LAB 2 HARDNESS TEST OBJECTIVES INTRODUCTION BRINELL HARDNESS TEST
|
|
- Moses Briggs
- 7 years ago
- Views:
Transcription
1 LAB 2 HARDNESS TEST OBJECTIVES (1) Make Brinell, Vickers and Rockwell hardness measurements on different materials specimens. (2) Compare the measurements in hardness with each other. INTRODUCTION Hardness can be defined as resistance to penetration, resistance to abrasion, resistance to scratching, or resistance to cutting. These are related in that they all require plastic flow of the material. A variety of tests for hardness are in use, depending on which of the above situations is of most interest. Material properties, such as hardness can be altered to desired levels by various heat treatment procedures. Heat treatments affect the microstructure of the metal. Detailed descriptions of the changes to the microstructure can be found in material science (1) lecture notes. This experiment will include Brinell, Vickers and Rockwell tests which measure resistance to penetration. The amount of deformation that occurs when a small, hard steel ball or diamond point is pressed into a material surface at some designated load is the measure of the hardness of the material. BRINELL HARDNESS TEST The Brinell test for this experiment uses steel ball with different diameters which is pressed into a specimen by a different load that is maintained for 15 to 30 seconds. The Brinell hardness number (BHN) is calculated by: Where: P is the test load [kg] D is the diameter of the ball [mm] d is the average impression diameter of indentation [mm] Since the Brinell number is based on the area of indentation, the diameter of the indentation must be measured. This is done with a microscope. The scale seen through Hardness Test 1/5
2 the microscope is in millimeters. The larger diameter indentation corresponds to a softer material and lower Brinell number. VICKERS HARDNESS TEST The Vickers hardness test method consists of indenting the test material with a diamond indenter, in the form of a right pyramid with a square base and an angle of 136 degrees between opposite faces subjected to a load of 1 to 100 kgf. The full load is normally applied for 10 to 15 seconds. The two diagonals of the indentation left in the surface of the material after removal of the load are measured using a microscope and their average calculated. The area of the sloping surface of the indentation is calculated. The Vickers hardness is the quotient obtained by dividing the kgf load by the square mm area of indentation. P is the load and it can be varied from 1 to 1000 grams d is the average diagonal diameter of indentation [mm] When the mean diagonal of the indentation has been determined the Vickers hardness may be calculated from the above formula. The Vickers hardness should be reported like 800 HV/10, which means a Vickers hardness of 800, was obtained using a 10 kgf force. The advantages of the Vickers hardness test are that extremely accurate readings can be taken, and just one type of indenter is used for all types of metals and surface treatments. ROCKWELL HARDNESS TEST The penetrators for the Rockwell hardness tester range from 1/2-inch diameter steel balls to very small diamond (brale) tips (points). The smaller points are used for harder materials that have a greater resistance to indentation. There are various force scales used for various materials. The Rockwell B and Rockwell C scales will be used for this experiment. The Rockwell B scale is suitable for soft engineering metals, and the Rockwell C scale is appropriate for hard engineering metals. Each scale requires a specified tip and load. The B scale uses a 1/16- inch diameter hard steel ball and a 100- kg load. The C scale uses a conical diamond point and a 150-kg load. Hardness Test 2/5
3 To perform the Rockwell tests, the penetrator is pressed against the specimen with an initial 10-kg preload to properly seat the penetrator. The remaining load is applied gradually after the dial on the hardness tester has been zeroed. After the penetrator has stopped moving into the specimen, the final position of the dial pointer indicates the Rockwell hardness number that is related to the depth of penetration. There are numerous scales in Rockwell test, which are made possible by the combination of different loads and indenters. The scales are identified by letters and the common scales range from A through K, with I and J left out, as given in the following table Hardness Test 3/5
