( II ) INDUSTRIAL & PROTECTIVE SYSTEM

( II ) INDUSTRIAL & PROTECTIVE SYSTEM (A) ALKYD BASE QUICK PAINT AUTO GLOSS PAINT GLOSS PAINT VARNISH TOP WOOD VARNISH ALUMINUM TOP RED OXIDE ZINC CHROMATE PRIMER RED OXIDE PRIMER AUTO GLOSS ZINC CHROMATE PRIMER RED LEAD PRIMER WASH PRIMER (2 PACK ETCH PRIMER) WASH PRIMER (1 PACK ETCH PRIMER) ROAD MARKING BLACK BOARD FLUORESCENT PAINT REMOVER

(B) AUTOMOTIVE PAINTS SYSTEM (B-1) NITROCELLULOSE PAINTS FLEX PUTTY FLEX PRIMER SURFACER FLEX PAINT TOP COAT (B-2) ACRYLIC NCR CRYL NCR PUTTY CRYL NCR PRIMER CRYL NCR PAINT ACRYLIC THINNER (B-3) NUMIX SYSTEM NUMIX CLEANER NUMIX PU PRIMER 2K NUMIX PRIMER 1K NUMIX ADHESION PROMOTER NUMIX HARDENER PRIMER NUMIX TOP COAT 2K NUMIX BASE COAT 1K NUMIX CLEAR COAT 2K NUMIX HARDENER NUMIX THINNER NUMIX RETARDANT THINNER NUMIX ANTI SILICON NUMIX SPOT REPAIR THINNER NUMIX PLASTICIZER NUMIX MA-4 MATTING PASTE (B-4) MISCELLANEOUS FAST CUT POLISH SOFT POLISH GRAVEL GUARD (GOMA)

(C) FURNITURE & WOOD FINISH PAINTS (C-1) NITROCELLULOSE PAINTS FLEX CLEAR COAT LACQUER TOP CLEAR COAT LACQUER FLEX SANDING SEALER TOP SANDING SEALER N.C WOOD STAIN N.C THINNER (C-2) ACRYLIC POLYURETHANE POLYURETHANE SANDING SEALER POLYURETHANE CLEAR COAT ACID CURING (D) STOVING SYSTEM ALKYD MELAMINE STOVING PAINT ACRYLIC STOVING PAINT SILICONE STOVING PAINT TIN PLATE LACQUER (E) EPOXY SYSTEM EPOXY INTERMEDIATE HB 2.19 EPOXY ZINC RICH PRIMER HB 10.03 GUARD EPOXY SF EPOXY ZINC PHOSPHATE PRIMER 10.06

(A) ALKYD BASE QUICK PAINT AUTO GLOSS PAINT GLOSS PAINT VARNISH TOP WOOD VARNISH ALUMINUM TOP RED OXIDE ZINC CHROMATE PRIMER RED OXIDE PRIMER AUTO GLOSS ZINC CHROMATE PRIMER RED LEAD PRIMER WASH PRIMER (2 PACK ETCH PRIMER) WASH PRIMER (1 PACK ETCH PRIMER) ROAD MARKING BLACK BOARD FLUORESCENT PAINT REMOVER

QUICK PAINT A quick drying gloss enamel, based on a special Alkyd, which gives an excellent, tough and flexible finish that has good adhesion and weather resistance. Metal work for interior and exterior applications, heavy duty equipment, vehicles, special military purposes and radiators, etc. As per shade card. Finish Glossy. Viscosity (25ºC) 8.5-9.5 Poise Specific Gravity 1.08 ± 0.1 (for White and Pastel shades). Solid by Weight % 62 ± 5% Coverage Rate (2 coat 10% 3-6 m 2 /Lit. (depending on the color used). dilution) Drying time Touch dry : 1 hr. Recoatable: 4 hrs. Flash point 30 C Application Methods Thining / Cleaning of Tools Film Thickness Spray. National Synthetic Thinner. (D.F.T.) 30 microns 1.2 mils. (W.F.T.) 60 microns 2.4 mils. Guiding Data for Airless Spray Nozzle Tip: 0.015" - 0.02" Nozzle Pressure: 2200 P.S.I. Surface should be cleaned thoroughly and should be dry and free from dust. HANDLING 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

AUTO GLOSS PAINT A special Alkyd base quick drying and glossy finish which is hard and weather resistant, its high gloss does not require any polishing. Suitable for Interior / Exterior and all wooden, masonry and metallic surfaces specially heavy duty equipment. As per shade card. Finish Glossy. Viscosity (25ºC) 7.5-8.5 Poise. Specific Gravity 1.07 ± 0.1 (for White and Pastel shades). Solid by Weight % 60 ± 5% Coverage Rate (2 coat 10% 4-8 m 2 /Lit. (depending on the color used). dilution) Drying time Touch dry : 1 hr. Hard dry : 3 hrs. Flash point 32ºC Application Methods Thining / Cleaning of Tools Mixing Ratio Film Thickness Spray National Special Thinner. 7.5% hardener maybe added to improve performance. (D.F.T.) 30 microns 1.2 mils. (W.F.T.) 60 microns 2.4 mils. Guiding Data for Airless Spray Nozzle Tip: 0.015" - 0.02". Nozzel Pressure: 2200 P.I.S. Surface should be cleaned and dry thoroughly and should be applied over National N.C. Putty or National N.C Primer. HANDLING 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

GLOSS PAINT An Alkyd base quick drying glossy finish which has high impact resistance and gloss. Special paint for trucks and heavy duty equipment. All major colours for trucks. Finish Glossy. Viscosity (25ºC) 7.5-8.5 Poise Specific Gravity 1.09 ± 0.1 Solid by Weight % 62 ± 5% Coverage Rate (2 coat 10% 3-6 m 2 /Lit. (depending on the color used). dilution) Drying time Touch dry : 2 hrs. Recoatable: 3-4 hrs. Flash point 32ºC Application Methods Thining / Cleaning of Tools Film Thickness Spray. National Synthetic Thinner. (D.F.T.) 30 microns 1.2 mils. (W.F.T.) 60 microns 2.4 mils. Guiding Data for Airless Spray Nozzle Tip: 0.015" - 0.02". Nozzle Pressure: 2200 P.S.I. Surface should be dry and free from dust and to be applied over National N.C. Putty or National N.C Primer. HANDLING 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

VARNISH A high quality synthetic Varnish for both exterior and interior use which gives a hard, tough, glossy finish resistant to water, oils, etc. Interior and Exterior, for soft wood, hard wood, doors, windows and furniture, also as a glaze coat for enamels. Transparent, Clear. Finish Glossy. Viscosity (25ºC) 8.5-9.5 Poise. Specific Gravity 0.90 ± 0.02 Solid by Weight % 58 ± 2% Coverage Rate (2 coat 10% 10-12 m²/lit. dilution) Drying time Touch dry : 6 hrs. Recoatable: 18 hrs. Flash point 38ºC Application Methods Brush, Roller or Spray. Thining / Cleaning of Tools White Spirits as needed 15-25%. Film Thickness (D.F.T.) 25 microns 1 mils. (W.F.T.) 50 microns 2 mils. Guiding Data for Airless Spray Nozzle Tip: 0.015 " - 0.020" Nozzle Pressure: 2200 P.S.I. Surface should be dry and clean. HANDLING 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

TOP WOOD VARNISH It is especially satin gloss and matt transparent alkyd urethane wood stain which can be applied over new wood substrates or old painted wooden surfaces. It has very good water repellency and can be used for interior and exterior wooden surfaces. Interior & exterior wood substrate. As per shade cards Finish Glossy & matt Specific Gravity 0.90 ± 0.94 Solid by Weight % 52 ± 2 Covering Rate 10-12 m²/lit. Drying Time Touch dry : 4 hrs. Recoatable : 24 hrs. Application Methods Thinning / Cleaning of Tools Brush, fine nylon roller Ready to use /White spirit Before application, the surface should be sound, clean and free from oil, grease, loose particles, dust and applied as follows: Primer National Varnish 1 coat Top Coat National Top Wood Varnish 2 coats CONDITIONS DURING APPLICATION The tempraure of the substrate should be minimum 10ºC above the dew point measured in the substrate vicinity. HANDLING product should be kept in cool and well ventilated place, protected from heat and direct sunlight at temp 5-35ºC. Containers must be kept tightly 24 months. - Avoid contact with skin and eyes. While painting it is advisable to wear eye protector. In case of contact with eyes, rinse immediately with plenty of water and seek medical advice. To remove splashes from skin; use soap and water or a recognized skin cleaner. obtained under controlled conditions. We reserve the right to change data without prior notice.

