A New Kind of Quiet AU 0920 Acoustic Insulation Acoustical Properties ASTM E-1050 Data Curves Absorption Coefficient Normal Incidence 1.00 0.90 0.80 0.70 0.60 0.50 0.40 0.30 0.20 0.10 AU 0920 10mm 0.00 160 250 400 630 1k 200 315 500 800 1.6k 1.25k 2k 2.5k 4k 3.15k One-Third-Octave Band Center Frequency (Hz) 5k 6.3k Product Description Thinsulate TM AU 0920 Acoustic Insulation is specifically designed for a wide variety of automotive applications: headliners, wheelwells, door panels, door pillars, instrument panels, trunks and many more. It is compressible, nonlinting, lightweight, formable and can be easily die-cut. It uses a polyolefin scrim on one side for fiber protection and consists of 71% polyolefin, 29% polyester. Weight 117 g/m 2 Density 11.7 kg/m 3 Thickness 10mm For more information on Thinsulate AU Acoustic Insulation please call 1-800-221-8211
TH-AU0920 70-0708-4709-3
A New Kind of Quiet AU 1220 Acoustic Insulation Acoustical Properties ASTM E-1050 Data Curves Absorption Coefficient Normal Incidence 1.00 0.90 0.80 0.70 0.60 0.50 0.40 0.30 0.20 0.10 AU 1220 14mm 0.00 160 250 400 630 1k 200 315 500 800 1.6k 1.25k 2k 2.5k 4k 3.15k One-Third-Octave Band Center Frequency (Hz) 5k 6.3k Product Description Thinsulate TM AU 1220 Acoustic Insulation is specifically designed for a wide variety of automotive applications: headliners, wheelwells, door panels, door pillars, instrument panels, trunks and many more. It is compressible, nonlinting, lightweight, formable and can be easily die-cut. It uses a polyolefin scrim on one side for fiber protection and consists of 69% polyolefin, 31% polyester. Weight 142 g/m 2 Density 10.1 kg/m 3 Thickness 14mm For more information on Thinsulate AU Acoustic Insulation please call 1-800-221-8211
TH-AU1220 70-0708-4710-1
A New Kind of Quiet AU 2020-1 Acoustic Insulation Acoustical Properties ASTM E-1050 Data Curves Absorption Coefficient Normal Incidence 1.00 0.90 0.80 0.70 0.60 0.50 0.40 0.30 0.20 0.10 AU 2020-1 16mm 0.00 160 250 400 630 1k 200 315 500 800 1.6k 1.25k 2k 2.5k 4k 3.15k One-Third-Octave Band Center Frequency (Hz) 5k 6.3k Product Description Thinsulate TM AU 2020-1 Acoustic Insulation is specifically designed for a wide variety of automotive applications: headliners, wheelwells, door panels, door pillars, instrument panels, trunks and many more. It is compressible, nonlinting, lightweight, formable and can be easily die-cut. It uses a polyolefin scrim on one side for fiber protection and consists of 68% polyolefin, 32% polyester. Weight 217 g/m 2 Density 13.6 kg/m 3 Thickness 16mm For more information on Thinsulate AU Acoustic Insulation please call 1-800-221-8211
TH-AU2020-1 70-0708-4711-9
A New Kind of Quiet AU 3002-2 Acoustic Insulation Acoustical Properties ASTM E-1050 Data Curves Absorption Coefficient Normal Incidence 1.00 0.90 0.80 0.70 0.60 0.50 0.40 0.30 0.20 0.10 AU 3002-2 19mm 0.00 160 250 400 630 1k 200 315 500 800 1.6k 1.25k 2k 2.5k 4k 3.15k One-Third-Octave Band Center Frequency (Hz) 5k 6.3k Product Description Thinsulate TM AU 3002-2 Acoustic Insulation is specifically designed for a wide variety of automotive applications: headliners, wheelwells, door panels, door pillars, instrument panels, trunks and many more. It is compressible, nonlinting, lightweight, formable and can be easily die-cut. It uses a polyolefin scrim on one side for fiber protection and consists of 70% polyolefin, 30% polyester. Weight 345 g/m 2 Density 18.2 kg/m 3 Thickness 19mm For more information on Thinsulate AU Acoustic Insulation please call 1-800-221-8211
