CERTIFICATE OF APPROVAL No ME 5078 1 İNŞAAT ve REKLAM ÜRÜNLERİ SAN. TİC. LTD. ŞTİ Kaleiçi Mah. Gökçeali Cad. No:39/A PK.34540 Çatalca/İstanbul Have been assessed against the requirements of the test standard(s) denoted below and are approved for use subject to the conditions appended hereto: CERTIFIED PRODUCT TEST STANDARD EURAMETAL Branded ACP EN 13501 - Classification A2-s1, d0 Signed and sealed for and on behalf of EWCL5 Sir Ken Knight Chairman WCL Impartiality Committee Paul Duggan Certification Manager Warrington Certification Ltd Page 1 of 6
General description Thickness of composite Weight per unit area of composite Description Composite aluminium panel EURAMETAL Branded ACP White Yalcinlar Aluminyum Kompozit Pls.Ins.Ve Rekl.Urun.San. Tic. Ltd. Sti 4-5mm (stated by sponsor) 4.15mm (determined by Exova Warringtonfire) 8.80kg/m² (stated by sponsor) 7.95 kg/m² (determined by Exova Warringtonfire) 3105/H26 PVDF (2 Coat)- Comp. Panel Top coat (Test face) Primer Number of coats Density Curing process per coat Number of coats Density Curing process per coat Thickness Weight per unit area Polyvinylidene difluoride (PVDF) Pre Painted Alum -PVDF - Comp. Panel Ral 7039, Ral 7036 Grey Also see Note 2 below One 20 microns 1.31g/cm³ Roll coating (in coil coating line) Oven ( 4 Zone) Chrome Free Grey One 5 microns 1.14g/cm³ Roll coating (in coil coating line) Oven ( 4 Zone) Aluminyum 3015/H26 0.50±0.05mm 1.283m²/kg The component is inherently flame retardant Page 2 of 6 Signed
Adhesive Core Adhesive Page 3 of 6 Signed Hydro-modified ethylene vinyl acetate (EVA) and polyethylene (PE) FR Adhesive Film Composition details Between 60 and 70% Ethylene-vinyl acetate copolymer Between 30 and 40% Low density polyethylene (LDPE) Application rate 56g/m² 0.06mm Heat lamination Curing process A2 Grade FR Core Composition details Calcium sulphate 50% hydroxide 40% Other 10% Thickness 3.2mm Weight per unit area 6.05kg/m² Hydro-modified ethylene vinyl acetate (EVA) and polyethylene (PE) FR Adhesive Film Composition details Between 60 and 70% Ethylene-vinyl acetate copolymer Between 30 and 40% Low density polyethylene (LDPE) Application rate 56g/m² 0.06mm Heat lamination Curing process Aluminyum 3015/H26 Thickness 0.50±0.05mm Weight per unit area 1.283m²/kg
Description The component is inherently flame retardant 3105/H26 Backcoat- Comp. Panel Coating (Back face) Mounting and fixing Brief description of manufacturing process Pre painted Alum-Backcoat- Comp. Panel Grey Also see Note 2 below Number of coats One per coat 5 7 microns Density 1.280g/cm³ Roll Coating ( in coil coating line) Curing process per coat Oven ( 4 Zone) The product was mechanically fixed with an airspace. The product was tested with no joints. Coil-coating, de-coiling (2 zone) + accumulator + de-greasing + rinse (2 zone) + pre-treatment (chem coating) + oven + primer coat + primer oven (4 zone) + air cooling unit + water cooling + topcoat (2 station) + topcoat oven (4 zone) + air cooling unit + water cooling + online dry coating thickness measurements + accumulator + quality control section + shearing + coiling + quality control tests + packaging Note 1: The sponsor was unwilling to provide this information. Note 2: The sponsor declared that the colour tested had the highest organic content of all available colours Page 4 of 6 Signed
Certification Evidence 1. This certificate relates to the reaction to fire classification of the product EURAMETAL Branded ACP, an aluminium composite panel, when tested and classified in accordance with EN 13501-1: 2009, Fire classification of construction products and building elements Part 1: Classification using data from reaction to fire tests. 2. The certification is issued on the basis of: i) Initial type testing of a sampled test specimen ii) Inspection and surveillance of factory production control iii) Certification of Quality Management Systems to ISO 9001:2008 Initial Type Testing evidence listed in the table: Name of Laboratory Name of sponsor Test reports/extended application report Nos. Test method / extended application rules & date Exova Warringtonfire YALÇINLAR ALÜMİNYUM KOMPOZİT PLASTİK İNŞAAT ve REKLAM ÜRÜNLERİ SAN. TİC. LTD. ŞTİ WF 363796 EN 13823 WF 363794, WF 363795, WF 364338 WF 366250 WF 366262 EN ISO 1716 EN ISO Composite Summary report Classification report EN 13501 Page 5 of 6 Signed
3. The test results are valid for the tested product composition and specimen configuration, as described in section 4.3 Field of application of the classification report. The test results are valid for all colours. 5. The test and classification results on test specimen constructed from EURAMETAL Branded ACP are reported in Exova Warringtonfire Classification Report No. 366262, dated 24 th May 2016. Reaction to fire classification: A2-s1, d0 Page 6 of 6 Signed