ALUMINUM A high luster reflective finish based on Aluminum pigment and special hard resins, which can withstand temperature upto 500Cº. Steel work, Electric poles, Iron towers, Pipes, Radiators, Exhaust Pipes etc Aluminum, Silver. Finish Glossy, Reflective. Viscosity (25ºC) 30 36 secs. Specific Gravity 0.99 ± 0.01 Solid by Weight % 52 ± 2% Theoretical Spreading Rate 18-20 m²/lit. Drying time Touch dry: 1-2 hrs. Hard dry : 18 hrs. Flash point 32ºC Application Methods Brush, Roller or Spray. Thining / Cleaning of Tools When required W.S. or Turpentine. Film Thickness (D.F.T.) 25 microns 1 mil. (W.F.T.) 60 microns 2.4 mils. Guiding Data for Airless Spray Nozzle Tip: 0.015 " - 0.020" Nozzle Pressure: 2200 P.S.I. Surface must be clean and free from dust. HANDLING 12 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

TOP RED OXIDE ZINC CHROMATE PRIMER An Alkyd / Zinc pigment base anticorrosive primer used as a general purpose, corrosion resistant, protective primer. Ferrous surfaces such as steel structure, metal works ect Brown. Finish Flat, Matt. Viscosity (25ºC) 9.5-10.5 Poise Specific Gravity 1.32 ± 0.02 Solid by Weight % 71 ± 2% Coverage Rate (2 coat 10% 14-16 m²/lit. dilution) Drying time Touch dry: 2-3 hrs. Recoatable: 12 hrs. Flash point 38ºC Application Methods Brush, Roller or Spray. Thining / Cleaning of Tools White Spirits as needed. Film Thickness (D.F.T.) 40 microns 1.6 mils. (W.F.T.) 80 microns 3.2 mils. Guiding Data for Airless Spray Nozzle Tip: 0.015 " - 0.020" Nozzle Pressure: 2200 P.S.I Remove all corrosions, mill scale, dirt, oil, grease, etc, by blast cleaning, flame cleaning, scraping, wire brushing or any other suitable technique. Ensure surface is absolutely dry at the time of painting or else rust will form underneath the paint film. HANDLING 18 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

RED OXIDE PRIMER An Alkyd base general purpose anticorrosive primer. Ferrous surfaces such as steel structures, metal works, etc Red, Brown. Finish Flat, Matt. Viscosity (25ºC) 11-12 Poise (25ºC). Specific Gravity 1.46 ± 0.02 Solid by Weight % 74.5 ± 2% Coverage Rate (2 coat 10% 11-12 m²/lit. dilution) Drying time Touch dry : 5 hrs. Recoatable: 18 hrs. Flash point 38ºC Application Methods Brush, Roller or Spray. Thining / Cleaning of Tools White Spirits. Film Thickness (D.F.T.) 55 microns 2.2 mils. (W.F.T.) 75 microns 3 mils. Guiding Data for Airless Spray Nozzle Tip: 0.015 " - 0.020" Nozzle Pressure: 2200 P.S.I. Remove all corrosions, mill scale, dirt, oil, grease, etc, by blast cleaning, flame cleaning, scraping, wire brushing or any other suitable technique. Ensure surface is absolutely dry at the time of painting or else rust will form underneath the paint film. HANDLING 18 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

AUTO GLOSS ZINC CHROMATE PRIMER A very good anticorrosive primer based on Alkyd resins and Zinc Chromate pigments. Used where extreme anticorrosion properties are required. Suitable for steel surfaces where finishing coats are white or pastel shades. Yellow, Yellowish Green. Finish Matt. Viscosity (25ºC) 7.5-8.5 Poise (25ºC). Specific gravity 1.27 ± 0.02 Solid by Weight % 65 ± 2% Theoretical Spreading Rate 15-17 m²/lit. Drying time Touch dry : 3 hrs. Recoatable: 12 hrs. Flash point 32ºC Application Methods Brush, Roller or Spray. Thining / Cleaning of Tools National Thinner or 121. Film Thickness (D.F.T.) 30 microns 1.2 mils. (W.F.T.) 60 microns 2.4 mils. Guiding Data for Airless Spray Nozzle Tip: 0.015 " - 0.020" Nozzle Pressure: 2200 P.S.I. Remove all corrosions, mill scale, dirt, oil, grease, etc, by blast cleaning, flame cleaning, scraping, wire brushing or any other suitable technique. Ensure surface is absolutely dry at the time of painting or else rust will form underneath the paint film. HANDLING 18 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

RED LEAD PRIMER An Alkyd base primer containing Red Lead pigments, which gives excellent rust preventing properties and is resistant to mild and moderate corrosive environments. On Ferrous surfaces like steel structures, etc Red, Orange. Finish Matt. Viscosity (25ºC) 20-22 Poise (25ºC). Specific Gravity 1.5 ± 0.02 Solid by Weight % 80 ± 2% Coverage Rate (2 coat 10% 12-15 m²/lit. dilution) Drying time Touch dry : 5 hrs. Recoatable: 24 hrs. Flash point 38ºC Application Methods Brush, Roller or Spray. Thining / Cleaning of Tools White Spirits. Film Thickness (D.F.T.) 45 microns 1.8 mils. (W.F.T.) 75 microns 3 mils. Guiding Data for Airless Spray Nozzle Tip: 0.015 " - 0.020" Nozzle Pressure: 2200 P.S.I. Remove all corrosions, mill scale, dirt, oil, grease, etc, by blast cleaning, flame cleaning, scraping, wire brushing or any other suitable technique. Ensure surface is absolutely dry at the time of painting or else rust will form underneath the paint film. HANDLING 18 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

WASH PRIMER {2 PACK ETCH PRIMER} A fast drying protective coating based on Polyvinyl Butyral resin/zinc Chromate pigment/phosphoric acid, which combines pretreatment and priming in one application, for non-ferrous metals to ensure good adhesion of subsequent coats. Aluminum cladding, Galvanized surfaces, Brass etc. Yellow, Green. Finish Flat Viscosity (25ºC) 18-22 Poise. Specific Gravity 1.05 ± 0.05 Solid by Weight % 39 ± 2% Coverage Rate (2 coat 10% dilution) 16.0 m²/lit. @ 8 microns (D.F.T.). Drying time Touch dry : 15 min. Recoatable: 1 hr. Flash point 13ºC Application Methods Brush, Roller or Spray. Mixing Ratio Add hardener and mix. Green Primer 1:1 hardener. Yellow primer 1:1 hardener. Thining / Cleaning of Tools National Thinner. Salt Spray & Humidity Resistance Excellent (500 hours). Film Thickness (D.F.T.) 16 microns 0.64 mils. (W.F.T.) 60 microns 2.4 mils. Guiding Data for AirlessSpray Nozzle Tip: 0.009 " - 0.011" Nozzle Pressure: 1500-2000 P.S.I. Degrease surface, wet abrading with abrasive paper. product should be kept in cool and well ventilated place, protected from heat and direct sunlight at temp 5-35ºC. Containers must be kept tightly HANDLING 18 months. - Avoid contact with skin and eyes. While painting it is advisable to wear eye protector. In case of contact with eyes, rinse immediately with plenty of water and seek medical advice. To remove splashes from skin; use soap and water or a recognized skin cleaner. obtained under controlled conditions. We reserve the right to change data without prior notice.

WASH PRIMER {1 PACK ETCH PRIMER} A fast drying protective coating based on Polyvinyl Butyral resin/zinc Chromate pigment/phosphoric acid, which combines pre-treatment and priming in one application, for non-ferrous metals to ensure good adhesion of subsequent coats. Aluminum cladding, Galvanized surfaces, Brass etc. Yellow, Green. Finish Flat Viscosity (25ºC) 18-22 Poise. Specific Gravity 1.05 ± 0.05 Solid by Weight % 39 ± 2% Coverage Rate (2 coat 10% 16.0 m²/lit. @ 8 microns (D.F.T.). dilution) Drying time Touch dry : 15 min. Recoatable: 1 hr. Flash point 13ºC Application Methods Thining / Cleaning of Tools Film Thickness Brush, Roller or Spray. National Thinner. (D.F.T.) 16 microns 0.64 mils. (W.F.T.) 60 microns 2.4 mils. Guiding Data for AirlessSpray Nozzle Tip: 0.009" - 0.011" Nozzle Pressure: 1500-2000 P.S.I. Degrease surface, wet abrading with abrasive paper. HANDLING 18 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

ROAD MARKING An Alkyd Resin and chlorinated rubber base road marking paint have fast drying, high abrasion resistance and good durability to severe weather conditions. For use on concrete or asphalt roads, curbstones, runways, etc. White, Yellow, Black. Finish Smooth & Matt. Viscosity (25ºC) 11.5-12.5 Poise. Specific Gravity 1.45 ± 0.05 Solid by Weight % 70 ± 5% Theoretical Spreading Rate 3-5 m 2 /Lit. Drying time Touch dry: 15-20 min. Hard dry : 2-4 hrs. Flash point 35ºC Application Methods Brush, Spray, Roller. Thining / Cleaning of Tools Ready for use, could be diluted by National Synthetic Thinner. Film Thickness (D.F.T.) 100 microns. Guiding Data for AirlessSpray Nozzle Tip: 0.015" - 0.20" Nozzle Pressure: 2200 P.S.I. Surface must be clean, dry and free from oil, grease, dirt etc. HANDLING 18 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

BLACK BOARD A Special Alkyd / Hard Resin base paint having good adhesion, high coverage, fast drying, good scratch resistance towards slippage of chalk during writing and easily cleanable. On wood and masonry, school boards as a finish coat. Black & Green. Finish Matt. Viscosity (25ºC) 7.5-8.5 Poise. Specific Gravity 1.32 ± 0.05 Solid by Weight % 65 ± 5% Theoretical Spreading Rate 10-12 m 2 /Lit. Drying time Touch dry: 4 hrs. Hard dry : 24 hrs. Ready to be used: after 3 days. Flash point 38ºC Application Methods Brush, Spray, Roller. Thining White Spirits as required. Guiding Data for AirlessSpray Nozzle Tip: 0.015" - 0.20" Nozzle Pressure: 2200 P.S.I. APPLICATION SYSTEM - One Coat of National Undercoat. - Two Coats of National Black Board. Surface must be clean and dry. HANDLING 18 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

FLUORESCENT An Acrylic base high visibility and good reflective finish. Excellent product for painting road signs. Red, Orange Yellow and Green. Viscosity (25ºC) 8-10 Poise. Specific Gravity 1.10 ± 0.05 Solid by Weight % 50 ± 2% Theoretical Spreading Rate 15 m 2 /Lit. Drying Time Touch dry: 30 min. Hard dry : 6-8 hrs. Application Methods Thinner Film Thickness Guiding Data for Airless Spray Surface must be clean and dry. HANDLING Spray, Roller, Brush. National Thinner. (D.F.T.) 35 microns. (W.F.T.) 70 microns. Tip Size: 0.432-0.482 mm. Line Pressure: 110-140 Bar. Fan Size: 60-80ºC 18 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

