BaC12 solution which was changed twice a day. Barium was chosen as the exchangeable cation because it will replace all other cations commonly found on clays including K + (Carroll, 1959). All the washings were collected for K + analysis by CP. XRD analysis RESULTS AND DSCUSSON The XRD traces for the initial and extracted clays are shown in Figs. 2 and 3. Fig. 2 shows the characteristic behaviour of smectites in all the traces: expansion of the 001 peak to 17 after glycollation for 4 h and a collapse to 10 A after heating at 375~ for 1 h. Similar t tl tl!~ i ~ lit'\ Traces m Air Dried... Glycolated 375oc 3 20,. 15 tl,,'/', ', tl: :~',-,,,/, ; \, t/',.,'/ ~\ -,,,, ttt/,, x, ",...~, \_<,..,, 3 2e ~ !il fi,, :/',,'r ~', L,',, \ ~'a ; 1~ Cation Exchange i/~ // '~ HC t:;i/ii ~;',,,,! 3 2e i3 3 2e Fi6.2. XRD traces for initial and extracted clays. Cu-Ko~ radiation. 15

5 Smectite extraction from calcareous rocks 77 \ LiOAc NaOAc Cation Exchange HC Fro. 3. XRD traces of air-dried initial and extracted clays. Cu-K0: radiation. 20 behaviour is seen for all the extracted clay traces as well as the initial clay trace. The only difference is seen when the air-dried traces are compared (Fig. 3); the main peak for the extracted clays, although in the same position, is sharper. This phenomenon can be related to the interlayer cations on the clays. n the initial clay the broad peak is due to a mixture of single and double water layer hydrates in the interlayers relating to K + and Ca 2+, respectively. With the treated clays the main interlayer cations (Ca 2+, Ca ~+ and Na +, or H form double water layer hydrates only, resulting in a sharper peak between 14 and 15 A (Barshad, 1950; Suquet et al., 1975; Cowking et al., 1983). Apart from this sharpening of the air-dried peak, however, the XRD traces for the clays are basically unaltered by any of the techniques. Bulk chemical analysis The results of the bulk chemical analyses are shown in Table 1. The cations have been assigned in appropriate amounts to tetrahedral, octahedral and interlayer positions to indicate chemical changes in the structural unit caused by any of the processes. t can be seen from Table 1 that clay samples washed with water or extracted by the use of either LiOAc, NaOAc or the cation exchange method show no significant variation in their chemical composition from that of the initial sample. For the HCl-extracted clay, however, there appears to be an enrichment of SiO2. f a constant SiO2 content is assumed and the results are corrected for this, there appears to have been leaching of Mg from octahedrat

6 m 78 R. J. Cook TABLE 1. Structural formulae of clays based on 22 oxygens. Average of 11 analyses per clay sample. Error in brackets given as maximum deviation from mean. HC Water wash LiOAc NaOAc Cation (1) (2) Tet. Si (0.257) (0.331) (0-211) (0.311) (0-388) A (0.039) (0.024) (0.041) (0-033) (0.037) -- Oct. A Mg (0.255) (0-421) (0.179) (0.433) (0.240) Ti (0.003) (0-012) (0-005) (0-004) (0.008) Mn (0.004) (0.008) (0.008) (0.004) (0.005) Fe (0.009) 0,039 (0.020) (0.015) (0.024) (0.020) Li (0.016) (0.012) (0.008) (0.002) (0.004) nt. Ca (0.023) (0.137) (0-031) (0.133) (0-105) K (0.053) (0.035) (0-011) (0.031) (0-037) Na (0.011) (0.081) (0-049) (0-020) (0.051) (0-371) (0-007) (0.358) (o.oo7) (0.004) (0.013) (0.009) (0-017) (0-038) (0-056) --initial clay composition. Water wash--clay after washing with water. LiOAc--clay extracted by lithium acetate method. NaOAc--clay extracted by sodium acetate method. Cation--clay extracted by cation-exchange acid method. HC--clay extracted by HC method; actual result (1), and corrected assuming constant silica (2). TABLE 2. Exchangeable K + results. Exchangeable % exchangeable Method K+/p.p.m. K + retained Water wash Water wash LiOAc LiOAc NaOAc NaOAc HC HC Cation exchange Cation exchange 22,260 21,940 22,470 22,580 9,497 10,153 2,494 1,834 3,752 2,635 1,329 1,109 1,301 1, sites in the clay. t is interesting to note that this change in structural chemistry occurred without significantly altering the XRD trace of the HC1 extracted clay. Exchangeable cation results' The variation in the exchangeable or interlayer cations can be seen in Table 1 and the effect on the exchangeable K in particular can be seen in Table 2. Although the results in