4 MATERIALS TO BE TESTED Different materials specimens will be tested in this laboratory experiment namely: aluminum alloy, carbon steel, stainless steel, Al-alloy, commercial pure copper and brass. The hardness of mild-steel washer will also be tested to check the validity of Brinell hardness test. EQUIPMENT TO BE USED: Zwick/ZHU Universal hardness tester up to kg STUDENT WORK Selected students will be invited to perform Brinell and Rockwell hardness test, instructor will do perform Vickers test in order to avoid the diamond pyramid damaging that could be taken place. For Brinell experiment, student has to calculate the BHN and depth of impression (h) through the following formulas for each material tested: For Vickers experiment, student has to calculate the VHN through the following formula for each material tested: For Rockwell experiment, student has to calculate the depth due to major load (t) through the following formulas for each material tested: Hardness Test 4/5
5 Rockwell Hardness Test Vickers Hardness Test Brinell Hardness Test Results: Exp. Type Material Mild steel Stainless steel Al alloy Pure copper Brass Steel washer d 1 [mm] d 2 [mm] d=(d1+d2)/2 [mm] P [kg] D [mm] H [mm] [mm] d/d H/h d 1 [mm] d 2 [mm] d=(d 1 +d 2 )/2 [mm] P [kg] R C (diamond & 140 kg) R B (1/16 & 90 kg) R E (1/8 & 90 kg) R H (1/8 & 50 kg) Comment: Hardness Test 5/5
PRACTICAL HARDNESS TESTING MADE SIMPLE. Table of Contents 1. GENERAL 1 2. INTRODUCTION 3 3. BRINELL HARDNESS TESTING 9 4. VICKERS HARDNESS TESTING 14
Table of Contents Page 1. GENERAL 1 2. INTRODUCTION 3 3. BRINELL HARDNESS TESTING 9 4. VICKERS HARDNESS TESTING 14 5. ROCKWELL HARDNESS TESTING 17 6. INFORMATIONS 22 i 1. GENERAL Important facts and features
More informationDescription of mechanical properties
ArcelorMittal Europe Flat Products Description of mechanical properties Introduction Mechanical properties are governed by the basic concepts of elasticity, plasticity and toughness. Elasticity is the
More informationThe measuring of the hardness
The measuring of the hardness In the field of mechanics one often meets with the notion of "hardness", and in fact the hardness is a fundamental characteristic to determine whether a certain material is
More informationProperties of Materials
CHAPTER 1 Properties of Materials INTRODUCTION Materials are the driving force behind the technological revolutions and are the key ingredients for manufacturing. Materials are everywhere around us, and
More informationME 354, MECHANICS OF MATERIALS LABORATORY
ME 354, MECHANICS OF MATERIALS LABORATORY 01 Januarly 2000 / mgj MECHANICAL PROPERTIES AND PERFORMANCE OF MATERIALS: HARDNESS TESTING* PURPOSE The purpose of this exercise is to obtain a number of experimental
More informationMENG 302L Lab 1: Hardness Testing
Introduction: A MENG 302L Lab 1: Hardness Testing Hardness Testing Hardness is measured in a variety of ways. The simplest is scratch testing, in which one material scratches or is scratched by another.
More informationHardness Testing at Elevated Temperatures. SJ Shaffer, Ph.D. Bruker-TMT Steven.shaffer@bruker-nano.com
Hardness Testing at Elevated Temperatures SJ Shaffer, Ph.D. Bruker-TMT Steven.shaffer@bruker-nano.com Outline What is Hardness? How is Hardness Measured? Overview of Hardness Test Methods Hardness Testing
More informationPenetration Testing for Material Hardness
Penetration Testing for Material Hardness Purpose The hardness of various materials, ranging from metals to plastics to rubber, can be an important design property. Consider, for instance, a camshaft in
More informationLABORATORY EXPERIMENTS TESTING OF MATERIALS
LABORATORY EXPERIMENTS TESTING OF MATERIALS 1. TENSION TEST: INTRODUCTION & THEORY The tension test is the most commonly used method to evaluate the mechanical properties of metals. Its main objective
More informationVeMet, Utrecht, NL «Solution in Wear Protection» 26.10.2011 Dipl.-Ing. Wolfgang Leichnitz. Quit
VeMet, Utrecht, NL «Solution in Wear Protection» 26.10.2011 Dipl.-Ing. Wolfgang Leichnitz Quit Theory and Practice of Wear Definition In materials science, wear is the erosion of material from a solid
More informationHow To Test A Rockwell Type Hardness Tester
ROCKWELL TYPE HARDNESS TESTER CV-600A TM Ready-to-test analogue Rockwell type tester with lever system for direct load application Basic regular Rockwell type tester offering accuracy, reliability and
More informationTechCut 4 Precision Low Speed Saw
Product Brochure TechCut 4 Precision Low Speed Saw 3" - 6" Blade Range Digital Speed Display 1-Micron Sample Indexing Spring-Loaded Dressing Stick Attachment All Aluminum & Stainless Steel Construction
More informationUniversity of Portland School of Engineering LABORATORY OUTLINE: TENSILE TESTING OF STEEL & ALUMINUM ALLOYS (ASTM E8)
TENSILE TESTING OF STEEL & ALUMINUM ALLOYS (ASTM E8) To carry out a standard tensile test on specimens of a hot rolled steel (AISI 1045), Type 2024- T351 aluminum, polymers (UHMW-PE, acrylic) and, from
More informationChapter Outline. Mechanical Properties of Metals How do metals respond to external loads?