PAINT REMOVER A highly effective medium base mixture of solvents and additives suitably thickened to give fast, effective and safe paint removing property. Used for removing all types of dried paint films from type of surfaces. Can be used as brush cleaning agent. On Concrete, Plaster, Wood or Metal surfaces. Transparent. Viscosity (25ºC) 9-10 Poise. Specific Gravity 1.19 ± 0.05 Solid by Weight % 5 ± 1% Theoretical Spreading Rate Various depending on surface, type of paint, paint film thickness etc. APPLICATION METHOD - Lay thick coat of undiluted paint remover on the old paint film, leave for 20 minutes for reacting until wrinkles emerge on the surface. - Remove the soften film along with excess chemical with hard tool. - If the film is thick or hard it may be necessary to repeat the process. - After fully removing the loosened paint film and chemical with a hard tool, wash the surface with water. SPECIAL PRECAUETION Use hand gloves. Do not allow National Paint Remover to come in contact with skin, in case of any accidental skin contact wash the affected areas thoroughly with fresh water. HANDLING 12 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

(B) AUTOMOTIVE PAINTS SYSTEM (B-1) NITROCELLULOSE PAINTS FLEX PUTTY FLEX PRIMER SURFACER FLEX PAINT TOP COAT (B-2) ACRYLIC NCR CRYL NCR PUTTY CRYL NCR PRIMER CRYL NCR PAINT ACRYLIC THINNER (B-3) NUMIX SYSTEM NUMIX CLEANER NUMIX PU PRIMER 2K NUMIX PRIMER 1K NUMIX ADHESION PROMOTER NUMIX HARDENER PRIMER NUMIX TOP COAT 2K NUMIX BASE COAT 1K NUMIX CLEAR COAT 2K NUMIX HARDENER NUMIX THINNER NUMIX RETARDAND THINNER NUMIX ANTI SILICON NUMIX SPOT REPAIR THINNER NUMIX PLASTICIZER NUMIX MA-4 MATTING PASTE (B-4) MISCELLANEOUS FAST CUT POLISH SOFT POLISH GRAVEL GUARD (GOMA)

(B-1) NITROCELLULOSE PAINTS FLEX PUTTY FLEX PRIMER SURFACER FLEX PAINT TOP COAT

FLEX PUTTY It is a special glazing putty based on Nitrocellulose / Alkyd for use on wooden & steel surfaces. As a body filler for automobiles and for leveling wooden surfaces. Red, Red Brown, Grey, White, Black. Gloss (60º) Matt. Viscosity (20ºC) Thick Viscosity. Specific Gravity 1.28 ± 0.02 Solid by Weight% (110ºC) 55 ± 1 % Covering Capacity 3-4 m 2 /Lit. (D.F.T. 30 µ). Drying time Touch dry: 30 min. Sanding Time: After 2 hrs. Hard dry : 3 4 hrs. Application Methods Thining / Cleaning of Tools Film Thickness Guiding Data for Airless Spray Glazing Knife. National N.C Thinner. Single pack, ready to use. Recommended 20-30 microns per coat (or as necessary depends upon surface). To be applied over National N.C Primer and the primered surface should be dry, clean and free from any loose particles. HANDLING 18 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

FLEX PRIMER SURFACER It is a specially formulated Primer based on Nitrocellulose / Alkyd resins for use on wooden and steel surfaces. For use on furniture, automobiles, doors, office cabinets etc Grey, White, Black, Yellow. Gloss (60º) Matt. Viscosity (20ºC) 65-70 Poise. Specific Gravity 1.32 ± 0.02 Solid by Weight% (110ºC) 55 ± 1 % Covering Capacity 3-4 m 2 /Lit. (D.F.T 30 µ). Drying time Touch dry: 30 min. Sanding Time: After 2-3 hrs. Hard dry : 3-4 hrs. Method of application Spray. Thinning / Cleaning of Tools National N.C. Thinner. Mixing Ratio Single pack, dilution (1:1). Film Thickness D.F.T Recommended 15-30 microns per coat (or as necessary depends upon surface). Guiding Data for Airless Spray Nozzle Orifice: 0.017" - 0.021" Nozzle Pressure: 2000-2300 P.S.I. The surface should be dry, clean, and well rubbed down with sandpaper, free of any loose particles. HANDLING 18 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

FLEX PAINT TOP COAT It is a fast drying excellent finish based on Nitrocellulose/Alkyd resins, which has good color retention, durability and water resistance. As a finish for automobiles and furniture etc As per shade card. Gloss (60º) Matt or Gloss. Viscosity (20ºC) Thick Viscosity. Specific Gravity 1.1 ± 0.1 Solid by Weight% (110ºC) 45 ± 1 % Covering Capacity 3-9 m 2 /Lit. (DFT: 30 µ). Drying time Touch dry : 30 min. Hard dry : 8-12 hrs. Recoatable : 3-4 hrs. for polishing. Method of application Spray. Thinning / Cleaning of Tools National N.C Thinner. Mixing Ratio Single pack, dilution (1:1). Film Thickness D.F.T Recommended 15-30 microns per coat (or as necessary depends upon surface). Guiding Data for Airless Spray Nozzle Orifice: 0.017" - 0.021". Nozzle Pressure: 2000-2300 P.S.I. To be applied over National N.C Putty or National N.C Primer as the case maybe, and can be over coated with National Clear Lacquer. HANDLING 24 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

(B-2) ACRYLIC NCR CRYL NCR PUTTY CRYL NCR PRIMER CRYL NCR PAINT ACRYLIC THINNER

CRYL NCR PUTTY National Cryl NCR Putty is a two-component Putty, formulated with high percentage of filler to cover all pores and give a smooth adequate touch. For wood and steel surface. White Finish Matt Viscosity (20ºC) Thick Paste. Specific Gravity 1.65 ± 0.05 (of mix). Solid by Weight % 75± 2 % Theoretical Spreading Rate 5 m²/lit. @ 40 microns (D.F.T.) Drying time Touch dry: 1-2 hrs. Hard dry : Min : 3 hrs. (20ºC). Max: 6 hrs. (20ºC). Flash Point 25ºC when mixed. Thinning / Cleaning of Tools National Thinner 204. Mixing Ratio Base: 100 parts by volume. Curing Agent (hardener): 1.0 part by volume. Pot Life 6 8 hrs (20ºC). The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. DRYING TIME For optimum Drying/Curing, good ventilation is always a recommendation. In oven: full curing needs 30 min. @ 60ºC. 18 months @ (20ºC) wear eye protector. In case of contact with eyes, rinse immediately with plenty of water and seek medical advice. To remove splashes from skin; use soap and water or a recognized skin cleaner. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

CRYL NCR PRIMER National Cryl NCR Primer is a two-component primer with excellent sanding and high coverage. As a primer surfacer coat for protection of steel in severely corrosive environment where gloss and color retention is required. White, Grey. Finish Flat. Viscosity (20ºC) 15-30 Poise. Specific Gravity 1.37 ± 0.05 (of mix). Solid by Weight % 68 ± 2 % Theoretical Spreading Rate 9 m²/lit. @ 40 microns (D.F.T.). Drying time Touch dry : 1-2 hrs. Recoatable: Min: 3 hrs. (20ºC). Max : 6 hrs. (20ºC). Flash Point 25ºC when mixed. Impact 50 cm forward - 50 cm backward. Scratch Pass Flexibility 7.5-10 mm. Application Methods Airless Spray Air Spray Thinning (Max Vol.) 204 (25%) 204 (25%) Thinning / Cleaning of Tools National Thinner 204. Mixing Ratio Base: 4.0 parts by volume. Curing Agent (hardener): 1.0 part by volume. Pot Life 6-8 hrs (20ºC). Film Thickness (D.F.T.) 80 microns 3.2 mils. (W.F.T.) 40 microns 1.6 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016 " - 0.019" Nozzle Pressure: 2000 P.S.I. The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. DRYING TIME For optimum Drying / Curing, good ventilation is always a recommendation. In oven: full curing needs 30 min @ 60ºC. 1/2

CRYL NCR PRIMER 18 months @ (20ºC) obtai ned under controlled conditions. We reserve the right to change data without prior notice. 2/2

CRYL NCR PAINT National Cryl NCR Paint is a two pack (Polyurethane), glossy topcoat that has excellent color retention and specially very good resistance against U.V rays. As a finishing coat for protection of steel in severely corrosive environment where gloss and color retention is required. As per shade card. Finish Glossy (93-96 @ 60 ). Viscosity (20ºC) 90-180 seconds. Specific Gravity 1.12 ± 0.20 (of mix) (for white and Pastel Shades). Solid by Weight % 45% - 65% Theoretical Spreading Rate 9-10 m²/lit. @ 40 microns (D.F.T.). Drying time Touch dry : 1-2 hrs. Recoatable: Min: 10 hrs. (20ºC). Max: 48 hrs. (20ºC). Flash Point 26ºC when mixed. Impact 50 cm forward / 50 cm backward. Scratch Pass. Flexibility 7.5-10 mm. Application Methods Airless Spray Air Spray Thinning (Max Vol.) 204 (25%) 204 (25%) Thinning / Cleaning of Tools National Thinner 204. Mixing Ratio Base: 2.0 parts by volume. Curing Agent (hardener): 1.0 part by volume. Pot Life 6-8 hrs (20ºC). Film Thickness (D.F.T.) 75 microns 3.0 mils. (W.F.T.) 40 microns 1.6 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016 " - 0.019" Nozzle Pressure: 2000 P.S.I. The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. 1/2

