Low Temperature Curing of Polyimide Precursors by Variable Frequency Microwave

Transcription

1 Low Temperature Curing of Polyimide Precursors by Variable Frequency Microwave Hiroshi Matsutani, Takashi Hattori, Masayuki he, Takumi Ueno, Robert L. Hubbard, and Zak Fathi Research & Development Center, Hitachi Chemical Co. Ltd., Higashi, Hitachi, Ibaraki , Japan Yamazaki Research & Development Center, Hitachi Chemical DuPont MicroSystems, Ltd., Higashi, Hitachi, Ibaraki , Japan Technology Development, Lambda Technologies, Inc., 3813 N. Barron, Mesa, Arizona , USA Polyimides are commonly used as a thermally stable insulator for semiconductors. To assure adequate chemical or physical properties, a layer of their precursors has to be cured in a convection oven at more than C. In this paper, we compare variable frequency microwave (VFM) heating with convection heating for curing various polyimide precursors and a photosensitive polyimide precursor. Then, we demonstrate that the use of VFM enables us to cure the precursor lower than the standard convection cure temperature while maintaining necessary film properties such as cyclization, T g, T d, and elongation. Keywords: polyimide, curing process, microwave, buffer coating 1. Introduction Polyimides are widely used in silicon technology process integration such as insulating, buffer coating, and interlayer dielectrics, because of their excellent electrical, thermal, and mechanical properties [1]. For these purposes, soluble polyimide precursors, namely poly(amic acid)s, are applied initially, and then they are converted to insoluble polyimides in the solid state (Scheme). This curing process requires more than C curing temperature. Recently, polyimides are applied to novel devices such as gate dielectric layers in organic field-effect transistors [2] or insulation layers in organic light emitting diodes [3]. However, fabrication of these devices requires much less than C curing temperature to obtain the satisfactory results. There are several approaches to reduce the curing temperature including the introduction of flexible structures or the addition of imidization promoters [4]. Microwave irradiation is currently a wellknown method for heating materials and is utilized not only in many households but also in industry. It is employed to organic synthesis [5] and polymer science [6], since it offers a number of advantages over conventional, i.e. convection or diffusion, heating such as non-contact heating, instantaneous, Scheme H NH NH H n microwave or convection Δ - H 2 solid state (film) N N n