Mechanical Properties of Metals How do metals respond to external loads? Stress and Strain Tension Compression Shear Torsion Elastic deformation Plastic Deformation Yield Strength Tensile Strength Ductility
More information5. MECHANICAL PROPERTIES AND PERFORMANCE OF MATERIALS
5. MECHANICAL PROPERTIES AND PERFORMANCE OF MATERIALS Samples of engineering materials are subjected to a wide variety of mechanical tests to measure their strength, elastic constants, and other material
More informationCEEN 162 - Geotechnical Engineering Laboratory Session 7 - Direct Shear and Unconfined Compression Tests
PURPOSE: The parameters of the shear strength relationship provide a means of evaluating the load carrying capacity of soils, stability of slopes, and pile capacity. The direct shear test is one of the
More informationUnmatched Metal Hardness Testing
Unmatched Metal Hardness Testing The Equostat 3 hardness tester can be connected both to the portable Equotip 3 platform and directly to a PC, with graphic user guidance Hardness Measurements made easy
More informationIntroduction to Hardness Testing
1 Introduction to Hardness Testing Hardness has a variety of meanings. To the metals industry, it may be thought of as resistance to permanent deformation. To the metallurgist, it means resistance to penetration.
More informationExperiment: Crystal Structure Analysis in Engineering Materials
Experiment: Crystal Structure Analysis in Engineering Materials Objective The purpose of this experiment is to introduce students to the use of X-ray diffraction techniques for investigating various types
More informationHR-15C Rockwell Hardness Tester
Equipment Type: Model: Rockwell Hardness Tester HR-15C Electrical Requirements : Frequency: 110 or 220 Volts (single-phase) 50/60 Hz Manual Revision Date: November 25, 2011 Contents Warranty PAGE ii 1.0
More informationPortable Hardness Tester
Portable Hardness Tester Large, easy to read display with backlight Highly accurate ± 4 HL Automatic correction for impact direction Converts to all common hardness scales (,,,, HS, R m ) Light weight
More informationAnodes and Misc Equipment
Anodes and Misc Equipment Application: Platinised Titanium Anodes Platinised titanium anodes are recommended for use in the following electrolytic processes:- Precious metal electroplating - e.g. Au, Pt,
More informationMobile Hardness Testing
GE Inspection Technologies Mobile Hardness Testing Application Guide for Hardness Testers Dr. Stefan Frank GE Inspection Technologies 2 Ultrasonics Mobile Hardness Testing Application Guide Dr. Stefan
More informationCHAPTER 7 DISLOCATIONS AND STRENGTHENING MECHANISMS PROBLEM SOLUTIONS
7-1 CHAPTER 7 DISLOCATIONS AND STRENGTHENING MECHANISMS PROBLEM SOLUTIONS Basic Concepts of Dislocations Characteristics of Dislocations 7.1 The dislocation density is just the total dislocation length
More informationSection 4: NiResist Iron
Section 4: NiResist Iron Section 4 Ni-Resist Description of Grades...4-2 201 (Type 1) Ni-Resist...4-3 202 (Type 2) Ni-Resist...4-6 Stock Listings...4-8 4-1 Ni-Resist Description of Grades Ni-Resist Dura-Bar
More informationCORRELATION BETWEEN HARDNESS AND TENSILE PROPERTIES IN ULTRA-HIGH STRENGTH DUAL PHASE STEELS SHORT COMMUNICATION
155 CORRELATION BETWEEN HARDNESS AND TENSILE PROPERTIES IN ULTRA-HIGH STRENGTH DUAL PHASE STEELS SHORT COMMUNICATION Martin Gaško 1,*, Gejza Rosenberg 1 1 Institute of materials research, Slovak Academy
More informationMeasurement of Length, Mass, Volume and Density
Measurement of Length, Mass, Volume and Density Experimental Objective The objective of this experiment is to acquaint you with basic scientific conventions for measuring physical quantities. You will
More informationExperiment: Heat Treatment - Quenching & Tempering
Experiment: Heat Treatment - Quenching & Tempering Objectives 1) To investigate the conventional heat treatment procedures, such as quenching and annealing, used to alter the properties of steels. SAE
More informationMechanical Properties of Metals Mechanical Properties refers to the behavior of material when external forces are applied
Mechanical Properties of Metals Mechanical Properties refers to the behavior of material when external forces are applied Stress and strain fracture or engineering point of view: allows to predict the
More informationREFERENCES. As an example..