CRYL NCR PAINT DRYING TIME For optimum Drying / Curing, good ventilation is always a recommendation. In oven: full curing needs 30 min. @ 60ºC. Without oven: see the table. STEEL TEMP DRY TO TOUCH IN RECOATING INTERVAL FULLY CURED HOURS MINIMUM MAXIMUM 20ºC 3 hrs 7 days 10 hrs 48 hrs 30ºC 2 hrs 6 days 8 hrs 48 hrs 40ºC 1 hr 5 days 6 hrs 48 hrs 24 months @ 20ºC. obtai ned under controlled conditions. We reserve the right to change data without prior notice. 2/2

ACRYLIC THINNER Special formulated thinner for acrylic polyurethane coatings application. It contains organic volatile solvents. For car refinish coating application at required existing temperature. Transparent Viscosity (20ºC) 15-20 sec. Specific Gravity 0.97-0.87 Evaporation Rate 5-15 min. Flash Point 25-54ºC Mixing Ratio by Volume 20-50% Fast Thinner 202 For spot and repairs - or for complete re-sprays provided the temperature in the spray booth does not exceed 20 C Slow Thinner 204 For treatment of large vehicles within the temperature range of 20-30 C Extra Slow 206 For treatment of large vehicles within the temperature range of 30-40 C The product must be stored according to National Regulations. The product should be kept in cool and well ventilated place, protected from heat and direct sunlight at temp 5-35ºC. Containers must be kept tightly - Avoid contact with skin and eyes. While painting it is advisable to wear eye protector. In case of contact with eyes, rinse immediately with plenty of water and seek medical advice. To remove splashes from skin; use soap and water or a recognized skin cleaner. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

(B-3) NUMIX SYSTEM NUMIX CLEANER NUMIX PU PRIMER 2K NUMIX PRIMER 1K NUMIX ADHESION PROMOTER NUMIX HARDENER PRIMER NUMIX TOP COAT 2K NUMIX BASE COAT 1K NUMIX CLEAR COAT 2K NUMIX HARDENER NUMIX THINNER NUMIX RETARDANT THINNER NUMIX ANTI SILICON NUMIX SPOT REPAIR THINNER NUMIX PLASTICIZER NUMIX MA-4 MATTING PASTE

NUMIX CLEANER Numix Cleaner is solvent specially selected to remove grease and other contaminants from bare metal, existing finishes, primer surfacer and plastic substrate. Bare metal, existing finishes, primer surfacer and plastic. Transparent Specific Gravity 0.80 Numix Cleaner is a very good general purpose cleaner, it is suitable for cleaning and degreasing bare metals, existing finishes primer surfacer, etc. Application Technique: Unsanded existing finishes: 1- Wash the vehicles with detergent and warm water to remove water soluble contaminants. 2- Wash down repaired area with Numix Cleaner to remove any other contaminants. 3- With clean towel dry off the cleaner before evaporation to ensure contaminants removal. Sanded existing finishes: Apply step 1 & 2 more than once a time after sanding and prior to topcoating. Untreated plastic substrates: Apply steps 1-3 in the same manner, when cleaning unpainted plastic parts allow drying out for 20-30 minutes after application of cleaner and prior to primer application. Bare metal, steel, zinc coated steel and aluminum substrates must be degreased as follows: 1. Wash down the metal with the cleaner. 2. With clean towel dry off the cleaner before evaporation taking into consideration to use one fresh towel for washing down and another one for wiping dry and replacing towels regularly. Precaution: Never allow for the cleaned vehicles to be touched with bare hands, moisture and oils which may cause adhesion or blistering problems. HANDLING 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

NUMIX PU PRIMER 2K Numix Polyurethane Primer is a two-component primer filler based on acrylic resin and polyisocyanate hardener, this product has quick drying, high filling and good sanding properties. It is a substrate for all type of car refinish. As a primer surfacer coat for protection of steel in severely corrosive environment and where gloss and color retention is required. Light Grey Finish Flat Viscosity (25ºC) 15 30 Poise Specific Gravity 1.48 ± 0.02 (of mix). Solid by Weight % 68 70 % Theoretical Spreading Rate 6-8 m²/lit. @ 50 microns (D.F.T.) Drying time Touch dry: 1-2 hrs. Recoatable: Min: 3 hrs. (20ºC). Max: 6 hrs. (20ºC). Flash Point 25 ºC when mixed Impact resistance (25 cm) 50 cm forward / 50 cm backward. Scratch resistance Pass Bending test ( 15 mm) 7.5 10 mm. Water resistance (24 hrs) spot Pass test Application Methods Airless Spray and Air Spray Thinning / Cleaning of Tools Numix Thinner. Mixing Ratio by Volume Base: 4 parts. Curing Agent (hardener): 1 part. Numix PU-Primer 2K Numix Hardener Primer Numix Thinner 100 25 20 Pot Life 2 4 hrs (20ºC). Film Thickness (D.F.T.) 40 microns 1.6 mils. (W.F.T.) 75 microns 3.0 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016 " - 0.019" Nozzle Pressure: 2000 P.S.I. The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. DRYING TIME For optimum Drying/Curing, good ventilation is always a recommendation. In oven: full curing needs 30 min. @ 60ºC. Without oven: see the table (Hardener Data Sheet). 1/2

NUMIX PU PRIMER 2K obtai ned under controlled conditions. We reserve the right to change data without prior notice. 2/2

NUMIX PRIMER 1K Numix Primer 1K is single component primer filler based on a combination of acrylic resin and nitrocellulose, this product is fast drying with high filling and good sanding properties. It is a suitable for all type of car refinish. As a primer surfacer coat for protection of steel in severely corrosive environment and where gloss and color retention is required. Grey, Greenish Yellow. Finish Flat Viscosity (25ºC) 20 25 Poise Specific Gravity 1.37 ± 0.02 (of mix) Solid by Weight % 60-65 % Theoretical Spreading Rate 6-8 m²/ltr. @ 50 microns (D.F.T.) Drying time Touch dry: 1-2 hrs. Recoatable: Min: 3 hrs. (20ºC). Max: 6 hrs. (20ºC). Flash Point 25 ºC when mixed Impact resistance (25 cm) 50 cm forward / 50 cm backward. Scratch resistance Pass Bending test ( 15 mm) 7.5 10 mm. Water resistance (24 hrs) spot Pass test Application Methods Airless Spray and Air Spray Thinning / Cleaning of Tools Numix Thinner. Mixing Ratio by Volume Numix Primer 1K 100 Numix Thinner 20 Film Thickness (D.F.T.) 40 microns 1.6 mils. (W.F.T.) 75 microns 3.0 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016 " - 0.019" Nozzle Pressure: 2000 P.S.I. The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. DRYING TIME For optimum Drying/Curing, good ventilation is always a recommendation. 1/2

NUMIX PRIMER 1K obtai ned under controlled conditions. We reserve the right to change data without prior notice. 2/2

NUMIX ADHESION PROMOTER It is special materials developed to conventional coating to adhere well to untreated polyethylene, polypropylene, or polypropylene / elastomer blends such as TPO s. Plastic Surfaces as a Primer. Yellowish Viscosity (20ºC) 1-2 Poise Specific Gravity 0.90 ± 0.02 Solid by Weight% (110ºC) 10 ± 0. 5 % Covering Capacity 4 6 m 2 /Ltr. Drying time Touch dry: 3 min. Method of application Thinning / Cleaning of Tools Air Spray Ready to use. Should be dry, clean and free from all loose particles. HANDLING 6 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

NUMIX HARDENER PRIMER Numix hardener Primer is a polyisocyanate hardener used for curing Numix PU Primer 2K to insure fast dry and high degree of hardness. As a hardener for Numix PU- Primer 2K. Transparent Specific Gravity 0.99 Solid by Weight % Approx. 24 Flash Point Approx 20 C. Mixing Ratio by Volume Numix PU-Primer 2K Numix Hardener Primer Numix Thinner 100 25 20 Pot Life 2 hrs Film Thickness 35 microns 1.4 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016 - " 0.019" Nozzle Pressure: 2000 P.S.I. HANDLING 12 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

NUMIX TOP COAT 2K Numix Top Coat 2K is two components system based on hydroxyl functional acrylic resin, includes 35 basic colors and used as a finishing coat in car refinish system. Used as a top coat to obtain glossy finish for cars. As per shade card. Gloss 96 98% Viscosity (20ºC) Approx. 8.75 Poise. Specific Gravity Variable and dependable on the color. Solid by Weight % Dependable on the color. Theoretical Spreading Rate 6-8 M 2 /Lit. Drying time 20 hrs @ 20 C 30 45 min. @ 60 C Flash Point Approx 22 C Surface should be well prepared to obtain excellent smooth surface. At the time of application it should be clean and dry. Application Methods Air Spray (H.V.L.P) Thinning Numix Thinner Mixing Ratio by Volume Numix Top Coat Numix Hardener Numix Thinner 100 50 30 Pot Life 2-4 hrs. Film Thickness 35 microns 1.4 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016 - " 0.019" Nozzle Pressure: 2000 P.S.I. HANDLING 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

NUMIX BASE COAT 1K Numix Base Coat 1K is a one component system based on acrylic resin and consists of 67 basic colors and used as a basic coat for the finishing layer National Clear Coat. As a base coat for car refinish system. Gloss Viscosity (20ºC) Specific Gravity Solid by Weight % Theoretical Spreading Rate Drying time Flash Point As per shade card. Matt. 7-8.75 Poise. Dependable on the color. Variable and dependable on the color. 6 8 m 2 /Lit. (depending on the color). 10-15 min. Approx. 22 C. Surface should be well prepared to obtain excellent smooth surface. At the time of application it should be clean and dry. Application Methods Air Spray (H.V.L.P) Thinning Numix Thinner. Mixing Ratio by Volume 100 : 100 Pot Life Unlimited. Film Thickness 35 microns 1.4 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016 - " 0.019" Nozzle Pressure: 2000 P.S.I. HANDLING 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

