1) Product Description: SD-0150 GENERAL PURPOSE ABS (Acrylonitrile Butadiene Styrene) (TA) General Purpose ABS, SD 0150 grade, is a rigid thermoplastic with good processing characteristics. It is a high flow injection molding grade with considerable impact strength and medium heat deflection. 2) Applications: This grade is intended for a wide range of applications including auto parts, home appliances, electrical parts/fittings, telecommunication and electronic devices. 3) Typical Data Characteristic Unit value Test Method MFI Gr/10 min 1.7 (200/5kg) Kj / m2 25 180 1/8 inch Tensile Strength @ Kgf /cm2 440 5mm/min Elongation @ Break % 40 5mm/min Kgf /cm2 640 2.8mm/min Flexural Modulus Kgf /cm2 20500 2.8mm/min (unannealed) 99 Rockwell Hardness R-Scale 104 785 5kg Flammability Recognized HB UL 94 1.5mm Specimen 1
*Typical Values : not to be construed as specifications. Density of this grade is approximately 1.04 gr/cm3. Shrinkage of all ABS grades in mold is approximately 0.3 % ~ 0.6 % ( 955). All tests are carried out at 23 unless otherwise stated. The above data are typical laboratory average. They are intended to serve as guide only. 4) Processing Condition: SD-0150 ABS granules absorbs moisture from atmosphere, with a rate depending on temperature and humidity. It is recommended that the material be dried in a dehumidifying dryer at 80 C to 85 C for 2-4 hours, prior to use.avoid excessive melt temperatures and long residence time, as they may cause thermal degradation. Processing temperatures are recommended to be at 190 C - 230 C for cylinder, and 40 C - 80 C for mold. SD-0150 ABS can be processed under different conditions based on machinery available and articles molded. Licensor: SAMUNG Packing: 25 Kg plastic bag 1) Product Description: SH-0150 EXTRUSION GRADE ABS (Acrylonitrile Butadiene Styrene) (TA) SH - 0150 ABS extrusion grade has been formulated to provide excellent mechanical properties, extrusion stability, vacuum formability and chemical resistance. It is a high flow extrusion grade with high impact strength at ambient temperature and considerable impact strength at low temperatures. This grade has a wide processing window. 2) Applications: SH - 0150 extrusion grade is mainly used for parts which need significant impact resistance. Since thin sheets can be vacuum formed, it is an appropriate grade for general sheets. 3) Typical Data 2
Characteristic Unit value Test Method MFI Gr/10 min 1.1 (200/5kg) Kj / m2 28 180 1/8 inch Tensile Strength @ Kgf /cm2 450 5mm/min Elongation @ Break % 5mm/min Kgf /cm2 640 2.8mm/min Flexural Modulus Kgf /cm2 22500 2.8mm/min (unannealed) 101.0 Rockwell Hardness R-Scale 106 785 5kg Flammability Recognized HB UL 94 1.5mm Specimen *Typical Values : not to be construed as specifications Density of this grade is approximately 1.03 gr/cm3. Shrinkage of all ABS grades in mold is approximately 0.3 % ~ 0.6 % ( 955). All tests are carried out at 23 unless otherwise stated. The above data are typical laboratory average. They are intended to serve as guide only. 4) Processing Condition: Processing temperatures are recommended to be at 180 C - 200 C for cylinder, 190 C - 220 C for die and 80 C -110 C for roll. SH-0150 ABS can be processed under different conditions based on machinery available and articles molded 3
Avoid excessive melt temperatures and long residence time, as they may cause thermal degradation. Licensor: SAMUNG Packing: 25 Kg plastic bag 1) Product Description: SV-0157 EXTRUSION GRADE ABS (Acrylonitrile Butadiene Styrene) (TA) SV - 0157 ABS extrusion grade has been formulated to provide excellent mechanical properties, extrusion stability, vacuum formability and chemical resistance. It has low flow with high impact strength at ambient temperature and considerable impact strength at low temperatures. This grade has a wide processing window. 2) Applications: SV-0157 extrusion grade is mainly used for parts which need significant impact resistance. Since sheets can be vacuum formed, it is the appropriate grade for refrigerator sheets which are in direct contact with rigid insulating foam produced with cyclo-pentane as blowing agent. 3) Typical Data Characteristic Unit value Test Method MFI Gr/10 min 0. 5 (200/5kg) Kj / m2 31 180 1/8 inch Tensile Strength @ Kgf /cm2 460 5mm/min Elongation @ Break % 70 5mm/min Kgf /cm2 630 2.8mm/min 4