Mechanical Engineering Department University of Massachusetts Lowell Lowell, Massachusetts 01854 978-934-4000 To: Students in Mechanical Engineering Classes with Report Writing Requirements From: Professor
More informationHR-200/300/400/500 Series
Test Equipment Rockwell Hardness Testing Machines HR-200/300/400/500 Series Bulletin No. 2025 Four economical Rockwell Hardness Testing Machines to HR-210MR Order No. 963-220-10A Rockwell Hardness Testing
More informationCutting Tool Materials
Training Objectives After watching the video and reviewing this printed material, the viewer will gain knowledge and understanding of cutting tool metallurgy and specific tool applications for various
More informationMassachusetts Institute of Technology Department of Mechanical Engineering Cambridge, MA 02139
Massachusetts Institute of Technology Department of Mechanical Engineering Cambridge, MA 02139 2.002 Mechanics and Materials II Spring 2004 Laboratory Module No. 5 Heat Treatment of Plain Carbon and Low
More informationAvailable Memory 4 GB 8 GB. Product Specifications. Product Material. Weight
Model F-002 A contemporary key shape design makes this model ideal most industries. Available s PMS # Silver : High Impact Plastics with aluminum Alloy surface : 9 Grams Inches: 2.32" x 1.02" x 0.3" Millimeters:
More informationSolution for Homework #1
Solution for Homework #1 Chapter 2: Multiple Choice Questions (2.5, 2.6, 2.8, 2.11) 2.5 Which of the following bond types are classified as primary bonds (more than one)? (a) covalent bonding, (b) hydrogen
More informationEFFECT OF HARDNESS VARIATION ON SURFACE INTEGRITY OF CARBURIZED P20 STEEL
Copyright 2013 by ABCM EFFECT OF HARDNESS VARIATION ON SURFACE INTEGRITY OF CARBURIZED P20 STEEL Franciele Litvin franciele-litvin@hotmail.com Larissa França Madeira Manfrinato lari_manfrinato@hotmail.com
More informationUsing Equotip Hardness Test Blocks Abstract 1. Introduction 2. Verification of Leeb hardness testers according to standards
Using Equotip Hardness Test Blocks Heinz-Horst Pollok, consultant for material testing and instrument electronics (Cologne, Germany) Dr. Ralph T. Mennicke, product manager for material testing, Proceq
More informationVERZUS 750CCD Universal Hardness Tester
VERZUS 750CCD Universal Hardness Tester UNIVERSAL HARDNESS TESTERS VERZUS 750CCD Microscope with high resolution CCD camera Industrial 8.4 LCD touch screen for easy tester operation, showing the force
More information1 1.5" (38 mm) Diameter
CAB Cable Rings and Saddles are offered in all sizes and materials. Please call or email if your preferred item is not listed on these charts. TABLE OF CONTENTS Part Numbers for 1.5 inch (38mm) diameter
More informationCOATED CARBIDE. TiN. Al 2 O 3
COATED CARBIDE GENERAL INFORMATION CVD = Chemical Vapour Deposition coated grades GC2015, GC2025, GC2135, GC235, GC3005, GC3015, GC3020, GC3025, GC3115, GC4015, GC4025, GC4035, S05F, and CD1810. PVD =
More informationHOSE, TUBE, AND PIPE CLAMPS
hose, tube & clamp B/W pages 24/6/08 9:28 AM Page 2 HOSE, TUBE, AND PIPE CLAMPS TABLE OF CONTENTS Introduction 3 Construction 3 Application 3 Mounting 3 Standard Duty Clamps (HRL) Arrangements 4 Dimensions
More informationImpact testing ACTIVITY BRIEF
ACTIVITY BRIEF Impact testing The science at work Impact testing is of enormous importance. A collision between two objects can often result in damage to one or both of them. The damage might be a scratch,
More informationTypes of Strain. Engineering Strain: e = l l o. Shear Strain: γ = a b
Types of Strain l a g Engineering Strain: l o l o l b e = l l o l o (a) (b) (c) Shear Strain: FIGURE 2.1 Types of strain. (a) Tensile. (b) Compressive. (c) Shear. All deformation processes in manufacturing