NUMIX CLEAR COAT 2K Numix Clear Coat is a two-component top coat with excellent gloss and color retention. Product noted for very good resistance against U.V. ray. As a finishing coat for car refinish for protection of structural steel in severely corrosive environment and where gloss and color retention is required. Clear Finish Glossy (96 98 @ 60 ). Viscosity (20ºC) 8-10 Poise. Specific Gravity 1.02 ± 0.05 (of mix). Solid by Weight % 50 ± 1 % Theoretical Spreading Rate 14.0 m²/ltr. @ 40 microns (D.F.T.). Drying time Touch dry : 30 40 min. @ 60ºC. Hard dry : 12 hrs. (20ºC). Recoatable: 18 hrs. (20ºC). Flash Point 25º C when mixed Impact 50 cm forward / 50 cm backward Scratch Pass Flexibility 7.5 10 mm. Application Methods Airless Spray Air Spray Thinning (Max Vol.) 206 Extra Slow (0.30 part by volume) 204 Slow (0.30 part by volume) 202 Fast (0.30 part by volume) 206 Extra Slow (0.30 part by volume) 204 Slow (0.30 part by volume) 202 Fast (0.30 part by volume) Thinning / Cleaning of Tools Numix Thinner 202. Mixing Ratio Base: 2.0 parts by volume. Curing Agent (hardener): 1.0 part by volume. Pot Life 4-6 hrs (20ºC). Film Thickness (D.F.T.) 33.5 microns 1.34 mils. (W.F.T.) 70 microns 2.8 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016 " - 0.019" Nozzle Pressure: 2000 P.S.I. The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. 1/2

NUMIX CLEAR COAT 2K DRYING TIME For optimum Drying / Curing, good ventilation is always a recommendation. In oven: full curing needs 30 min. @ 60ºC. Without oven: see the table. STEEL TEMP DRY TO TOUCH IN RECOATING INTERVAL FULLY CURED HOURS MINIMUM MAXIMUM 20ºC 6 hrs 7 days 12 hrs 48 hrs 30ºC 5 hrs 6 days 10 hrs 48 hrs 40ºC 3 hrs 5 days 8 hrs 48 hrs Shelf Life 24 months @ 20ºC. obtai ned under controlled conditions. We reserve the right to change data without prior notice. 2/2

NUMIX - HARDENER Diluted aliphatic polyisocyanate hardener for polyurethane acrylic paint. Polyurethane acrylic coating application - depends on prevailing temperature. Transparent Viscosity (20Cº) ford cup 4 15 sec Specific Gravity 0.96 Solid by Weight% 37 ± 2 Mixing Ratio 50% Drying time Fast hardener Standard Hardener Slow hardener L20 S20-30 M30 20 C Dust Free 25 min. 45 min. 45 min. Tack free 3 hrs. 3.5 hrs. 4 hrs. Dry To Handle 6 hrs. 10 hrs. 12 hrs. Hard Dry 9 hrs. 16 hrs. 18 hrs. 60 C Dust Free 5 min. 5 min. 5 min. Tack free 15 min. 15 min. 15 min. Dry To Handle 20 min. 40 min. 50 min. Hard Dry 25 min. 45 min. 50 min. Pot life 25 C 2 hrs. 6 hrs. 8 hrs. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

NUMIX THINNER Special formulated thinner for acrylic polyurethane coatings application. It contains organic volatile solvents. For car refinish coating application at prevailing temperature. Transparent Viscosity (20ºC) 15-20 sec. Specific Gravity 0.97-0.87 Evaporation Rate 5-15 min. Flash Point 25-54ºC Mixing Ratio by Volume 20-50% Fast Thinner 202 For spot and repairs - or for complete re-sprays provided the temperature in the spray booth does not exceed 20 C Slow Thinner 204 For treatment of large vehicles within the temperature range of 20-30 C Extra Slow 206 For treatment of large vehicles within the temperature range of 30-40 C obtai ned under controlled conditions. We reserve the right to change data without prior notice.

NUMIX RETARDANT THINNER Slow thinner of special composition which can be used in conjunction with various thinners or pure at high temperatures and/or when large vehicles are to be painted, to keep 1K/2K product film longer open to give better overspray met-in and better flow, certainly at high temperature. It will not affect the gloss level. At high temperatures (above 25 C) and when large vehicles are to be painted. Transparent Flash Point 94 C Mixing Ratio by Volume: At high temperatures (above 25 C) and when large vehicles are to be painted, it is recommended to add 10-30 % by volume of Numix Retardant Thinner to the thinner specified for the product concerned at higher temperatures (204 Thinner Slow or 206 Extra Slow, for example). Next add this mix to the product, using the mixing ratio specified in its technical data sheet. This will have a positive effect on its spray and flow characteristics and overspray will be avoided. At temperatures above 40 C, Numix Retardant Thinner can also be used pure. In this case, add Numix Retardant Thinner to the product as specified in its technical data sheet, using it as a substitute for the thinner originally recommended. Thinning None the product comes ready to use. HANDLING 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

NUMIX ANTI SILICON Specially selected additive to improve the leveling and remove paint film defects such as fish eye or craters. Leveling improvement of car refinish coating by adding 2% to the paint. Transparent Specific Gravity 0.96 Flash Point 27 C Mixing Ratio by Volume 5-10 gram for liter of paint at spraying viscosity. Mix well before spray. Surface should be well prepared to obtain excellent smooth surface. At the time of application it should be clean and dry. HANDLING 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

NUMIX SPOT REPAIR THINNER Numix Spot Repair Thinner is a clear transparent blending additive thinner that contains acrylic resin and special blend of solvent to allow easier application of Numix Base Coat Spot Repair. It is ready to use where it can be used as foundation for fade out area or used as additive with basecoat colors, solids or metallic, before application of fade out area. Can be applicable over Numix Top Coat 2K and Numix Clear Coat 2K. As a clear foundation coat for fade out areas. Application Methods: The application method and mixing ratio are depending on the specific use of the product, where the user can select the appropriate method as follows: 1- As a clear foundation to improve the blending of base coat in the spot repair area. Apply 1 single coat of Numix Spot Repair Thinner over the blending area where high gloss and shining coat must be obtained, allow 3-5 minutes flash off @ (20ºC) before spot area with Numix Base Coat 1K taking into consideration that base coat must stay within the coated area spot repair thinner. Note: clear coat must be applied over the spot repair area. 2- Numix Spot Repair Thinner as additive to base coat before blending and fading out. Mix: 100 parts by volume base coat. 50 parts by volume Numix Thinner fast or slow. Apply the mixture until full coverage over the primer area; allow 2-3 minutes flash-off time between coats. Then mix base coat color 100 parts, with 100 parts by volume of Numix Spot Repair Thinner, spray 1-2 single coats extending beyond the spot repair area with gradual fading out. Allow 15-20 minutes @ 20 C finally apply a Numix Clear Coat. Thinning HANDLING None, the product comes ready to use. 12 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

NUMIX PLASTICIZER Numix Plasticizer is designed to increase flexibility, impact resistance, chip resistance, and U.V. protection in Numix Top Coat 2K products, it mixes easily and does not affect dry or cure times. To improve the flexibility of Numix Top Coat 2K and Numix Clear Coat 2K and over a wide variety of semi-rigid and flexible plastic parts. Slightly Yellowish. Flash Point 27ºC Application Methods To be added to Numix Top Coat 2K and Numix Clear Coat 2K. Mixing Ratio by Volume 5-10% for a liter of paint to be added at spraying viscosity, mix well after addition. Pot Life 4-6 hrs. Surface should be well prepared to obtain excellent smooth surface. At the time of application it should be clean and dry. HANDLING 12 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

NUMIX MA - 4 MATTING PASTE Numix MA-4 Matting Paste standard matting paste designed specially to matt and reduces the gloss level old Numix Top Coat 2K. Over plastic substrates or any other areas that require low gloss. Transparent Viscosity (20ºC) 45 Poise Specific Gravity 1.40 ± 2 Solid by Weight % 55 ± 2 Flash Point Approx 22 C. Application Methods Thinning Mixing Ratio by Volume Numix MA-4 Matting Paste can be used with any ratio according to the desired level of gloss, the table below explains the mixing ratio with Numix Top Coat 2K: Gloss Level Parts Numix Top Parts Numix MA-4 Coat 2K Matting Paste Eggshell (40-60) 100 50 Matt (10-20) 100 100 Numix Thinner. Film Thickness 35 microns 1.4 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016" - 0.019" Nozzle Pressure: 2000 P.S.I After mixing Numix Top Coat 2K with Numix MA-4 Matting Paste stir the mixture thoroughly, then continue by adding the hardener and the thinner of your choice as per the following ratio: Numix Top Coat 2K & Numix Numix Numix MA-4 Matting Paste Hardener Thinner 100 50 30 Surface should be well prepared to obtain excellent smooth surface. At the time of application it should be clean and dry. 1/2

NUMIX MA - 4 MATTING PASTE HANDLING 12 months. obtained under controlled conditions. We reserve the right to change data without prior notice. 2/2

(B-4) MISCELLANEOUS FAST CUT POLISH SOFT POLISH GRAVEL GUARD (GOMA)

FAST CUT POLISH A special water base formulation based on resins and coarse silica which cleans the surface, removes imperfections in the finish and polishes it to give a very smooth surface. Use before National Soft Polish for automotive finishes (National N.C. and Acrylic Polyurethane). Orange Viscosity (25ºC) Paste like Specific Gravity 1.39 ± 0.05 Solid By Weight% (110ºC) 54 ± 5% PH 9.5 ± 1 Silica Contants (<=75µ) 53 ± 4 % Oil Contents (P.B<80ºC) 17 ± 4% Thinning / Cleaning of Tools Cleaning of Tools By cotton or special tool. Put polish on surface and apply several times by equal pressure on the surface with smooth cloth or cotton,.then this use National Soft Polish to maximise the gloss. Water. Should be dry, clean and free from all loose particles. CONDITIONS DURING APPLICATION The temperature of the substrate should be minimum 10ºC above the dew point and relative humidity measured in the substrate vicinity. Polishing should be carried out after complete drying of paint and according to paint system. HANDLING 12 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