7 Smectite extraction from calcareous rocks 79 Table 2 relate to K only, they do indicate that loss of exchangeable cations occurs during the process. The best result was produced by the NaOAc method which showed retention of between 11 and 17% of exchangeable K. This result, however, is still not good and none of the methods is satisfactory in leaving the exchangeable K content unaltered. t should also be noted that washing the clay sample with deionized water for 0.5 h produced a loss of over 50% of the exchangeable K. This would tend to suggest that preservation of exchangeable cations on clays would be difficult if the technique involves solution methods. CONCLUSONS None of the methods tried affected the XRD traces of the clays other than causing a sharpening of the 001 peak of the air-dried clay. From the XRD results it would appear that there is nothing to choose between the methods. On the basis of the XRD results alone, therefore, HC1 would appear to be the best method because it takes only 1 h compared with 8 h for the next fastest. From the bulk chemistry results, however, it is seen that the use of HC1 causes the stripping of cations from the structure, whereas the use of the buffered weak acids or the cation-exchange acid does not appear to alter the bulk chemistry of the clay. When considering the exchangeable cation results, there is again little to chose between any of the methods; they are all equally poor in the preservation of the exchangeable cations. n comparing the methods, those using buffered weak acid or the cation-exchange acid would be preferable to the HC1 method as no damage occurred to the clay structure. The cation-exchange method may be preferable to either of the buffered weak acid methods as it is faster. The use of a cation exchanger, however, makes the process much more expensive. Comparing the two weak acid methods is hampered by the difference in methodology. Extractions have been carried out using single additions of NaOAc-buffered acid and there is no difference in the results over the multiple addition method. n the author's opinion the NaOAc-buffered acid, either using single or multiple additions, is an efficient and simple method for the dissolution of carbonate with minimal amount of damage occurring to the clay. ACKNOWLEDGMENTS This work was undertaken whilst in receipt of a Natural Environmental Research Council studentship. would like to thank Dr B. Sellwood and especially Dr A. Parker for encouragement given with this work. This paper is Reading University PRS Contrib. No REFERENCES BAN D.C. & SMTH B.F.L. (1987) Chemical analysis. Pp in: A Handbook of Determinative Methods in Clay Mineralogy (M.J. Wilson, editor). Blackie & Son, Glasgow & London. BARSHAD. (1950) The effect of the interlayer cations on the expansion of the mica type of crystal lattice. Am. Miner. 35, CARROLL, D. (1959) on exchange in clays and other minerals. Bull. Geol. Soc. Am. 70, CHAUSSDON J. (1962) The exchange complex: The general laws of anion and cation exchange. Pp in: Constituents and Properties of Soils (M. Bonneau & B. Souchier, editors). Academic Press, London. COLEMAN C.F., BLAKE JR. C.A. & BROWN K.B. (1962) Analytical potential of separation by liquid ion exchange. Talanta 9,

8 80 R. J. Cook COWKNG A., WLSON M.J., TAT J.M. & ROBERTSON R.H.S. (1983) Structure and swelling of fibrous and granular saponitic clay from Orrock Quarry, Fife, Scotland. Clay Miner. 18, 49~54. ESLN6ER E. & PEVEAR D. (Editors) (1988) Clay Minerals for Petroleum Geologists and Engineers: SEPM Short Course No. 22, pp. A-28. SEPM, USA. JACKSON M.L. (1969) Soil Chemical Analysis--Advanced Course. 2nd ed., pp Published by the author, Madison, Wisconsin. OSTROM M.E. (1961) Separation of clay minerals from carbonate rocks by using acid. J. Sed. Pet. 31, PETERSON M.N.A. (1961) Expandable chloritic clay minerals from Upper Mississipian carbonate rocks of the Cumberland Plateau in Tennessee. Am. Miner. 46, RAY S., GAULT H.R. & DODO C.G. (1957) The separation of clay minerals from carbonate rocks. Am. Miner. 42, 681~586. SUQUET H., CALLE C. DE LA & PEZERAT H. (1975) Swelling and structural organization of saponite. Clays Clay Miner. 23, 1-9.