More informationCLASSIFICATIONS OF INJECTION MOLDS
CLASSIFICATIONS OF INJECTION MOLDS General Notes The following classifications are guidelines to be used in obtaining quotations and placing orders for uniform types of molds. It is our desire, through
More informationThere are as many reasons to test metals as there are metals:
Testing Their Mettle Metals testing procedures ensure quality in raw materials and finished products BY BILL O NEIL, ADRIAN RIDDICK, FRANK LIO, PAUL KING, CHRIS WILSON, AND PATTY HARTZELL There are as
More informationPROPERTIES OF MATERIALS
1 PROPERTIES OF MATERIALS 1.1 PROPERTIES OF MATERIALS Different materials possess different properties in varying degree and therefore behave in different ways under given conditions. These properties
More informationULTRASONIC THICKNESS GAUGE TT100/110/120/130
ULTRASONIC THICKNESS GAUGE TT100/110/120/130 TT100 TT110 Portable size and easy operation Suitable for any metallic and non-metallic materials ultrasonic can go through Self-compensating of nonlinearity
More informationSERIE NEMESIS 9000 TM
Load cell, closed loop, linear force actuator, fixed workpiece position Flexible modular design Force configuration 250kgf/2.45kN 750kgf/7.35kN 3000kgf/29kN Introduction NEMESIS 9000 Series, represents
More informationProperties of Knife Blade Materials
Properties of Knife Blade Materials Articles in knife magazines and discussions on the Internet concerning knife blade steels are getting pretty technical these days. The problem is that many terms are
More informationMT90 Series MicroHardness Traverse Testing System
MT90 Series MicroHardness Traverse Testing System A Unique System with Unrivaled Speed And Accuracy in Case Depth Measurement. MT90 Microhardness Traverse Testing System Unrivaled Speed And Accuracy in
More informationTubing Data. Contents. Tubing Selection. Tubing Handling. Tubing Material. Tubing Outside Diameter Hardness. Tubing Wall Thickness
www.swagelok.com Tubing Data Contents Tubing Selection... 1 Tubing Handling.... 1 Gas Service... 2 Tubing Installation.... 2 Suggested Allowable Working Pressure Tables Carbon Steel Tubing... 3 Stainless
More informationPin & Vee Block Test Machine
Pin & Vee Block Test Machine Picture of the apparatus Used in Standard Test Methods ASTM Standards D 2670, D2626, D3233, D5620 Federal Test Methods FTM-791-3807.1, FTM-791-3812.1 Chrysler Corporation 461-C-84-01,
More informationTensile Testing of Steel
C 265 Lab No. 2: Tensile Testing of Steel See web for typical report format including: TITL PAG, ABSTRACT, TABL OF CONTNTS, LIST OF TABL, LIST OF FIGURS 1.0 - INTRODUCTION See General Lab Report Format
More informationCOASTAL BEND COLLEGE WELDING SYLLABUS (Revise 11/13) Intermediate Shielded Metal Arc Welding (SMAW)
COASTAL BEND COLLEGE WELDING SYLLABUS (Revise 11/13) WLDG 1457: Intermediate Shielded Metal Arc Welding (SMAW) Semester Hours: 4 Textbook: Course Description: Course Learning Outcomes: Supplementary Materials:
More informationFABRICATION AND CHARACTERIZATION OF
FABRICATION AND CHARACTERIZATION OF CONDUCTING POLYMER COMPOSITE Ritu Tomar 1 and Dr. Chirag R Sharma 2 1 Department of Engineering Physics, Sambhram Institute of Technology and Research Scholar, Nitte
More informationGeneral Guidelines for Building Aluminum Production Injection Molds
General Guidelines for Building Aluminum Production Injection Molds Using 7000 series Aluminum Mold Plate By David Bank Aluminum Injection Mold Company Rochester, New York 1 Introduction This high strength
More informationWhy HARDOX in tipping trailers?