SOFT POLISH A special water base formulation based on resins and coarse silica which gives high gloss polish to the smooth surface and also cleans by removing the dirts. Use before National Fast Cut Polish for automotive finishes (National N.C. and Acrylic Polyurethane). White. Viscosity (25ºC) 70-80 Poise. Specific Gravity 1.2 ± 0.02 Solid By Weight% 42 ± 2 % PH 9.5 ± 0.5 Thinning / Cleaning of Tools Cleaning of Tools By cotton or special tool. Put polish on surface and apply several times by equal pressure on the surface with by smooth cloth or cotton. Water. Should be dry, clean and free from all loose particles. CONDITIONS DURING APPLICATION The temperature of the substrate should be minimum 10ºC above the dew point and relative humidity measured in the substrate vicinity. Polishing should be carried out after complete drying of paint and according to paint system. HANDLING 12 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

GRAVEL GUARD (GOMA) A special resin blend base undercoat which gives a tough textured undercoat to the refinishing that gives extra protection against stone and gravel chipping. Has good color retention, high resistance to severe weather conditions, good durability and flexibility. For refinishing plastisol area on cars as replacement coating. Color White, Black. Finish Matt textured. Viscosity (25ºC) 8-12 Poise. Specific Gravity 1.45 ± 0.07 Solid by Weight % 70 ± 5% Theoretical Spreading Rate 5-12 m 2 /Lit. Drying time Touch dry: 5-10 min. Hard dry : 8 hrs. Impact resistance (25 cm) pass Scratch resistance pass Bending test ( 15 mm) pass Water resistance (24 hrs) spot pass test Application Methods Special Spray Gun. Thinning / Cleaning of Tools Ready for use, could be diluted with Synthetic Thinner Film Thickness (D.F.T.) 70 microns. Guiding Data for Airless Spray Nozzle Tip: 0.015" - 0.20" Nozzle Pressure: 2200 P.S.I. Surface must be clean, dry and free from oil grease, dirt etc. HANDLING 12 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

(C) FURNITURE & WOOD FINISH PAINTS (C-1) NITROCELLULOSE PAINTS FLEX CLEAR COAT LACQUER TOP CLEAR COAT LACQUER FLEX SANDING SEALER TOP SANDING SEALER N.C WOOD STAIN N.C THINNER (C-2) ACRYLIC POLYURETHANE POLYURETHANE SANDING SEALER POLYURETHANE CLEAR COAT ACID CURING

(C-1) NITROCELLULOSE PAINTS FLEX CLEAR COAT LACQUER TOP CLEAR COAT LACQUER FLEX SANDING SEALER TOP SANDING SEALER N.C WOOD STAIN N.C THINNER

FLEX CLEAR COAT LACQUER It is a fast drying special clear finish based on combination of Nitrocellulose and Alkyd Resins. It has good flexibility and water resistance. On wooden furniture, kitchen cabinets and as clear finish on automobiles. It can also be used with wood stains. Clear Finish Matt or Glossy (85-92 @ 60 ). Viscosity (25ºC) 45-50 Poise (if dilute with thinner 1:1 for application) 15-25 sec. (ford cup). Specific Gravity 0.96 ± 0.02 Solid by Weight % 40 ± 2 % Theoretical Spreading Rate 6-7 m²/lit. @ 25 microns (D.F.T.). Drying time Touch dry: 20 min. Recoatable: Min 1 hr. Max 3 hrs. @ 20ºC. Hard dry: 6 hrs. (depending upon thickness). Flash Point 7ºC when mixed. Application Methods Airless Spray Air Spray Thinning (Max Vol.) (50%) (50%) Thinning / Cleaning of Tools National Thinner 121 or National Special Thinner. Mixing Ratio Single pack dilution (1:1). Film Thickness (D.F.T.) 25 microns 1.0 ml. (W.F.T.) 70 microns / 2.8 ml. Guiding Data for Airless Spray Nozzle Tip: 0.016 " - 0.019" Nozzle Pressure: 2000 P.S.I. The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. HANDLING 24 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

TOP CLEAR COAT LACQUER It is a fast drying special clear finish based on combination of Nitrocellulose and Alkyd Resins. It has good flexibility and water resistance. On wooden furniture, kitchen cabinets and as clear finish on automobiles. It can also be used with wood stains. Clear Finish Matt or Glossy (85-92 @ 60 ). Viscosity (25ºC) 8-12 Poise. Specific Gravity 1.01 ± 0.02 Solid by Weight % 50 ± 1 % Theoretical Spreading Rate 7-8 m²/lit. @ 30 microns (D.F.T.). Drying time Touch dry: 20 min. Recoatable: Min 1 hr. Max 3 hrs. @ 20ºC. Hard dry: 6 hrs. (depending upon thickness). Flash Point 7ºC when mixed. Application Methods Airless Spray Air Spray Thinning (Max Vol.) (100%) (100%) Thinning / Cleaning of Tools National Thinner 121 or National Special Thinner. Mixing Ratio Single pack dilution (1:1). Film Thickness (D.F.T.) 30 microns 1.2 ml. (W.F.T.) 70 microns 2.8 ml. Guiding Data for Airless Spray Nozzle Tip: 0.016 " - 0.019" Nozzle Pressure: 2000 P.S.I. The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. HANDLING 24 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

FLEX SANDING SEALER It is a special fast drying Sealer based on Nitrocellulose/Alkyd combination. On wooden surfaces like furniture, kitchen cabinets, etc. can also be used with wood stains. Clear Finish Matt. Viscosity (25ºC) 80-100 Poise. Specific Gravity 0.96 ± 0.04 Solid by Weight % 40 ± 5% Theoretical Spreading Rate Approx. 8-10 m²/lit. (depending upon porosity of the surface). Drying time Touch dry: 10-15 min. Recoatable: 3-4 hrs. Hard dry: 3-4 hrs. (depending upon thickness). Flash Point 7º C when mixed. Application Methods Airless Spray Air Spray Thinning (Max Vol.) (100%) (100%) Thinning / Cleaning of Tools National Thinner 121 or National Special Thinner. Mixing Ratio Single pack dilution (1:1) Film Thickness (D.F.T.) 25 microns 1.0 mils. (W.F.T.) 70 microns 2.8 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016 " - 0.019" Nozzle Pressure: 2000 P.S.I. The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. HANDLING 24 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

TOP SANDING SEALER It is a special fast drying Sealer based on Nitrocellulose/Alkyd combination. On wooden surfaces like furniture, kitchen cabinets etc. Can also be used with wood stains. Clear Finish Matt. Viscosity (25ºC) 80-100 Poise. Specific Gravity 1.00 ± 0.02 Solid by Weight % 45 ± 2% Theoretical Spreading Rate Approx. 4-5 m²/lit. (depending upon porosity of the surface) Drying time Touch dry: 20 min. Recoatable: Min 1 hr. Max 3 hrs. @ (20ºC). Hard dry: 3-4 hrs. (depending upon thickness). Flash Point 7ºC when mixed. Application Methods Airless Spray Air Spray Thinning (Max Vol.) (100%) (100%) Thinning / Cleaning of Tools National Thinner 121 or National Special Thinner. Mixing Ratio Single pack dilution (1:1). Film Thickness (D.F.T.) 25 microns 1.0 mils. (W.F.T.) 70 microns 2.8 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016 " - 0.019" Nozzle Pressure: 2000 P.S.I. The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. HANDLING 24 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

N.C. WOOD STAIN A decorative color stain based on Nitrocellulose Resin which gives a transparent wood color, weather resistant and durable. On wooden surfaces. As per shade card. Viscosity (25ºC) 30-35 sec. Specific Gravity 0.93 ± 0.02 Solid by Weight % 18 ± 3 % Covering Capacity 15 m 2 /Lit. Drying time Touch dry : 10-15 min. Recoatable: 30-45 min. Flash Point 8ºC Application Methods Thinner / Cleaning of Tools Brush or spray. National Thinner 121 or National Special Thinner. Surface should be dry, clean and free from dust. HANDLING 24 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

N.C. THINNER It is a special blend of organic solvents developed for thinning the National range of products bearing the application requirements in mind. For Nitrocellulose lacquers and other Industrial Paints. Clear Flash Point (T.C.C / F) 40-50 Boiling Point (760 torr/ F) 150-200 Specific Gravity (60 F) 0.85-0.90 Refractive Index (20 C) 1.30-1.50 HANDLING 24 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

(C-2) ACRYLIC POLYURETHANE POLYURETHANE SANDING SEALER POLYURETHANE CLEAR COAT ACID CURING

POLYURETHANE SANDING SEALER National Polyurethane Sanding Sealer is a fast drying, two-component base sealer, which has excellent resistance to water, abrasion and marine environments. As a wooden surface for all architectural purposes where reasonable high degree of filling, leveling and sanding is a criterion. Clear Finish Smooth, Matt. Viscosity (20ºC) 6-8 Poise. Specific Gravity 0.98 ± 0.02 Solid by Weight % 40 ± 2 % Theoretical Spreading Rate Approx. 5-6 m²/lit. (depending upon porosity). Drying Time Touch dry : 30 min. Sandable dry: 2 hrs. (20ºC) Recoatable : 4 hrs. (20ºC) Flash Point 25ºC. Flexibility 7.5-10 mm. Application Methods Airless Spray Air Spray Thinning (Max Vol.) 204 (15-20%) 204 (15-20%) Thinning / Cleaning of Tools National Thinner 204. Mixing Ratio Base: 5 parts by volume. Curing Agent (hardener): 2.5 part by volume. Pot Life 6-8 hrs (20ºC). Film Thickness (D.F.T.) 27 microns 1.08 mils. (W.F.T.) 70 microns 2.8 mils. Guiding Data for Airless Spray Nozzle Pressure: 1500-2100 P.S.I. Nozzle Tip: 0.016 " - 0.019" The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