TH-AU3002-2 70-0708-4712-7
TAI-2047 1. Sound Absorption Coefficient (ASTM E 1050) 1.0 0.9 Sound Absorption Coefficient Normal Incident 0.8 0.7 0.6 0.5 0.4 0.3 0.2 0.1 0.0 100 1000 10000 Frequency[Hz] 2. Test Method Thickness 1.0cm Measurement under 0.002 psi (=1.37 10-3 N/cm 2 ) Weight 200 g/m 2 Water content 0.4 % JIS L 3203 Thermal Coductivity 0.0342 W/mK ASTM C 518 or JIS A 1412 (Average Temp.: 22.5 ) Heat Resistance Tensile Strength Sound absorption was kept after 2000hr aging at 120 MD: 9.3 N(0.95kgf) CD: 10.0 N(1.02kgf) ASTM E 1050 Sample Width: 50mm, Sample length: 200mm Tensile Speed: 200mm/min. Flammability FMVSS No.302 Pass FMVSS No.302 Material Composition Polypropylene: 65 % Polyester : 35 % These data is not standard value,but actual value of sample product.
TAI-3047 1.Sound Absorption Coefficient (ASTM E 1050) 1.0 0.9 Sound Absorption Coefficient Normal Incident 0.8 0.7 0.6 0.5 0.4 0.3 0.2 0.1 0.0 2. 100 1000 10000 Frequency[Hz] Test Method Thickness 1.8cm Measurement under 0.002 psi (=1.37 10-3 N/cm 2 ) Weight 300 g/m 2 Water content 0.4 % JIS L 3203 Thermal Coductivity 0.0361 W/mK ASTM C 518 or JIS A 1412 (Average Temp.: 22.5 ) Heat Resistance Tensile Strength Sound absorption was kept after 2000hr aging at 120 MD: 10.5 N(1.07kgf) CD: 12.9 N(1.32kgf) ASTM E 1050 Sample Width: 50mm, Sample length: 200mm Tensile Speed: 200mm/min. Flammability FMVSS No.302 Pass FMVSS No.302 Material Composition Polypropylene: 65 % Polyester : 35 % These data is not standard value,but actual value of sample product.
TAI-4047 1. Sound Absorption Coefficient (ASTM E 1050) 1.0 0.9 Sound Absorption Coefficient Normal Incident 0.8 0.7 0.6 0.5 0.4 0.3 0.2 0.1 0.0 100 1000 10000 Frequency[Hz] 2. Test Method Thickness 2.3cm Measurement under 0.002 psi (=1.37 10-3 N/cm 2 ) Weight 400 g/m 2 Water content 0.4 % JIS L 3203 Thermal Coductivity 0.0372 W/mK ASTM C 518 or JIS A 1412 (Average Temp.: 22.5 ) Heat Resistance Tensile Strength Sound absorption was kept after 2000hr aging at 120 MD: 10.6 N(1.08kgf) CD: 17.9 N(1.83kgf) ASTM E 1050 Sample Width: 50mm, Sample length: 200mm Tensile Speed: 200mm/min. Flammability FMVSS No.302 Pass FMVSS No.302 Material Composition Polypropylene: 65 % Polyester : 35 % These data is not standard value,but actual value of sample product.
TAI-1527 1.Sound Absorption Coefficient(ASTM E 1050) Sound Absorption Coefficient Normal Incident 1 0.9 0.8 0.7 0.6 0.5 0.4 0.3 0.2 0.1 0 100 1000 10000 2. Frequency[Hz] Test Method Thickness 1.0cm Measurement under 0.002 psi (=1.37 10-3 N/cm 2 ) Weight 150 g/m 2 Excludes white scrim (white scrim:15 g/m 2 ) Water content 0.4 % JIS L 3203 Thermal Conductivity 0.0367 W/mK ASTM C 518 or JIS A 1412 (Average Temp.: 22.5 ) Heat Resistance Sound absorption was kept after 500hr aging at 120 ASTM E 1050 Tensile Strength MD: 22.3 N( 2.28 kgf) CD: 14.4 N( 1.47 kgf) Sample Width: 50mm, Sample length: 200mm Tensile Speed: 200mm/min. Flammability FMVSS No.302 FMVSS No.302 Material Composition Polypropylene: 65 % Polyester : 35 % Excludes white scrim (white scrim :Polypropylene 100 %) These data is not standard value,but actual value of sample product.