Why HARDOX in tipping trailers? 1. Higher elastic limit and higher ultimate stress 2. Longer life span (higher resistance to deformation, abrasion and scratching) 3. Excellent resistance to impact 4. Less
More informationInspection Methods Overview and Comparison
Inspection of Metals Understanding the Basics Copyright 2013 ASM International F.C. Campbell, editor All rights reserved www.asminternational.org CHAPTER 1 Inspection Methods Overview and Comparison INSPECTION
More informationVICKERS HARDNESS TESTER. HBS HBW Kc
ICKERS HARDNESS TESTER H HK HBS HBW Kc Clean Touch Panel coordinated with highly integrated PC board. Measuring procedures, conditions and data are displayed clearly. (F-800 Series) Accurate light load
More informationabc FACILITIES LIST East Carolina Metal Treating, Inc. INTRODUCTION
East Carolina Metal Treating, Inc. 1117 Capital Blvd. Raleigh, NC 27603 919-834-2100 fax 919-833-1764 www.ecmtinc.com FACILITIES LIST INTRODUCTION East Carolina Metal Treating, a commercial heat treating
More informationTHE INFLUENCE OF STEEL GRADE AND STEEL HARDNESS ON TOOL LIFE WHEN MILLING IN HARDENED TOOL STEEL
THE INFLUENCE OF STEEL GRADE AND STEEL HARDNESS ON TOOL LIFE WHEN MILLING IN HARDENED TOOL STEEL S. Gunnarsson, B. Högman and L. G. Nordh Uddeholm Tooling AB Research and Development 683 85 Hagfors Sweden
More informationME2256 STRENGTH OF MATERIALS LABORATORY MANUAL
ME2256 STRENGTH OF MATERIALS LABORATORY MANUAL FOR FOURTH SEMESTER B.E MECHANICAL ENGG Academic Year-2013-2014 (FOR PRIVATE CIRCULATION ONLY) ANNA UNIVERSITY -CHENNAI NAME : REG NO : BATCH : DEPARTMENT
More informationObjectives. Experimentally determine the yield strength, tensile strength, and modules of elasticity and ductility of given materials.
Lab 3 Tension Test Objectives Concepts Background Experimental Procedure Report Requirements Discussion Objectives Experimentally determine the yield strength, tensile strength, and modules of elasticity
More informationStructural Bolting. Notice the Grade 5 has a much smaller head configuration and a shorter shank then the A325 structural bolt. Rev.
Structural Bolting ASTM A325 and ASTM A490 are the two U.S. standard structural bolts. When looking at the mechanical requirements of bolts it appears that an ASTM A325 and SAE J429 Grade 5 are identical
More informationA Beginner s Guide to MIG Welding
A Beginner s Guide to MIG Welding MIG Welding Names MIG welding, or MIG, is an acronym for Metal Inert Gas welding. MIG is a commonly used and accepted slang term that was appropriate when the process
More informationWelding. Module 19.2.1
Welding Module 19.2.1 Hard Soldering Hard soldering is a general term for silver soldering and brazing. These are very similar thermal joining processes to soft soldering in as much that the parent metal
More informationParametric analysis of combined turning and ball burnishing process
Indian Journal of Engineering & Materials Sciences Vol. 11, October 2004, pp. 391-396 Parametric analysis of combined turning and ball burnishing process U M Shirsat a* & B B Ahuja b a Department of Mechanical
More informationSTAVAX SUPREME. Stainless tool steel
STAVAX SUPREME Stainless tool steel General Demands placed on plastic mould tooling are increasing. Such conditions require mould steels that possess a unique combination of toughness, corrosion resistance
More informationGENERAL SCIENCE LABORATORY 1110L Lab Experiment 5 THE SPRING CONSTANT
GENERAL SCIENCE LABORATORY 1110L Lab Experiment 5 THE SPRING CONSTANT Objective: To determine the spring constant of a spiral spring Apparatus: Pendulum clamp, aluminum pole, large clamp, assorted masses,
More informationStandard Specification for Stainless Steel Bars and Shapes 1
Designation: A 276 06 Standard Specification for Stainless Steel Bars and Shapes 1 This standard is issued under the fixed designation A 276; the number immediately following the designation indicates
More informationPORTABLE MICROSCOPES PORTABLE MICROSCOPES PORTABLE MICROSCOPES PORTABLE MICROSCOPES PORTABLE MICROSCOPES PORTABLE MICROSCOPES
British Made Portable Microscopes with Image Erection PCB Through - Hole Scope Depthscope Brinell Hardness Impression Microscope Cathode Ray Tube Inspector Portable Video Scope Metallurgical Microscope