POLYURETHANE CLEAR COAT National Polyurethane Clear Coat is a two-component topcoat with excellent gloss and color retention and specially very good resistance against U.V rays. As a finishing coat for protection of structural steel in severely corrosive environment, where gloss and color retention is required. Also suitable as topcoat in superior exterior masonry finishes. Also as a finish coat for furniture and wooden work (joinery). Clear. Finish Glossy (93-96 @ 60 ) Viscosity (20ºC) 60-90 seconds. Specific Gravity 1.02 ± 0.05 (of mix). Solid by Weight % 56 % Theoretical Spreading Rate 5-6 m²/lit. @ 40 microns (D.F.T.). Drying Time Touch dry: 3-5 hrs. Recoatable: Min: 12 hrs. (20ºC). Max : 48 hrs. (20ºC). Flash Point 25ºC when mixed Impact 50 cm forward / 50 cm backward. Scratch Pass Flexibility 7.5-10 mm. Application Methods Airless Spray Air Spray Thinning (Max Vol.) 204 (10%) 204 (10%) Thinning / Cleaning of Tools National Thinner 204. Mixing Ratio Base: 2.0 parts by volume. Curing Agent (hardener): 1.0 part by volume. Pot Life 6-8 hrs (20ºC). Film Thickness (D.F.T.) 33.5 microns 1.34 mils. (W.F.T.) 70 microns 2.8 mils. Guiding Data for Airless Spray Nozzle Tip: 0.016 " - 0.019" Nozzle Pressure: 2000 P.S.I. The surface should be clean and dry at the time of application and its temperature must be above the dew point to avoid condensation. 1/2

POLYURETHANE CLEAR COAT DRYING TIME For optimum Drying / Curing, good ventilation is always a recommendation. In oven: full curing needs 30 min. @ 60ºC. Without oven: see the table. STEEL TEMP DRY TO TOUCH IN RECOATING INTERVAL FULLY CURED HOURS MINIMUM MAXIMUM 20ºC 6 hrs 7 days 12 hrs 48 hrs 30ºC 5 hrs 6 days 10 hrs 48 hrs 40ºC 3 hrs 5 days 8 hrs 48 hrs product should be kept in cool and well ventilated place, protected from heat and direct sunlight at temp 5-35ºC. Containers must be kept tightly 24 months @ 20ºC. wear eye protector. In case of contact with eyes, rinse immediately with plenty of water and seek medical advice. To remove splashes from skin; use soap and water or a recognized skin cleaner. obtai ned under controlled conditions. We reserve the right to change data without prior notice. 2/2

ACID CURING A two component fast drying Acid Curing finish, with excellent gloss, excellent impact scratch, water and grease resistance. For sealing and top-coating of wood for interior and exterior applications. Clear & Color. Finish Glossy & Matt. Viscosity (25ºC) 6.5-7.5 Poise. Specific Gravity 1.1 ± 0.1 Solid by Weight % 52 ± 2% Theoretical Spreading Rate 8-10 m 2 /Lit. Drying Time Touch dry: 15 min. Sanding dry: 1½ - 2 hrs. Flash Point Above 20ºC Pot Life 8 hrs. Application Methods Spray gun or curtain coater. Thinner / Cleaning Tools Acid Curing Thinner. Mixing Ratio Parts (A) 9 : Parts (B) (curing agents) 1. Film Thickness (D.F.T.) 40-45 microns. (W.F.T.) 80-100 microns. Guiding Data for Airless Spray Nozzle Tip: 0.011" - 0.013" Nozzle Pressure: 1500 P.S.I. A thorough sanding between the coats is essential to the adhesion. HANDLING 18 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

(D) STOVING SYSTEM ALKYD MELAMINE STOVING PAINT ACRYLIC STOVING PAINT SILICONE STOVING PAINT TIN PLATE LACQUER

ALKYD MELAMINE STOVING PAINT A high class stoving finish, based on Alkyd / Melamine resins, nonyellowing, and having excellent hardness and durability, mar proofness and water resistance. For all house appliances, such as Washing Machines, Gas Cookers and Refrigerators, etc As per shade card. Gloss Gloss, 80 @ 60. Viscosity (25ºC) 5-8 Poise. Specific Gravity 1.1 ± 0.12 Solid by Weight% 55 ± 5% Covering Capacity 7-12 m 2 /Lit. Flash Time 20 minutes at normal temperature. Method of Application Thinning Clearing of Tools Viscosity of application (20ºC) (Ford cup No 4) Thermohardening Stoving condition Spray Gun. 10-20 % with National Stoving Thinner. With National Stoving Thinner. 20-30 sec. 20 minutes @ 120ºC. In case of pinholes presence, add 0.1% of National Antisilicone by weight per batch. Elongation (180º pin, 7mm) Impact Strength (Erichsen 5/8) 10 inch Adhesiveness Hardness (lead pencil) Water Resistance (38 C, 200 hr) Corrosion Resistance (38 C, 200 hr) AFTER APPLICATION TESTS No cracks No cracks No squares F - H No change 2.0 mm. Surface should be dry and free from dust. 1/2

ALKYD MELAMINE STOVING PAINT HANDLING The product must be stored according to National Regulations.The product should be kept in cool and well ventilated place, protected from heat and direct sunlight at temp 5-35ºC. Containers must be kept tightly 12 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice. 2/2

ACRYLIC STOVING PAINT A high class stoving finish, based on Acrylic / Epoxy resins, non-yellowing and having excellent hardness and durability, mar proofness and water resistance. For all house appliances, such as Washing Machines, Gas Cookers and Refrigerators, etc White. Gloss Gloss, 80 @ 60 Viscosity (25ºC) 5 8 Poise. Specific Gravity 1.23 ± 0.02 Solid by Weight% 57 ± 2% Covering Capacity 10 m 2 /Lit. Flash Time 20 minutes at normal temperature. Method of Application Thinning Clearing of Tools Viscosity of application (20ºC) (Ford cup No4) Thermohardening Stoving condition Spray Gun. 10 20 % with National Stoving Thinner. With National Stoving Thinner. 20-30 sec. 20 minutes @ 180ºC. In case of pinholes presence, add 0.1% of antisilicone by weight per batch. AFTER APPLICATION TESTS Elongation 180º pin, 7mm No cracks Impact Strength (Erichsen 5/8) 28 No cracks inche Adhesiveness No squares Hardness (Lead Pencil) F - H Ethyl Alcohol Resistance 94%, 24 hrs. No change Sodium Hydroxide Resistance 2%, 24 No change hrs. ORGANIC ACID RESISTANCE: Citric Acid 8% No change Acetic Acid 8% No change Lactic Acid 8% No change FOODSTUFFS RESISTANCE: Olive Oil 24 hrs. No change Coffee 24 hrs. No change Tomato Paste 24 hrs. No change Water Resistance (38 C, 200 hrs.) No change Corrosion Resistance (38 C, 200 hrs.) 2.0 mm 1/2

ACRYLIC STOVING PAINT Surface should be dry and free from dust. : HANDLING: : : The product must be stored according to National Regulations.The product should be kept in cool and well ventilated place, protected from heat and direct sunlight at temp 5-35ºC. Containers must be kept tightly 12 months. - Avoid contact with skin and eyes. While painting it is advisable to wear eye protector. In case of contact with eyes, rinse immediately with plenty of water and seek medical advice. To remove splashes from skin; use soap and water or a recognized skin cleaner. obtai ned under controlled conditions. We reserve the right to change data without prior notice. 2/2

SILICONE STOVING PAINT A high class stoving finish, based on Alkyd/Melamine and Silicon resins, non-yellowing and having excellent hardness and durability, mar proofness and water resistance. For all house appliances, such as Washing Machines, Gas Cookers and Refrigerators, etc Red, Silver, White, Black. Gloss Gloss Viscosity (25ºC) 2 6 Poise. Specific Gravity 1.10 ± 0.02 Solid by Weight % 55 ± 5 % Covering Capacity 6 12 m 2 /Lit. (depending on the colors used). Flash Time 30 minutes at normal temperature. Method of Application Thinning / Cleaning of Tools Viscosity of application (20ºC) (Ford cup No 4) Thermohardening Stoving condition Spray Gun. 5 10 % with National Stoving Thinner. 30 50 30 minutes @ 200ºC. In case of pinholes presence, add 0.1% of antisilicone by weight per batch. AFTER APPLICATION TESTS Elongation (180º pin, 7mm) No cracks Impact Strength (Erichsen 5/8) 28 No cracks inch Adhesiveness No squares Hardness (lead pencil) F H Ethyl Alcohol Resistance 94%, 24 No change hrs. Sodium Hydroxide Resistance 2%, 24 No change hrs. ORGANIC ACID RESISTANCE: Citric Acid 8% No change Acetic Acid 8% No change Lactic Acid 8% No change FOODSTUFFS RESISTANCE: Olive Oil 24 hrs. No change Coffee 24 hrs. No change Tomato Paste 24 hrs. No change Water Resistance (38 C, 200 hrs.) No change Corrosion Resistance (38 C, 200 hrs.) 2.0 mm 1/2

SILICONE STOVING PAINT Surface should be dry and free from dust. : HANDLING: : : The product must be stored according to National Regulations.The heat and direct sunlight at temp 5-35ºC. Containers must be kept tightly 12 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice. 2/2

TINPLATE LACQUER A Protection Lacquer based on Epoxy / Phenolic / Acrylic resins, which is flexible and has good adhesion. For Internal Lacquering of Drums - Tinplate - Cans. etc... Yellow. Gloss 80-90 Angel 60º. Viscosity (20ºC) 85 ± 5 sec. Specific Gravity 0.98 ± 0.02 g/ml. Solid by Weight% 39 ± 2 % DryingTime 1 coat : 15 min 160ºC 2 coats: 15 min 220ºC Or if single coat: 15 min. 220ºC. Film Thickness Single coat Double coat Film Thickness Film Weight Film Thickness Film Weight WET Film 71.4µ 83.3 47.6µ 59.5 gm/m 2 gm/m 2 DRY Film 30µ 35 20µ 25 gm/m 2 gm/m 2 Flash point 38ºC Application Methods Airless Spray Thinning / Clearing of Tools Xylene Mixing Ratio Single pack ready for use or you can reduce by thinner 10%. : HANDLING: : : The product must be stored according to National Regulations.The heat and direct sunlight at temp 5-35ºC. Containers must be kept tightly 12 months. obtai ned under controlled conditions. We reserve the right to change data without prior notice.

