An Overview of Candle Packaging Products and the Thermoforming Process

Transcription

1 An Overview of Candle Packaging Products and the Thermoforming Process

2 Contents Overview of Candle Packaging The Thermoforming Process and More Overview Vacuum Forming, Pressure Forming, Drape Forming Prototype Process Options Tooling Process Production Equipment Set-up What is Thermoforming? Inspection Considerations Process for Customization Options Packaging Material Options Comparative Applications for PET and PVC Candle Packaging Limitations of Packaging Materials Fragrance & Essential Oil Compatibility Summary

3 Overview of Candle Packaging Candle packaging is manufactured using the thermoforming process with PVC, PET and other thermoplastic materials as required. This presentation will explain the different types of thermoforming processes, tooling, machine set-up, inspection considerations, customization options, uses and limitations of PET and PVC materials for candle applications fragrance compatibility.

4 Typical Thermoformed Products for the Candle Industry A Wide Variety of Single and Multi-Cavity Packaging Products can be manufactured using the Thermoforming Process Some Examples are: 6 Cavity Melt Clamshell P.O.P. Display Tray

5 Vacuum Forming In Vacuum Thermoforming, vacuum is used to pull the hot film/sheet of plastic against the mold Used to obtain a more defined part/component by way of applying vacuum to the film/sheet Some formers utilize both vacuum and pressure to increase definition of part/component providing for the best possible outcome Due to the mold complexity, tooling is slightly more costly than the Drape Formed version.

6 Pressure Forming In Pressure Thermoforming, pressure is used to push the hot plastic film or sheet against the mold Used to obtain a more defined part/component by way of applying pressure to the film/sheet Also aides in the cooling process Some formers utilize both pressure and vacuum to increase definition of part/component providing for the best possible outcome Due to the mold complexity, tooling is slightly more costly than the Drape Formed version.

7 Drape Forming In Drape Forming, no vacuum is used Used for parts with a more gradual bends and little to no definition Tooling costs are less than Vacuum and/or Pressure Formed versions Typically not used for production quantities Drape Forming

8 Prototype Process for Composite Tooling Engineering creates 2D drawing to determine layout (tool size, machine utilization, type of material, blank material size, cycle times for equipment, secondary operations and more) Engineering creates geometry for Pattern Shop to produce composite tool Programming takes above geometry & creates geometry for prototype cutting die(s) Pattern Shop manufactures composite (typically R-Shape or Repro) prototype tool Tool Shop mounts composite tool onto a base plate & box for prototyping process Die Shop cuts, bends, lines & mounts steel-rule die for prototype die-cutting process

9 Prototype Process for 3D Printed Tooling Engineering creates 2D drawing to determine layout (tool size, machine utilization, type of material, blank material size, cycle times for equipment, secondary operations and more) Engineering creates geometry for 3D Printer & uploads STL file to produce composite tool Material is then loaded into the 3D Printer & print program is run Programming takes above geometry & creates geometry for prototype cutting die(s) Tool Shop mounts 3D Printed tool onto a base plate & box for prototyping process Die Shop cuts, bends, lines & mounts steel-rule die for prototype die-cutting process

10 Production Tooling Process Engineering creates 2D drawing to determine layout (tool size, machine utilization, type of material, blank material size, cycle times for equipment, secondary operations and more) Engineering creates geometry CNC Machining Center cutter paths Programming takes above geometry & creates CNC Machining Center programs & geometry for cutting die(s) Machining Center manufactures 1 st Tool Profile for customer approval After customer approval, Machining Center manufactures remaining Die Shop cuts, bends, lines & mounts steel-rule die for die-cutting process

11 Production Equipment Set-Up 1. Install forming station used to form part 2. Set-up & mount pressure box (if applicable) used to provide for more definition of part/component 3. Set-up & mount plug assist (if applicable) used to assist heated material further down into the cavities 4. Install Trim Station (if applicable) used to die-cut parts/components 5. Install & Align Stacker Station (if applicable) used to separate & stack parts/components 6. Trouble shoot set-up & make adjustments as needed to all of the above 7. Submit full shot (cut & uncut) to Quality Control (if applicable) for inspection