More informationMechanical Behavior, Testing, and Manufacturing Properties of Materials
M2_KALP1681_6_SE_C2.QXD 1/12/9 7:46 PM Page 56 C H A P T E R 2 Mechanical Behavior, Testing, and Manufacturing Properties of Materials 2.1 Introduction 56 2.2 Tension 57 2.3 Compression 66 2.4 Torsion
More informationIntroduction. ε 1 θ=55 ε 2. Localized necking Because ν=0.5 in plasticity, ε 1 =-2ε 2 =-2ε 3. ε 3,ε 2
SHEET METALWORKING 1. Cutting Operation 2. Bending Operation 3. Drawing 4. Other Sheet-metal Forming 5. Dies and Presses 6. Sheet-metal Operation 7. Bending of Tube Stock 1 Introduction Cutting and forming
More informationFatigue. 3. Final fracture (rough zone) 1. Fatigue origin. 2. Beach marks (velvety zone)
Fatigue Term fatigue introduced by Poncelet (France) 1839 progressive fracture is more descriptive 1. Minute crack at critical area of high local stress (geometric stress raiser, flaws, preexisting cracks)
More informationGuide rail bracket (for adjustable heads)
(for adjustable heads) Part. 209 40 ø,5 ø10,5 2 2,5 115 15 42 5 11 37 72 4 70 Code 209 / 0754 MATERIALS: Bracket made out of reinforced polyamide black colour. FEATURES: To be used with heads Part.221,
More informationSaw Tooth Design and Tipping Materials
Saw Tooth Design and Tipping Materials Bruce Lehmann, P.Eng, Ph.D. Sr. Engineer, Thin Kerf Technologies Inc. British Columbia, Canada Introduction The purposes of a saw tooth are to: 1. Remove a chip from
More informationSURFACE TREATMENT BOND TEST
Test Procedure for SURFACE TREATMENT BOND TEST Effective Date: March 2011 Published: February 2012 1. SCOPE 1.1. This test procedure is used to determine the bond strength characteristics of the interfaces
More informationMany Products...One Source
PRESSURE GAUGES Dedicated Sales Rep for Your Area 97%Fill Rate Shipping within 24 Hours State of the Art Warehouse System Technical Support Quality Control Program 25 Whaley Avenue Milverton, Ontario N0K
More informationEstimating Welding Preheat Requirements for Unknown Grades of Carbon and Low-Alloy Steels
SUPPLEMENT TO THE WELDING JOURNAL, NOVEMBER 2008 Sponsored by the American Welding Society and the Welding Research Council Estimating Welding Preheat Requirements for Unknown Grades of Carbon and Low-Alloy
More informationCommonwealth of Pennsylvania PA Test Method No. 632 Department of Transportation October 2013 5 Pages LABORATORY TESTING SECTION. Method of Test for
Commonwealth of Pennsylvania PA Test Method No. 632 Department of Transportation 5 Pages LABORATORY TESTING SECTION Method of Test for TIME OF SETTING OF CONCRETE MIXTURES BY PENETRATION RESISTANCE 1.
More informationPhysics Lab Report Guidelines
Physics Lab Report Guidelines Summary The following is an outline of the requirements for a physics lab report. A. Experimental Description 1. Provide a statement of the physical theory or principle observed
More informationModule 3 Machinability. Version 2 ME, IIT Kharagpur
Module 3 Machinability Lesson 1 Cutting Tool Materials of common use Instructional Objectives At the end of this lesson, the students will be able to (i) Identify the needs and cite the chronological development
More informationABRASION RESISTANT STEEL PIPING SYSTEMS FOR SLURRY TRANSPORT IN MINING APPLICATIONS
ABRASION RESISTANT STEEL PIPING SYSTEMS FOR SLURRY TRANSPORT IN MINING APPLICATIONS Robert E. Klemm, P.E. UltraTech, Port Washington, WI 53074-308 USA ABSTRACT Various metallurgical and material enhancements
More informationTechnical Data BLUE SHEET. Martensitic. stainless steels. Types 410, 420, 425 Mod, and 440A GENERAL PROPERTIES APPLICATIONS PRODUCT FORM
Technical Data BLUE SHEET Allegheny Ludlum Corporation Pittsburgh, PA Martensitic Stainless Steels Types 410, 420, 425 Mod, and 440A GENERAL PROPERTIES Allegheny Ludlum Types 410, 420, 425 Modified, and
More informationTheory of Heating by Induction
CHAPTER 2 Theory of Heating by Induction INDUCTION HEATING was first noted when it was found that heat was produced in transformer and motor windings, as mentioned in the Chapter Heat Treating of Metal
More informationTensile Testing Laboratory