(E) EPOXY SYSTEM EPOXY INTERMEDIATE HB 2.19 EPOXY ZINC RICH PRIMER HB 10.03 GUARD EPOXY SF EPOXY ZINC PHOSPHATE PRIMER 10.06

EPOXY INTERMEDIATE HB 2.19 A heavy duty, high built epoxy undercoat suitable for the protection of steel surfaces in very aggressive environmental conditions and in general for all surfaces in non-immersion conditions. It can be over coated by epoxy finish 10.41 or where resistance to yellowing and chalking is required, National Acrylic Urethane (2K) Finish or National Acrylic (1K) Finish is recommended. Can also be over coated by conventional and chlorinated rubber finish coats. White. Finish Matt. Specific Gravity 1.3 ± 0.05 Kg/Lit. Volume Solid 59% Theoretical Spreading Rate 4.7-5.9 m 2 / Lit. Drying Time (25ºC) Touch dry: 6 hrs. Hard dry: 48 hrs. Recoatable: 24-72 hrs. Flash Point >40 C. Application Methods Airless spray; brush or roller application. Thinning / Cleaning of Tools Epoxy Thinner 6.03. Mixing Ratio Volume: 80 A : 20 B. Potlife (25 C) 6 hrs. Film Thickness (D.F.T.) 100-125 microns. (W.F.T.) 170-212 microns. Guiding Data for Airless Spray Tip Size: 0.482-0.660 mm. Line pressure: 120-150 Bar. Fan angle: 60-80. Surface should be dry and clean from rust, dust, dirt, grease, etc. : HANDLING: : : The product must be stored according to National Regulations.The heat and direct sunlight at temp 5 35ºC. Containers must be kept tightly 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice.

ZINC RICH EPOXY PRIMER HB 10.03 A zinc pigmented quick drying epoxy primer for grit blasted steel which is highly weather resistant and will protect against corrosion for extended time periods. Can be used as a shop primer or holding primer and may even be left without a topcoat in areas inaccessible after fabrication. This product is also recommended for use in container systems. It has been specially formulated to have more than 90% Zinc content in the dry film. Always avoid a first coat which contains materials that react with Zinc e.g. drying oils. Grey. Finish Matt. Specific Gravity 2.4 Kg/Lit. Volume Solid 65% Theoretical Spreading Rate 8.7-13 m 2 / Lit. Drying Time (25ºC) Touch dry: 1 hrs. Hard dry: 10 hrs. Recoatable: 3 4 days. Flash Point >40 C. Application Methods Designed for application by spray (either conventional or airless) but small areas maybe touched up by brush ideally. Thinner / Cleaning of Tools Epoxy Thinner. Mixing Ratio Volume: 80 A : 20 B. Potlife (25 C) 8 hrs. Film Thickness (D.F.T.) 50-75 microns. (W.F.T.) 77-115 microns. Guiding Data for Airless Spray Tip Size: 0.331-0.381 mm. Line pressure: 120-150 Bar. Fan angle: 60º - 80. Surface should be free from grease, salt and should be dry before grit. Pay particular attention to welds and cut areas to ensure no dirt is left on the steel. 1/2

ZINC RICH EPOXY PRIMER HB 10.03 : HANDLING: : : The product must be stored according to National Regulations.The heat and direct sunlight at temp 5-35ºC. Containers must be kept tightly 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice. 2/2

Guard Epoxy SF A solvent free, two component, self leveling, high build, pure epoxy coating which cures to a film with excellent resistance to water, mineral oils, chemicals, various acid & alkali solution. Dried film has good impact and abrasion resistance and environment-friendly. Protective coating for concrete & cement walls and floors. Industrial floors, workshop floors, kitchens, breweries, beverage stores, hospitals and operation rooms, stalls and garages. TECHNICAL DATA Finish Glossy or Semi-Gloss Limited Clear Volume Solid 100% 100% Specific Gravity KG/L 1.40 ± 0.05 (mixed) pastel color 1.09 ± 0.05 clear Theoretical Spreading Rate 3.3 m 2 / Ltr 3.3 m 2 / Ltr Film Thickness (DFT) Mircons 300 300 Film Thickness (WET) Mircons 300 300 Drying Time (30ºC) Temperature, humidity, air movement, film thickness and number of coats all affect the drying time. Touch dry : 5-6 hrs. Recoatable : 8-48 hrs. Fully cured : 7 days Application Methods Airless spray, trowel, roller or brush (touch-up). Thinning (Volume) Ready for use Thinner / Cleaner National Epoxy Thinner Guiding Data for Airless Spray Nozzle Tip : 0.025" - 0.030" Nozzle Pressure : 3000 P.S.I Conv. Spray Requirments Atomizing pressure. : 50 P.S.I Mixing Ratio Base: Hardener : 4 :1 and for Clear 2:1 Potlife (30 C) 15-20 minutes. Recommended System Apply on clean, dust free surface No of coats x DFT (microns) - National Guard Primer For Cement (Clear) 1 x 40 - National Guard Epoxy SF 1-2 x 300 For anti-skidding, spread aggregates, when first coat is wet. Apply second coat as a topcoat after 8 hrs. Surface should be free of salt, grease etc. After blasting remove dust by suction cleaning before inspection. Apply coating after inspection approval only. 1/3

Guard Epoxy SF : HANDLING: : : The product must be stored according to National Regulations.The heat and direct sunlight at temp 5-35ºC. Containers must be kept tightly 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice. 2/3

Guard Epoxy SF CHEMICAL RESISTANCE 1. HYDROCARBONS All of them except Xylene, Toluene, Styrene. 2. ALCOHOLS Almost all except high conc. of Ethanol above 50%. 3. ALDEHYDES Formaldehyde 37-40%. 4. ACIDS INORGANIC All acids conc. Ranging (5-10%) only, like Nitric Acid 10% and Hydrochloric acid 10%. Except Phosphoric Acid 40%. 5. ACIDS ORGANIC All acids conc. Ranging (5-10%) Except Lactic Acid 10%. 6. KETONES Not Recommended only (Di-Isobutyl Ketone). 7. ETHER / GLYCOL ETHER Not Recommended. 8. ESTER Not Recommended. 9. CHLORINATED SOLVENT Some of them like CCL 4. 10. AMINES, AMIDES, IMIDES Ammonia 25-40%. 11. VEGETABLE & ANIMAL OILS Castor Oil, Coconut Oil, Fuel Oil, Linseed Oil, Peanut Oil, Pine Oil, Sunflower, Tall Oil. 12. MISCELLANEOUS De-ionized Water, Creosol, Sodium Chloride 2%, Sodium Hydroxide 5% - 30%. 13. NaCl 5% 24 hrs resistance Mechanical Resistance 14. SCRATCH RESISTANCE 1KG Pass 15. BENDING RESISTANCE 10 MM Pass 3/3

EPOXY ZINC PHOSPHATE PRIMER 10.06 Zinc Phosphate Epoxy Primer is a two component rust preventing primer based on epoxy resin and zinc phosphate as corrosion inhibiting pigment. As a primer on steel in moderate to severe corrosive environment. Grey. Finish Matt. Specific Gravity 1.6 ± 0.06 Kg/Lit. Volume Solid 56 % Theoretical Spreading Rate 10m 2 / Lit (D.F.T 50 µ) Drying Time (25ºC) Touch dry: 4-6 hrs.. Recoatable: min: 10 hrs max: 3 days (20 C). Flash Point 25 C (when Mixed). Application Methods Airless Air Spray Brush Thinning / Cleaning of Tools 5% 15% 10% Epoxy Thinner (max Volum) Mixing Ratio Base: 4 parts by volume: Curing Agent: 1 part by volume. Potlife (25 C) 8 hrs (20 C). Film Thickness (D.F.T.) 56 microns 2.24 mil (W.F.T.) 100 microns 4 mils. Guiding Data for Airless Spray Nozzle Orifice: 0.020" Nozzle Pressure: 2300 P.S.I. Surface should be dry and clean from rust, dust, dirt, grease, etc. DRYING TIME - For optimum Drying / Curing good ventilation is always a recommendation: Steel Temp Dry To Touch Fully Cured Recoating Interval Minimum Maximum 25 C 6 hrs 7 days 10 hrs 3 days 35 C 5 hrs 6 days 8 hrs 2 days 45 C 4 hrs 5 days 6 hrs 1 day 1/2

EPOXY ZINC PHOSPHATE PRIMER 10.06 : HANDLING: : : The product must be stored according to National Regulations.The heat and direct sunlight at temp 5-35ºC. Containers must be kept tightly 24 months. obtained under controlled conditions. We reserve the right to change data without prior notice. 2/2