2 rapid heating, and so on. Furthermore, the use of variable frequency microwave (VFM, vide infra) in the curing of polymers has been reported for polyimides [7] and others [8] for rapid heating. Herein, we cured various polyimide precursors and a photosensitive polyimide precursor with a VFM oven and a convection oven. We then compare the resulting film properties, such as cyclization, T g, T d, and elongation, from the standpoint of low temperature cure [9]. 2. Method 2.1. Materials Non-photosensitive polyimide precursors, namely poly(amic acid)s, PIX-813, PIX-34, and PI-2611 were commercially available as solutions and obtained from HD Microsystems. Non-photosensitive polyimide precursors, SPL-6 and SPL-178 were also obtained from HD Microsystems. A photosensitive polyimide precursor HD-88 was available from HD Microsystems as a commercial product. 2.2 Percentage of rigid chain length (PRCL) Percentage of rigid chain length (PRCL) is one of parameters which express rigidity of a polymer chain [1]. The PRCL is applied herein to polyimides according to the previous literature for poly(ether sulfone), and is estimated by the following equation (1). PRCL = L rigid /L total (1) where, L rigid is the length of a rigid part in a monomer unit, and L total is the length of the whole of the unit. Generally, polymers having aromatic rings are high PRCL, and those having aliphatic or other flexible chains (eg. ether linkage) are low PRCL. In this study, the imide part as a common structural unit is omitted for calculating PRCL for simplification. The PRCL of fully aromatic polyimides are defined as %, and that of fully aliphatic polyimides are defined as % Variable frequency microwave (VFM) oven Curing involving cyclization of a polyimide precursor was done with a MicroCure 2, a Lambda Technologies Inc. product. Some of important features of this system include frequency sweeping from 5.85 to 7. GHz, and delivering power into a cavity. In as short as milliseconds, over 4, frequencies are launched to ensure uniform energy distribution, and also to eliminate arcing to allow components and devices with metals or circuits to be processed. IR and Ga-As probes monitor the temperatures on a film and under a substrate, respectively. A feed back control is also introduced to the system to control the temperature of the sample to be cured. The control system adjusts the power level automatically to maintain the sample at the desired temperature Processing A solution of a polyimide precursor was spin-coated on a silicon wafer, which was then soft-baked on a hot plate at around C for about 3 min to give a thin film whose thickness was adjusted to ca 15 μm. The resulting film was then cured by VFM irradiation in air. Irradiation power varied between W to 5 W. And the cure was executed at 125 C or 225 C for 1 h or 4 h. n comparison to VFM cure, the soft-baked film was also cured in convection oven at 125 C or 35 C for 1 h under a nitrogen atmosphere by an INH-9CD-S, a Koyo Thermo Systems product. Then, the cured film was peeled off from the wafer with the aid of diluted hydrofluoric acid Evaluation of cured films Degree of imidization was monitored by IR spectroscopy (Shimazu FTIR-8). Glass transition temperature (T g ) was obtained by Thermo-mechanical analysis (TMA) using TM/SS6 (Seiko Instruments Inc.). A T g (TMA-based) is defined as an inflection point in a temperature-displacement curve. Thermogravimetric analysis (TGA) was conducted by using TG/DTA6 (Seiko Instruments Inc.) to determine thermal degradation temperature (T d ). Tensile property was measured by Autograph AGS-N (Shimazu) with 2 mm chuck distance. 3. Results and Discussion 3.1. Non-photosensitive polyimide precursors T g of convection cured films As mentioned above, we choose polyimide precursors which are derived from various monomers (diamines and tetracarboxylic acid dianhydrides). Herein, we introduce PRCL (vide supra), since chemical structures of polyimides could be converted into numerical values. The calculated PRCLs of polyimides are listed in Table 1. This result indicates that rigidity of polymer chains increases in the following order: PIX- 813<SPL-6<PIX-34<SPL-178<PI-2611.

3 35 PIX-34 T g/ºc 25 SPL-6 SPL-178 PI-2611 : 35 C convection : 25 C convection : C VFM PIX PRCL/% Fig. 1. PRCL of polyimide precursors versus T g of cured films, : 35 C convection, : 25 C convection, : C VFM. Prior to VFM curing experiments, the polyimide precursor films on silicon wafers were cured with a convection oven at 25 C or 35 C for 1 h. Then we measured TMA-based T g of the resulting films, since T g is one of the important properties for thermally stable materials. Table 1. PRCL of polyimide precursors used in this study PI precursor PIX-813 SPL-6 PIX-34 SPL-178 PI-2611 PRCL/% The T g is plotted as a function of PRCL as shown in Figure 1. We find that the T g value for the 35 C cured films increases linearly with increasing PRCL ( in Figure 1). A similar relationship is observed in the preceding result on poly(ether sulfone) [1]. We also find that the T g s of the cured films of PIX-813 and SPL-6, whose PRCLs are relatively low, seem to be intact even if the cure temperature is reduced from 35 C to 25 C ( in Figure 1). In contrast, the T g s of 25 C cured films drop down to ca 27 C from their initial values for SPL-178 and PI-2611, whose PRCLs are high. To our surprise, however, the T g of PIX-34 cured at 25 C is found to remain high and close to the value for a 35 C convection cure. We summarize as follows. The T g s of polyimides are correlated with PRCL. For 35 C cured films, T g increases linearly with increasing PRCL. When the cure temperature is reduced, T g decreases for high PRCL polyimides T g of VFM cured films We cured polyimide precursor films with a VFM oven at C. The T g s of the resulting films are shown in the Figure 1 ( ) in conjunction with convection cure data. It is noteworthy that T g of films cured by VFM at C is found to be approximately identical to that of 25 C convection cured films for PIX-813, SPL-6, SPL-178, and PI-2611 ( vs ). This result suggests that cure temperature might be reduced with 5 C by using VFM irradiation regardless of PRCL value. In other words, low temperature cure might be accessible for polyimide precursors independently of their structures [11, 12]. To our surprise, for PIX-34, T g of the film cured at C by VFM (T g = 36 C) significantly exceeds that of the 35 C convection cured film (T g = 293 C) Film properties of PIX-34 with different curing method As mentioned in the previous section, PIX-34 exhibits a unique property for both VFM and convection. Thus, we measured several properties of the PIX-34 films cured at various temperatures compared with the different curing methods (convection and VFM). First, cyclization (degree of reaction or imidization) that is calculated from the IR spectrum is shown in Figure 2 ( for VFM cured films and for convection cured films). We find that the cyclization of the 15 C VFM cured film is equal to the case of C convection. This result implies the possibility of a 5 C lower