Tensile Testing Laboratory By Stephan Favilla 0723668 ME 354 AC Date of Lab Report Submission: February 11 th 2010 Date of Lab Exercise: January 28 th 2010 1 Executive Summary Tensile tests are fundamental
More informationGREY RELATIONAL ANALYSIS TO OPTIMIZE WELDING PARAMETERS FOR DISSIMILAR SHEETS OF MATERIAL IN RESISTANCE SPOT WELDING
International Journal of Mechanical Engineering and Technology (IJMET) Volume 6, Issue 11, Nov 2015, pp. 23-32, Article ID: IJMET_06_11_003 Available online at http://www.iaeme.com/ijmet/issues.asp?jtype=ijmet&vtype=6&itype=11
More informationCATHODIC PROTECTION SYSTEM DESIGN
CATHODIC PROTECTION SYSTEM DESIGN Presented By DENIS L ROSSI P.E. CORROSION ENGINEER New England C P Inc. Corrosion Fundamentals What is corrosion? It is defined as the degradation or deterioration of
More informationROLL PASS DESIGN EVAULUATION USING SOFTWARE APPLICATION ARINDAM MUKHERJEE PROJECT MANAGEMENT CELL UNDP/GEF PROJECT (STEEL)
ROLL PASS DESIGN EVAULUATION USING SOFTWARE APPLICATION ARINDAM MUKHERJEE PROJECT MANAGEMENT CELL UNDP/GEF PROJECT (STEEL) OBJECTIVE OF ROLL PASS DESIGN Steel sections are generally rolled in several passes,
More informationLapping and Polishing Basics
Lapping and Polishing Basics Applications Laboratory Report 54 Lapping and Polishing 1.0: Introduction Lapping and polishing is a process by which material is precisely removed from a workpiece (or specimen)
More informationMATHEMATICS FOR ENGINEERING BASIC ALGEBRA
MATHEMATICS FOR ENGINEERING BASIC ALGEBRA TUTORIAL 4 AREAS AND VOLUMES This is the one of a series of basic tutorials in mathematics aimed at beginners or anyone wanting to refresh themselves on fundamentals.
More informationBUMAX. REYHER your partner for the BUMAX range
BUMAX high-tensile stainless steel fasteners REYHER your partner for the BUMAX range Strongest stainless steel fasteners in the world BUMAX 88 and BUMAX ready for delivery from stock Wide range of BUMAX
More informationSpecifications for Lightning Protection. ASAE Engineering Practice
Chapter 8: Lightning Specifications for Lightning Protection ASAE safety standards are not laws. They are recommended voluntary standards used by designers, engineers, manufacturers and users of the equipment,
More informationSAMPLE FORMAL LABORATORY REPORT. Fatigue Failure through Bending Experiment Adapted from a report submitted by Sarah Thomas
SAMPLE FORMAL LABORATORY REPORT Fatigue Failure through Bending Experiment Adapted from a report submitted by Sarah Thomas Lab Partners: David Henry and James Johnson ME 498 November 10, 2004 Professor
More informationStone Code Explanation Chart & Surface Finish Guide. Abrasive Types A - Aluminum Oxide C, J - Silicon Carbide DM, DR, DV - Diamond NM, NR - CBN
Stone Code Explanation Chart & Surface Finish Guide K8 A 5 7 Series Abrasive Grit Hard Type Size ness 188 Approximate Surface Finish in Micrometers (µm)ra Material Abrasive Type Grit Size 80 150 2 280
More informationNANO INDENTERS FROM MICRO STAR TECHNOLOGIES
NANO INDENTERS FROM MICRO STAR TECHNOLOGIES Micro Star makes a variety of nano indenters following defined standards or custom requested geometries and dimensions. Micro Star calibration laboratory complies
More informationLONG LIFE BEARING SERIES
LONG LIFE BEARING SERIES . Extension of Bearing Life. Mechanism of Flaking FLAKING IN CONTAMINATED LUBRICANT Mechanism Type SURFACE STARTING FLAKING SURFACE FLAKING Abrasion caused by small hard particles
More informationA word to our valued customers,
A word to our valued customers, CV Instruments developed and marketed their first hardness testing instrument in 1971. Now, 35 years later, CV Instruments has taken an important position in the metals
More informationDrive shaft, servicing
Volkswagen Passat B6 - Drive shaft, servicing Стр. 1 из 41 40-7 Drive shaft, servicing Drive shafts, overview I - Assembly overview: Drive axle with CV joint VL100 40-7, Drive axle with CV joint VL100,
More informationChapter 5 - Aircraft Welding
Chapter 5 - Aircraft Welding Chapter 5 Section A Study Aid Questions Fill in the Blanks 1. There are 3 types of welding:, and, welding. 2. The oxy acetylene flame, with a temperature of Fahrenheit is produced
More information