Chapter 5. Second Edition ( 2001 McGraw-Hill) 5.6 Doped GaAs. Solution



Similar documents
Solid State Detectors = Semi-Conductor based Detectors

Solar Cell Parameters and Equivalent Circuit

SEMICONDUCTOR I: Doping, semiconductor statistics (REF: Sze, McKelvey, and Kittel)

Semiconductors, diodes, transistors

FUNDAMENTAL PROPERTIES OF SOLAR CELLS

The Physics of Energy sources Renewable sources of energy. Solar Energy

ENEE 313, Spr 09 Midterm II Solution

Fall 2004 Ali Shakouri

FYS Vår 2015 (Kondenserte fasers fysikk)

Characteristic curves of a solar cell

High Open Circuit Voltage of MQW Amorphous Silicon Photovoltaic Structures

Project 2B Building a Solar Cell (2): Solar Cell Performance

3. Diodes and Diode Circuits. 3. Diodes and Diode Circuits TLT-8016 Basic Analog Circuits 2005/2006 1

The Electrical Conductivity and Hall Effect of Silicon. Royal Radar Establishment, Malvern, Worcs.

Solid-State Physics: The Theory of Semiconductors (Ch ) SteveSekula, 30 March 2010 (created 29 March 2010)

Energy band diagrams. Single atom. Crystal. Excited electrons cannot move. Excited electrons can move (free electrons)

Lecture 2 - Semiconductor Physics (I) September 13, 2005

Energy Transport. Focus on heat transfer. Heat Transfer Mechanisms: Conduction Radiation Convection (mass movement of fluids)

Crystalline solids. A solid crystal consists of different atoms arranged in a periodic structure.

Sheet Resistance = R (L/W) = R N L

Quantitative Photoluminescence. Studies in. a-si:h/c-si Solar Cells

Optical Hyperdoping: Transforming Semiconductor Band Structure for Solar Energy Harvesting

MOS (metal-oxidesemiconductor) 李 2003/12/19

a) The volume of the copper cylinder is given by: 3.14 x (0.5 x 10-6 ) 2 x 1 x 10-6 m 3 = 0.78 x m 3 ;

Semiconductor doping. Si solar Cell

Numeric modeling of synchronous laser pulsing and voltage pulsing field evaporation

ELECTRICAL CONDUCTION

Silicon Sensors for CMS Tracker at High-Luminosity Environment - Challenges in particle detection -

Diodes and Transistors

1. Degenerate Pressure

Solar Photovoltaic (PV) Cells

Broadband THz Generation from Photoconductive Antenna

Free Electron Fermi Gas (Kittel Ch. 6)

ELEC 3908, Physical Electronics, Lecture 15. BJT Structure and Fabrication

Resistivity. V A = R = L ρ (1)

University of California at Santa Cruz Electrical Engineering Department EE-145L: Properties of Materials Laboratory

2 Absorbing Solar Energy

Conduction in Semiconductors

Silicon, the test mass substrate of tomorrow? Jerome Degallaix The Next Detectors for Gravitational Wave Astronomy Beijing

Applied Physics of solar energy conversion

Lecture 3: Optical Properties of Bulk and Nano. 5 nm

A Course Material on. Engineering Physics - II

Introduction to VLSI Fabrication Technologies. Emanuele Baravelli

Hierarchical Classification of the Photovoltaic Materials by Data Analysis Method

CONTENTS. Preface Energy bands of a crystal (intuitive approach)

THE CURRENT-VOLTAGE CHARACTERISTICS OF AN LED AND A MEASUREMENT OF PLANCK S CONSTANT Physics 258/259

NTC Thermistor theory TABLE OF CONTENTS

9 Electrical conductivity

Chapter 6. Current and Resistance

Types of Epitaxy. Homoepitaxy. Heteroepitaxy

DIFFUSION IN SOLIDS. Materials often heat treated to improve properties. Atomic diffusion occurs during heat treatment

ELG4126: Photovoltaic Materials. Based Partially on Renewable and Efficient Electric Power System, Gilbert M. Masters, Wiely

NORGES TEKNISK- NATURVITENSKAPELIGE UNIVERSITET INSTITUTT FOR FYSIKK. Eksamen i Emne TFY4220 Faste Stoffers Fysikk