4 temperature cure. Moreover, the cyclization is improved significantly and almost completed at the low cure temperature region (more than 175 C). Cyclization/% Fig. 2. Cyclization of PIX-34 cured films,,. Next, as shown in Figure 3, we find that T g of cured films by VFM at 175 C and C is higher than that by convection at 35 C (299 C and 36 C, respectively vs 293 C). We emphasize again that VFM improves T g (TMA-based) absolutely at the low temperature region. Surprisingly, using convection heating, T g s of 15 C and 125 C cured films remain high (293 C and 288 C, respectively). Therefore, the abnormality of PRCL vs T g may be attributed to the specific property of PIX-34. Further investigation has to be done to explain this specificity. T g/ºc Fig. 3. T g of PIX-34 cured films,,. Next, we measured thermal degradation temperature (5% weight loss temperature T d5 ) using TGA. The result is shown in Figure 4. We find that the VFM cured films at more than 15 C exhibit excellent T d5 around 5 C. Note that T d5 of the C VFM cured film (53 C) is quite similar to that of the 25 C and 35 C convection cured film (526 C and 533 C, respectively). Therefore, the possibility of more than 5 C low temperature cure is supported by the T d5 data. T d5/ºc Fig. 4. Thermal degradation temperature (5%, T d5 ) of PIX-34 cured films,,. Elongation/% 15 5 Fig. 5. Average elongation at break of PIX-34 cured films,,. Finally, elongation at break of various cured films, which is the average value of more than five samples, is presented in Figure 5. We find that the value of C cured film is favorable by using VFM. Although the elongation of cured films by VFM at 175 C and C is inferior to that by convection at 25 C and 35 C, this value is quite superior to that obtained by convection at C.

5 We have noted that owing to VFM, more than 5 C lower temperature cure can be achieved while maintaining the necessary film properties, such as cyclization, T g, T d, and elongation, compared to the standard convection cure temperature for PIX-34. According to our result, PIX-34 can be processed with VFM at 175 C and C. In addition, T g of the VFM cured PIX-34 film elevates significantly which is not realized by convection. We have also disclosed that 5 C lower temperature cure can be accessible by considering the T g data for all other non-photosensitive polyimide precursors we have examined Photosensitive polyimide precursor A polyimide precursor, HD-88, is positivetone photosensitive, which can be developed by a common aqueous solution (2.38 wt% TMAH). The HD-88 consists of not only a polyimide precursor but also photoactive compounds. We expect that VFM is able to accelerate a dehydrative cyclization (imidization) at a low temperature region in the presence of photoactive compounds. Thus, we measured the properties of a HD-88 film cured by VFM or convection at various temperatures. photosensitive polyimide. Then, we measured T g, and the result is summarized in Figure 7. The T g s of both 175 C and C VFM cured films are comparable to the value of 25 C cured by convection. Moreover, at cure temperature of 225 C, T g is improved significantly by using VFM, and close to the value of the 35 C convection cured film. T g/ºc Fig. 7. T g of HD-88 cured films,,. 6 Cyclization/% Fig. 6. Cyclization of HD-88 cured films,,. First; degree of imidization is shown in Figure 6. The temperature-imidization curve of VFM cured film ( ) shifts to ca 5 C lower than that of cured film by convection ( ). We also find that more than 9% imidization is achieved by VFM cure at 225 C, which is comparable to convection cure at C. This result indicates the possibility of low temperature cure even for the T d5/ºc 5 4 Fig. 8. Thermal degradation temperature (5%, T d5 ) of HD-88 cured films,, Next, we evaluated T d5 of the films to observe similar results for cyclization and T g as expressed in Figure 8. The temperature-t d5 curve of VFM cured film shifts into a lower temperature region from that of cured film by convection. It is noteworthy to say that T d5 of the 225 C VFM cured film is much higher compared with convection at the same cure temperature, and is also inaccessible with convection at 35 C. These results suggest accessibility of reducing cure