Flexural Modulus Kgf /cm2 21900 2.8mm/min (unannealed) 100.5 Rockwell Hardness R-Scale 104 785 5kg Flammability Recognized HB UL 94 1.5mm Specimen *Typical Values : not to be construed as specifications Density of this grade is approximately 1.03 gr/cm3. Shrinkage of all ABS grades in mold is approximately 0.3 % ~ 0.6 % ( 955). All tests are carried out at 23 unless otherwise stated. The above data are typical laboratory average. They are intended to serve as guide only. 4) Processing Condition: SV-0157 ABS granules absorb moisture from atmosphere, with a rate depending on temperature and humidity. It is recommended that the material be dried in a dehumidifying dryer at 80 C to 85 C for 2-4 hours, prior to use Avoid excessive melt temperatures and long residence time, as they may cause thermal degradation. Processing temperatures are recommended to be at 180 C - 200 C for cylinder, 190 C -220 C for die and 80 C -110 C for roll. SV-0157 ABS can be processed under differentconditions based on machinery available and articles molded. Licensor: SAMUNG Packing: 25 Kg plastic bag ABS- 10 5
GHAED BASSIR Characteristic Unit value Test Method kj/m2 (ft.ib/in) 28 (5.1) MFI g/10min 30 Rock well Hardness R-scal 102 HDT Tensile Strength 85 (185) 95 (203) 420 (5964) Tensile Elongation % 25 Flexural Modulus 600 (8520) 20000 (284000) -256 (180) - 1133 785 2039/2 648 75/4 306 B 178 178 6.4mm,notched 220/10KG 1.82 MPa(264 psi) Un annealed 23, 2.8mm/min Specific Gravity 1.04 792 23 Mold Shrinkage % 0.4~0.7 955 Note1) these are typical property values, not specification. 6
Note2) In case of colored products the values could slightly differ by color. Note3) Values are measured at 23 C and RH OF 50%On Injection molded specimens in natural color. ABS- 30 GHAED BASSIR Classification: Heat Resistant ABS>Semi Heat Resistant Characteristics: Semi Heat Resistant Application: Rice cookers, Microwave oven components,automobile parts,etc. Characteristic Unit value Test Method kj/m2 (ft.ib/in) 20 (3.7) MFI g/10min 10 Rock well Hardness R-scal 108 HDT Tensile Strength 93 (199) 103 (217) 460 (5700) Tensile Elongation % 20 650 (9230) -256 (180) - 1133 785 2039/2 648 75/4 306 B 178 6.4mm,notched 220/10KG 1.82 MPa(264 psi) Un annealed 23, 2.8mm/min 7
Flexural Modulus 21000 (298200) 178 Specific Gravity 1.04 792 23 Mold Shrinkage % 0.4~0.7 955 Note1) these are typical property values, not specification. Note2) In case of colored products the values could slightly differ by color. Note3) Values are measured at 23 C and RH OF 50%On Injection molded specimens in natural color. ABS-40 GHAED BASSIR Classification: General purpose > Impact Resistance. Characteristics: High Impact Resistance Application: Home appliances, Automobile parts such as radiator,protective Helmets, Shoe heels,etc. Characteristic Unit value Test Method kj/m2 (ft.ib/in) 30 (5.5) MFI g/10min 23-256 (180) - 6.4mm,notched 220/10KG 8
Rock well Hardness R-scal 98 HDT Tensile Strength 82 (180) 923 (198) 400 (5680) Tensile Elongation % 30 Flexural Modulus 550 (7810) 16000 (2227200) 1133 785 2039/2 648 75/4 306 B 178 178 1.82 MPa(264 psi) Un annealed 23, 2.8mm/min Specific Gravity 1.04 792 23 Mold Shrinkage % 0.4~0.7 955 Note1) ABS-40 is ideal for self coloring; Special Colors can be arranged on request. Note2) these are typical property values, not specification. Note3) In case of colored products the values could slightly differ by color. Note4) Values are measured at 23 C and RH OF 50%On Injection molded specimens in natural color. ABS-50 9
GHAED BASSIR Classification: General purpose > Impact Resistance. Characteristics: High Impact Resistance Application: Home appliances, Automobile parts such as radiator, Protective Helmets, Shoe heels,etc. Characteristic Unit value kj/m2 (ft.ib/in) 30 (5.5) MFI g/10min 23 Rock well Hardness R-scal 98 HDT Tensile Strength 82 (180) 923 (198) 400 (5680) Tensile Elongation % 30 Flexural Modulus 550 (7810) 16000 (2227200) Test Method - 256 (180) - 1133 785 2039/2 648 75/4 306 B 178 6.4mm,notched 220/10KG 1.82 MPa(264 psi) Un annealed 23, 2.8mm/min 10
Specific Gravity 1.04 Mold Shrinkage % 0.4~0.7 178 792 955 23 Note1) ABS-40 is ideal for self coloring; Special Colors can be arranged on request. Note2) these are typical property values, not specification. Note3) In case of colored products the values could slightly differ by color. Note4) Values are measured at 23 C and RH OF 50%On Injection molded specimens in natural color. ABS-70 GHAED BASSIR Classification: General ABS > Extrusion Molding Characteristics: General Extrusion Molding use Application: Profiles, Released Extruded products, Injected Parts,etc. Characteristic Unit value kj/m2 (ft.ib/in) 27 (5) MFI g/10min 12 Rock well Hardness R-scal 109 Test Method - 256 (180) - 1133 785 6.4mm,notched 220/10KG 11