Blackbody Radiation References INTRODUCTION

Conductivity of silicon can be changed several orders of magnitude by introducing impurity atoms in silicon crystal lattice.

where h = J s

CHAPTER 10 Fundamentals of the Metal Oxide Semiconductor Field Effect Transistor

UNIT I: INTRFERENCE & DIFFRACTION Div. B Div. D Div. F INTRFERENCE

Photovoltaic and Photoelectrochemical Solar Cells

Sample Exercise 12.1 Calculating Packing Efficiency

Lecture 3: Optical Properties of Bulk and Nano. 5 nm

SUPERCONDUCTIVITY. PH 318- Introduction to superconductors 1

Chapter 5: Diffusion. 5.1 Steady-State Diffusion

acta physica slovaca vol. 54 No. 5, October 2004 THE PHOTOREFRACTIVE EFFECT IN LiNbO 3 CRYSTALS WITH VARIOUS DOPANTS

CHAPTER 7 DISLOCATIONS AND STRENGTHENING MECHANISMS PROBLEM SOLUTIONS

LAB IV. SILICON DIODE CHARACTERISTICS

Gamma and X-Ray Detection

Characteristic and use

Peltier Application Note

The MOSFET Transistor

Interference. Physics 102 Workshop #3. General Instructions

Avalanche Photodiodes: A User's Guide

EE 332 Photovoltaic Cell Design Iowa State University Electrical and Computer Engineering Dept

Timothy M. Burke, Sean Sweetnam, Koen Vandewal, and Michael D. McGehee* FULL PAPER. 1. Introduction. 2. Background Information

Chapter Outline. Diffusion - how do atoms move through solids?

Application Notes FREQUENCY LINEAR TUNING VARACTORS FREQUENCY LINEAR TUNING VARACTORS THE DEFINITION OF S (RELATIVE SENSITIVITY)

Solar Cells in Concentrating Systems and Their High temperature Limitations

Mechanical Properties of Metals Mechanical Properties refers to the behavior of material when external forces are applied

Statistical Models for Hot Electron Degradation in Nano-Scaled MOSFET Devices

PTYS/ASTR 206 Section 2 Spring 2007 Homework #2 (Page 1/5) NAME: KEY

Understanding the p-n Junction by Dr. Alistair Sproul Senior Lecturer in Photovoltaics The Key Centre for Photovoltaic Engineering, UNSW

How To Understand Light And Color

Hard Condensed Matter WZI

Photons. ConcepTest ) red light 2) yellow light 3) green light 4) blue light 5) all have the same energy. Which has more energy, a photon of:

Tuesday 20 May 2014 Morning

Technology Developments Towars Silicon Photonics Integration

Semiconductor research leading to the point contact transistor

Concept 2. A. Description of light-matter interaction B. Quantitatities in spectroscopy

Umicore Germanium Optics Leading the way in infrared optics

Field-Effect (FET) transistors

Yrd. Doç. Dr. Aytaç Gören

Efficiency of a Light Emitting Diode

NEUTRON TRANSMUTATION DOPED (NTD) SILICON FOR HIGH POWER ELECTRONICS

Designing of Amorphous Silicon Solar Cells for Optimal Photovoltaic Performance

Electronic transport properties of nano-scale Si films: an ab initio study

Silicon Wafer Solar Cells

Predicted Performance Advantages of Carbon Nanotube Transistors with Doped Nanotubes as Source/Drain

Cambridge International Examinations Cambridge International Advanced Subsidiary and Advanced Level

Basic Concepts in Nuclear Physics

Radiation Transfer in Environmental Science

Transcription:

Chapter 5 5.6 Doped GaAs Consider the GaAs crystal at 300 K. a. Calculate the intrinsic conductivity and resistivity. Second Edition ( 2001 McGraw-Hill) b. In a sample containing only 10 15 cm -3 ionized donors, where is the Fermi level? What is the conductivity of the sample? c. In a sample containing 10 15 cm -3 ionized donors and 9 10 14 cm -3 ionized acceptors, what is the free hole concentration? Solution a Given temperature, T = 300 K, and intrinsic GaAs. From Table 5.1 (in the textbook), n i = 1.8 10 6 cm -3, µ e 8500 cm 2 V -1 s -1 and µ h 400 cm 2 V -1 s -1. Thus, σ = en i (µ e + µ h ) σ = (1.602 10-19 C)(1.8 10 6 cm -3 )(8500 cm 2 V -1 s -1 + 400 cm 2 V -1 s -1 ) σ = 2.57 10-9 Ω -1 cm -1 ρ = 1/σ = 3.89 10 8 Ω cm b Donors are now introduced. At room temperature, n = N d = 10 15 cm -3 >> n i >> p. σ n = en d µ e (1.602 10-19 C)(10 15 cm -3 )(8500 cm 2 V -1 s -1 ) = 1.36 Ω -1 cm -1 ρ n = 1/σ n = 0.735 Ω cm In the intrinsic sample, E F = E Fi, n i = N c exp[ (E c E Fi )/kt] (1) In the doped sample, n = N d, E F = E Fn, n = N d = N c exp[ (E c E Fn )/kt] (2) Eqn. (2) divided by Eqn. (1) gives, N d n i = exp E E Fn Fi kt E F = E Fn E Fi = kt ln(n d /n i ) (4) Substituting we find, E F = (8.617 10-5 ev/k)(300 K)ln[(10 15 cm -3 )/(1.8 10 6 cm -3 )] E F = 0.521 ev above E Fi (intrinsic Fermi level) (3) 5.1

c The sample is further doped with N a = 9 10 14 cm -3 = 0.9 10 15 cm -3 acceptors. Due to compensation, the net effect is still an n-type semiconductor but with an electron concentration given by, n = N d N a = 10 15 cm -3 0.9 10 15 cm -3 = 1 10 14 cm -3 (>> n i ) The sample is still n-type though there are less electrons than before due to the compensation effect. From the mass action law, the hole concentration is: p = n i 2 / n = (1.8 10 6 cm -3 ) 2 / (1 10 14 cm -3 ) = 0.0324 cm -3 On average there are virtually no holes in 1 cm 3 of sample. We can also calculate the new conductivity. We note that electron scattering now occurs from N a + N d number of ionized centers though we will assume that µ e 8500 cm 2 V -1 s -1. σ = enµ e (1.602 10-19 C)(10 14 cm -3 )(8500 cm 2 V -1 s -1 ) = 0.136 Ω -1 cm -1 5.7 Degenerate semiconductor Consider the general exponential expression for the concentration of electrons in the CB, n = N c exp (E E ) c F kt and the mass action law, np = n i 2. What happens when the doping level is such that n approaches N c and exceeds it? Can you still use the above expressions for n and p? Consider an n-type Si that has been heavily doped and the electron concentration in the CB is 10 20 cm -3. Where is the Fermi level? Can you use np = n i 2 to find the hole concentration? What is its resistivity? How does this compare with a typical metal? What use is such a semiconductor? Solution Consider n = N c exp[ (E c E F )/kt] (1) and np = n i 2 These expressions have been derived using the Boltzmann tail (E > E F + a few kt) to the Fermi Dirac (FD) function f(e) as in Section 5.1.4 (in the textbook). Therefore the expressions are NOT valid when the Fermi level is within a few kt of E c. In these cases, we need to consider the behavior of the FD function f(e) rather than its tail and the expressions for n and p are complicated. It is helpful to put the 10 20 cm -3 doping level into perspective by considering the number of atoms per unit volume (atomic concentration, n Si ) in the Si crystal: n at = (Density)N A = (2.33 103 kg m -3 )(6.022 10 23 mol 1 ) 3 1 M at (28.09 10 kg mol ) i.e. n at = 4.995 10 28 m -3 or 4.995 10 22 cm -3 Given that the electron concentration n = 10 20 cm -3 (not necessarily the donor concentration!), we see that (2) 5.2