12 Thermoforming Process What is Thermoforming? It is the forming of plastic with heat.

13 Basic Thermoforming Steps Step 1: Material enters oven Heating the plastic film or sheet to a softening temperature Step 2: Material comes out of the oven and proceeds to the Forming Station Parts/components are formed over the mold Step 3: Parts then proceed from the forming station to the Die Station (if applicable) Parts/components are die-cut by way of a floating steel-rule die(s) Step 4: Parts/components then proceed to the Stacker Station where they are separated and stacked (if applicable) Step 5: Final Inspection of parts/components (if applicable)

14 Process Inspection All products should be subject to manual in-process inspections Inspection process should be performed at the beginning of production once per hour, at a minimum at least one carton per skid before shipment Typical inspection steps includes visual for proper forming and color consistency dimensional inspection clamshell functionality do they stay closed when snapped together? visual/manual for hanger holes proper cut and ease of removal liquid leak check using hot (150F) water

15 Causes for Inspection Failure Webbing (wrinkling in the part) Lack of vacuum holes Sheet material inconsistent Poor product detail Insufficient vacuum, vacuum leaks Sheet too cold Blisters or bubbles Moisture in the sheet

16 Causes for Inspection Failure Product that is cut out of tolerance or is not clean / Hanger holes that cannot be easily removed Dies require new cutting rule New die plate needed Product that is difficult to close or does not remain closed Cold forming (sheet too cold) Products that leak during the hot water check Defects in film blemish, pin holes, debris Something on mold or plug

17 Process Customization Options Customized Products can Include Candle Covers (round or square, male or female), Blisters, Clamshells, Tri-folds, Display Trays, Molds, Box Inserts, and more Wick holes (punched or punched and cleared) Custom cut-outs to the customers specifications Logos and/or patterns using hot stamped colored foil or printed labels Logos and/or patterns engraved into the tooling (size of area to be engraved will contribute to the legibility of the engraved logo and/or pattern) Materials in custom colors, grades and gauges As expected, customized products do come at a higher cost

18 Design Related Tooling Options Custom Designs can be incorporated into the final part by machining patterns into the tooling. When the plastic hardens, it takes the shape of the designs. Tooling and process cost must be considered when incorporating custom patterns Standard non-custom tooling will always be lower cost Custom shapes requiring definition typically require vacuum and/or pressure forming

19 Packaging Options Clear PVC Clear PET Max Use Temperature ( 0 F) Price Comparison Blue Tint - Lowest Higher (typically) Water Clear - Higher Typical Grades General Purpose APET(Virgin) RPET (Recycled or Utility) Typical Clarity Blue Tint & Water Clear APET Clear RPET Clear to Off Color Clear Recycle Codes 3 1 Waxes Availability Soy marginal Yes Paraffin Yes Yes Blended Wax Yes Yes Palm Wax Yes No PVC is the preferred material because of low cost, higher impact and cold crack resistance unless there are compatibility issues with the fragrance and essential oil additives

20 Limitations of Packaging Materials Packaging Materials Should be Stored under Controlled Temperature and Environmental Conditions Exposure to freezing temperatures or temperatures above 90F can reduce the shelf life of the material. Exposure to sunlight and humidity swings can also reduce shelf life A typical acceptable shelf life is six months. Long term storage at room temperature in airtight sealed and dark containers may help extend the shelf life. Any exposure to temperature, sunlight and humidity can Cause discoloration Reduce flexibility (cause brittleness) Reduce chemical resistance Reduce thermal performance

21 Fragrance and Essential Oil Compatibility (reference Hansen solubility parameters) Fragrances and Essential Oils are additives in many candle waxes These additives can be absorbed into the packaging and act as plasticizers A plasticizer will soften the plastic and reduce its use for the application Reference: The American Institute for Conservation site that discusses solubility parameters with a section on Hansen. In order to determine the correct packaging material up front, the wax formulation and solubility parameters of the packaging must be known. If unknown, testing is highly recommended. For example Essential oils are caustic to PET at 10% loading, but ok at 3% or less

22 SUMMARY The thermoforming process is a low cost method to manufacture quality candle packaging products using clear PVC and PET polymers Customized patterns, shapes and multiple cavities are just some of the options that can be incorporated into the thermoforming process Proper selection of the plastic will ensure compatibility with the wax and additives Materials, number of tool cavities, design options will all contribute to the final product cost

23 Questions? Thank You!

24 Contact Information: Jacquelinne Martinez x222