TAI-2027 1.Sound Absorption Coefficient(ASTM E 1050) 1.0 0.9 Soud Absorption Coefficient Normal Incident 0.8 0.7 0.6 0.5 0.4 0.3 0.2 0.1 0.0 100 1000 10000 Frequency[Hz] 2. Test Method Thickness 13mm Measurement under 0.002 psi (305mmx305mm) (=1.37 10-3 N/cm 2 ) Weight 215 g/m 2 Includes white scrim (white scrim:15 g/m 2 ) Water content 0.4 % JIS L 3203 Thermal Conductivity Heat Resistance Tensile Strength 0.0376 W/mK ASTM C 518 or JIS A 1412 (Average Temp.: 22.5 ) Sound absorption was kept after 500hr aging at 120 MD: 22.9 N( 2.34 kgf) CD: 12.0 N( 1.22 kgf) ASTM E 1050 Sample Width: 50mm, Sample length: 200mm Tensile Speed: 200mm/min. Flammability FMVSS No.302 FMVSS No.302 Material Composition Polypropylene: 65 % Polyester : 35 % Excludes white scrim (white scrim :Polypropylene 100 %) These data is not standard value,but actual value of sample product.
TAI-4027 1.Sound Absorption Coefficient(ASTM E 1050) 1.0 0.9 Sound Absorption Coefficient Normal Incident 0.8 0.7 0.6 0.5 0.4 0.3 0.2 0.1 0.0 100 1000 10000 Frequency[Hz] 2. Test Method Thickness 2.6cm Measurement under 0.002 psi (=1.37 10-3 N/cm 2 ) Weight 400 g/m 2 Excludes white scrim (white scrim:15 g/m 2 ) Water content 0.4 % JIS L 3203 Thermal Conductivity 0.0386 W/mK ASTM C 518 or JIS A 1412 (Average Temp.: 22.5 ) Heat Resistance Sound absorption was kept after 500hr aging at 120 ASTM E 1050 Tensile Strength MD: 23.4 N( 2.39 kgf) CD: 17.4 N( 1.77 kgf) Sample Width: 50mm, Sample length: 200mm Tensile Speed: 200mm/min. Flammability FMVSS No.302 FMVSS No.302 Material Composition Polypropylene: 65 % Polyester : 35 % Excludes white scrim (white scrim :Polypropylene 100 %) These data is not standard value,but actual value of sample product.
TAI-1547 1.Sound Absorption Coefficient(ASTM E 1050) Sound Absorption Coefficie Normal Incident 0.9 0.8 0.7 0.6 0.5 0.4 0.3 0.2 0.1 0.0 2. 100 1000 10000 Frequency[Hz] Test Method Thickness 0.8cm Measurement under 0.002 psi (=1.37 10-3 N/cm 2 ) Weight 150 g/m 2 Water content 0.4 % JIS L 3203 Thermal Conductivity 0.0333 W/mK ASTM C 518 or JIS A 1412 (Average Temp.: 22.5 ) Heat Resistance Tensile Strength Sound absorption was kept after 2,000hr aging at 120 MD: 7.7 N( 0.79 kgf) CD: 8.2 N( 0.84 kgf) ASTM E 1050 Sample Width: 50mm, Sample length: 200mm Tensile Speed: 200mm/min. Flammability FMVSS No.302 FMVSS No.302 Material Composition Polypropylene: 65 % Polyester : 35 % Excludes white scrim (white scrim :Polypropylene 100 %) These data is not standard value,but actual value of sample product.