n/n at = (10 20 cm -3 ) / (4.995 10 22 cm -3 ) = 0.00200 which means that if all donors could be ionized we would need 1 in 500 doping or 0.2% donor doping in the semiconductor (n is not exactly N d for degenerate semiconductors). We cannot use Equation (1) to find the position of E F. The Fermi level will be in the conduction band. The semiconductor is degenerate (see Figure 5Q7-1). Impurities forming a band g(e) CB E E Fn E c CB E c E v E v E Fp VB Figure 5Q7-1 (a) Degenerate n-type semiconductor. Large number of donors form a band that overlaps the CB. (b) Degenerate p-type semiconductor. (a) (b) 2000 1000 Holes Electrons 100 50 10 15 10 16 10 17 10 18 10 19 10 20 Dopant Concentration, cm -3 Figure 5Q7-2 The variation of the drift mobility with dopant concentration in Si for electrons and holes at 300 K. Take T = 300 K, and µ e 900 cm 2 V -1 s -1 from Figure 5Q7-2. The resistivity is ρ = 1/(enµ e ) = 1/[(1.602 10-19 C)(10 20 cm -3 )(900 cm 2 V -1 s -1 )] ρ = 6.94 10-5 Ω cm or 694 10-7 Ω m Compare this with a metal alloy such as nichrome which has ρ = 1000 nω m = 10 10-7 Ω m. The difference is only about a factor of 70. 5.3

This degenerate semiconductor behaves almost like a metal. Heavily doped degenerate semiconductors are used in various MOS (metal- oxide- semiconductor) devices where they serve as the gate electrode (substituting for a metal) or interconnect lines. 5.8 Photoconductivity and speed Consider two p-type Si samples both doped with 10 15 B atoms cm -3. Both have identical dimensions of length L (1 mm), width W (1 mm), and depth (thickness) D (0.1 mm). One sample, labeled A, has an electron lifetime of 1 µs whereas the other, labeled B, has an electron lifetime of 5 µs. a. At time t = 0, a laser light of wavelength 750 nm is switched on to illuminate the surface (L W) of both the samples. The incident laser light intensity on both samples is 10 mw cm -2. At time t = 50 µs, the laser is switched off. Sketch the time evolution of the minority carrier concentration for both samples on the same axes. b. What is the photocurrent (current due to illumination alone) if each sample is connected to a 1 V battery? Solution a G ph Laser on t = 0 Laser off t = 10 µs Time t t τ B B τ B G ph τ A A τ A G ph t = 0 τ A τb Time t = 0 Figure 5Q8-1 Schematic sketch of the excess carrier concentration in the samples A and B as a function of time from the laser switch-on to beyond laser switch-off. 5.4

b From the mobility vs. dopant graph (Figure 5Q8-2), µ h = 450 10-4 m 2 V -1 s -1 and µ e = 1300 10-4 m 2 V -1 s -1. Given are the wavelength of illumination λ = 750 10-9 m, light intensity I = 100 W/m 2, length L = 1 mm, width W = 1 mm, and depth (thickness) D = 0.1 mm. 2000 1000 Holes Electrons 100 50 10 15 10 16 10 17 10 18 10 19 10 20 Dopant Concentration, cm -3 Figure 5Q8-2 The variation of the drift mobility with dopant concentration in Si for electrons and holes at 300 K. The photoconductivity is given by (see Example 5.11 in the textbook): ( ) σ = eηiλτ µ + µ e h hcd where η = 1 is the quantum efficiency. Assume all light intensity is absorbed (correct assumption as the absorption coefficient at this wavelength is large). The photocurrent density and hence the photo current is given by: Substitute: J = I/A = E σ I = ( W D ) V L I = WVeηIλτ µ + µ e h Lhc eηiλτ ( µ e + µ h ) hcd ( ) The photocurrent will travel perpendicular to the W D direction, while the electric field E will be directed along L. Substituting the given values for sample A (electron lifetime τ A = 10-6 s, voltage V = 1 V): I A = ( 0.001 m)1 ( V)1.602 ( 10 19 C ()100 ( W/m 2 )750 ( 10 9 m)10 ( 6 s) 0.13 m2 I A = 1.06 10-5 A ( 0.001 m) ( 6.626 10 34 J s)3.0 10 8 m/s ( ) V s + 0.045 m2 V s The photocurrent in sample B can be calculated with the same equation, using the given value of τ B = 5 10-6 s. After calculation: I B = 5.29 10-5 A 5.5

5.6