HDT Tensile Strength 87 (189) 97 (207) 480 (6816) Tensile Elongation % 25 Flexural Modulus 670 (9514) 23000 (327000) Specific Gravity 1.04 Mold Shrinkage % 0.4~0.7 2039/2 648 75/4 306 B 178 178 792 955 1.82 MPa(264 psi) Un annealed 23, 2.8mm/min 23 Note1) ABS-70 is ideal for self coloring, Special Colors can be arranged on request. Note2) these are typical property values, not specification. Note3) In case of colored products the values could slightly differ by color. Note4) Values are measured at 23 C and RH OF 50%On Injection molded specimens in natural color. 12
ABS-70SR GHAED BASSIR Classification: General ABS > Extrusion Molding Characteristics: General Extrusion Molding use Application: Profiles, Released Extruded products, Injected Parts,etc. Characteristic Unit value kj/m2 (ft.ib/in) 28 (5.1) MFI g/10min 8.5 Rock well Hardness R-scal 111 HDT Tensile Strength 87 (189) 97 (207) 480 (6816) Tensile Elongation % 20 670 (9514) Test Method - 256 (180) - 1133 785 2039/2 648 75/4 306 B 178 6.4mm,notched 220/10KG 1.82 MPa(264 psi) Un annealed 23, 2.8mm/min Flexural Modulus 22000 13
(312000) 178 Specific Gravity 1.04 Mold Shrinkage % 0.4~0.7 792 955 23 Note1) ABS-70 is ideal for self coloring, Special Colors can be arranged on request. Note2) these are typical property values, not specification. Note3) In case of colored products the values could slightly differ by color. Note4) Values are measured at 23 C and RH OF 50%On Injection molded specimens in natural color. ABS-72 GHAED BASSIR Classification: General ABS > Refrigerator Sheet. Characteristics: Hi Impact Strength, HI Rigidity. Application: Refrigerator interior container, Door liners,etc. Characteristic Unit value kj/m2 (ft.ib/in) 29 (5.3) Test Method - 256 6.4mm,notched 14
MFI g/10min 8 Rock well Hardness R-scal 110 HDT Tensile Strength 86 (187) 96 (205) 470 (6674) Tensile Elongation % 22 Flexural Modulus 670 (9514) 22000 (312000) Specific Gravity 1.04 Mold Shrinkage % 0.4~0.7 (180) - 1133 785 2039/2 648 75/4 306 B 178 178 792 955 220/10KG 1.82 MPa(264 psi) Un annealed 23, 2.8mm/min 23 Note1) ABS-72 is ideal for self coloring, Special Colors can be arranged on request. Note2) these are typical property values, not specification. 15
Note3) In case of colored products the values could slightly differ by color. Note4) Values are measured at 23 C and RH OF 50%On Injection molded specimens in natural color. ABS-75 GHAED BASSIR Classification: General purpose > Medium Impact Strength and. Characteristics: High Flow Application: office Equipment, miscellaneous goods,etc. Characteristic Unit value Test Method MFI kj/m2 (ft.ib/in) g/10min 45 (8.3) D-256 38 (7.0) 1.5 4.5 8.0 D- 3.2mm,notched 23 6.4mm,notched 23 220 /5.0KG 220 /10.0KG 200 /21.6KG Rock well Hardness R-scal 103 D 785 HDT Tensile Strength 86 (185) 95 (203) 450 (6390) D 648 1.82 MPa(264 psi) Un annealed D D 23,50mm/min Tensile Elongation % 20 D 23,50mm/min 16
Flexural Modulus 630 (8946) 21000 (298200) D 79 D 79 23, 2.8mm/min 23,50mm/min Specific Gravity 1.04 792 23 Mold Shrinkage % 0.4~0.7 955 Note1) these are typical property values, not specification. Note2) in case of colored products the values could slightly by color. Note3) values are measured at 23 C and RH of 50% on injection molded specimens in natural color. ABS-H-2938 GHAED BASSIR Classification: General purpose > Medium Impact Strength and. Characteristics: High Flow Application: office Equipment, miscellaneous goods,etc. Characteristic Unit value Test Method Izod Impact Strength kj/m2 (ft.ib/in) 18 (3.3) MFI g/10min 5-256 (180) - 1133 6.4mm,notched 220/10KG Rock well Hardness R-scal 107 17
HDT Tensile Strength 98 (208) 108 (226) 460 (6532) Tensile Elongation % 18 Flexural Modulus 650 (9230) 22500 (319500) Specific Gravity 1.04 Mold Shrinkage % 0.4~0.7 785 2039/2 648 75/4 306 B 178 178 792 955 1.82 MPa(264 psi) Un annealed 23, 2.8mm/min 23 Note1) these are typical property values, not specification Note2) in case of colored products the values could slightly by color Note3) values are measured at 23 C and RH of 50% on injection molded specimens in natural color 18