6 temperature by 5 C and more. Finally, elongation at break of HD-88 cured films was measured and plotted in Figure 9. We observe that elongation of VFM cured film somewhat drops at 225 C from C. However, elongation of the film cured by VFM at C improves drastically compared with convection at the same curing temperature, and nearly equals that of a C convection cured film. Elongation/% Fig. 9. Average elongation at break of HD-88 cured films,,. We emphasize again that more than 5 C low temperature cure is accessible by VFM while maintaining several properties compared with a standard convectional heating condition ( C to 35 C) for HD-88. More specifically, HD- 88 can be processed with VFM at C to 225 C. This result suggests that VFM is a powerful and practical tool for low temperature cure of both non-photosensitive and photosensitive polyimide precursors. The reason why polyimide precursors processed with VFM result in reducing curing temperature is yet to be elucidated. However, the difference in evaporation rate of remained solvent between VFM and convection has been reported [8]. There is an argument about a non-uniform temperature profile on a molecular scale [8, 11]. Further study is underway in our group. 4. Conclusion Various polyimide precursor films have been cured by different heating methods which involve variable frequency microwave (VFM) heating and convection heating to study the possibility for reduction of cure temperature. We find that more than 5 C lower temperature processing can be realized by VFM compared with convection methods to produce sufficient properties. VFM is found to be valid for polyimides independently of their PRCL values (the rigidity of the polymers). The low temperature cure is accessible regardless of photosensitivity of polyimides. In addition, some of polyimide films cured by VFM show significant properties that are not achieved by conventional methods. References 1. See, for a example: A. Saiki, S. Harada, T. kubo, K. Mukai, and T. Kimura, J. Electrochem. Soc., 124 (1977) Y. Kato, S. Iba, R. Teramoto, T. Sekitani, T. Someya, H. Kawaguchi, and T. Sakurai, Appl. Phys. Lett., 84 (4) R. kada, K. Miyoshi, N. Arai, and M. Tomikawa, J. Photopolym. Sci. Technol., 17 (4) See, for examples: M. Kakuta, Shikizai, 69 (1996) 678. K.-i. Fukukawa, Y. Shibasaki, and M. Ueda, Chem. Lett., 33 (4) A selected review: M Larhed, C. Moberg, and A. Hallberg, Acc. Chem. Res., 35 (2) A selected review: D. Bogdal, P. Penczek, J. Pielichowski, A. Prociak, Adv. Polym. Sci., 163 (3). 7. K. D. Farnsworth, R. N. Manépalli, S. A. Bidstrup Allen, and P. A. Kohl, IEEE Trans. Components Packaging Technol., 24 (1) R. V. Tanikella, S. A. B. Allen, and P. A. Kohl, J. Appl. Polym. Sci., 83 (2) For the preliminary communication, see: R. L. Hubbard, Z. Fathi, I. Ahmad, H. Matsutani, T. Hattori, M. he, T. Ueno, and C. E. Schuckert, Annu. Int. Electron. Manuf. Technol. Symp. Proc, 29 (4) V. Carlier, J. Devaux, R. Legras, and P. T. McGrail, Macromolecules, 25 (1992) Reaction temperature enhancement in 5 C has been reported on the kinetic study of microwave (2.45 GHz) assisted imidization in solution: D. A. Lewis, J. D. Summers, T. C. Ward, J. E. McGrath, J. Polym. Sci., Part A: Polym. Chem., 3 (1992) The VFM curing of a specific polyimide at C in view of imidization has been disclosed: R. V. Tanikella, S. A. Bidstrup Allen, and P. A. Kohl, Proc. Int. Adv. Packaging Mater. Symp., 8 (2) 254.