Influence of Steel Scrap on Microstructure and Mechanical Properties of Spheroidal Graphite Cast Iron



Similar documents
How To Study The Effects Of Section Size On The Content Of Ductile Iron

Inoculation of cast irons: practices and developments

MATERIAL SPECIFICATIONS CATALOGUE

CHROMIUM STEEL POWDERS FOR COMPONENTS. JEANETTE LEWENHAGEN Höganäs AB, Sweden

The mechanical properties of metal affected by heat treatment are:

Section 4: NiResist Iron

Development of a High Performance Nickel-Free P/M Steel. Bruce Lindsley. Senior Materials Engineer, Hoeganaes Corporation, Cinnaminson, NJ 08077, USA

Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications 1

Avoiding Shrinkage Defects and Maximizing Yield in Ductile Iron

Objectives/Introduction Extraction of zinc Physical properties of zinc Zinc casting alloys Wrought zinc alloys Engineering design with zinc alloys

Appendice Caratteristiche Dettagliate dei Materiali Utilizzati

North American Stainless

North American Stainless

North American Stainless

APPLYING DATA MINING METHODS TO PREDICT DEFECTS ON STEEL SURFACE

Aluminum Alloys. casting or a semisolid casting

HIGH STRENGTH DUCTILE IRON PRODUCED BY THE ENGINEERED COOLING: PROCESS CONCEPT

Technical Data BLUE SHEET. Martensitic. stainless steels. Types 410, 420, 425 Mod, and 440A GENERAL PROPERTIES APPLICATIONS PRODUCT FORM

Stainless steel grade chart

Standard Specification for Stainless Steel Bars and Shapes 1

North American Stainless

Durcomet 100 CD4MCuN. Bulletin A/7l

Crystal Structure of Aluminum, Zinc, and their Alloys By: Omar Fajardo Sebastian Henao Devin Baines ENGR45, F2014, SRJC

ASTM A860/A860M-09 Standard Specification for Wrought High Strength. Ferritic Steel Butt Welding Fittings. 1. Scope :- 2. Reference Documents :-

DIN STEEL PIPES FOR PIPE LINES FOR THE TRANSPORT OF COMBUSTIBLE FLUIDS AND GASES

Material data sheet. EOS Aluminium AlSi10Mg. Description

EFFECT OF COPPER ALLOY ADDITION METHOD ON THE DIMENSIONAL RESPONSE OF SINTERED FE-CU-C STEELS

EXTRACTION OF METALS

Rely on Our Material Competence for Your Demanding Industrial Processes

FEATURES AND BENEFITS OF DIFFERENT PLATINUM ALLOYS. Kris Vaithinathan and Richard Lanam Engelhard Corporation

Chapter 2 Fractal Analysis in CNC End Milling

Improved Broaching Steel Technology

X15TN TM. A high hardness, corrosion and fatigue resistance martensitic grade CONTINUOUS INNOVATION RESEARCH SERVICE.

Material Expansion Coefficients

Standard Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes 1

Chemical Proportions in Compounds

B) atomic number C) both the solid and the liquid phase D) Au C) Sn, Si, C A) metal C) O, S, Se C) In D) tin D) methane D) bismuth B) Group 2 metal

Using the PDF for material identification using elemental data. from XRF and SEM EDS.

GENERAL PROPERTIES //////////////////////////////////////////////////////

WEIGHTS AND MASS STANDARDS

Heat Treatment of Steels : Spheroidize annealing. Heat Treatment of Steels : Normalizing

Module 3 Machinability. Version 2 ME, IIT Kharagpur

ALLOY 2205 DATA SHEET

BUMAX. REYHER your partner for the BUMAX range

North American Stainless

AUSTENITIC STAINLESS DAMASCENE STEEL

3. What would you predict for the intensity and binding energy for the 3p orbital for that of sulfur?

Materials Standards for Metal Injection Molded Parts

THREE MAIN SOLIDIFICATION REACTIONS OF VANADIUM MODIFIED T1 TUNGSTEN HIGH SPEED TOOL STEEL. Hossam Halfa

SAND CAST CHILL CAST LM4 - TF

Anodes and Misc Equipment

CORRELATION BETWEEN HARDNESS AND TENSILE PROPERTIES IN ULTRA-HIGH STRENGTH DUAL PHASE STEELS SHORT COMMUNICATION

ARMSTRONG MOLD GRAPHITE DIE CASTING DIVISION

PART 6 SPECIAL CONTRACT RULES FOR METALS CONTENTS

APPENDIX B: EXERCISES

SUS. Company Profile. Ulrich Nell, Feldstr.23, D Oberhausen, Tel. 0049(0)208/ Fax 0049(0)208/658536

Massachusetts Institute of Technology Department of Mechanical Engineering Cambridge, MA 02139

Evaluation of the Susceptibility of Simulated Welds In HSLA-100 and HY-100 Steels to Hydrogen Induced Cracking

Politecnico di Torino. Porto Institutional Repository

WJM Technologies excellence in material joining

Think precision, Think HSS REAMING

9.11 Upon heating a lead-tin alloy of composition 30 wt% Sn-70 wt% Pb from 150 C and utilizing Figure

Aluminium as Construction Material in Ammonia Refrigeration Cycles

Introduction to Materials Science, Chapter 9, Phase Diagrams. Phase Diagrams. University of Tennessee, Dept. of Materials Science and Engineering 1

INFLUENCE OF Cr, Mn AND Mo ON STRUCTURE AND PROPERTIES OF V MICROALLOYED MEDIUM CARBON FORGING STEELS

Ablation of Hybrid Metal Matrix Composites

S355 European Standard Steel

Material data sheet. EOS StainlessSteel GP1 for EOSINT M 270. Description, application

Casting Process Simulation of Compacted Graphite Iron (03-025)

Development of Zinc Die Casting Alloys with Improved Fluidity Progress in Thin Section Zinc Die Casting Technology

Full Density Properties of Low Alloy Steels

North American Stainless

Safety Data Sheet Aluminium profiles Apply for alloys Sapa EN AW 6060, 6063, 6005, 6005A, 6082, yellow chromated, with or without powder coating.

ALLOY 7475 PLATE AND SHEET HIGHEST TOUGHNESS/STRENGTH

Theory of Heating by Induction

High-Strength Low-Alloy Steels

Development of a manufacturing technology of compacted graphite iron castings from a cupola furnace

Analysis and Optimization of Investment Castings to Reduce Defects and Increase Yield

THE POSSIBILITIES OF RUNNER PLACEMENTS FOR CASTINGS PRODUCED BY SPIN CASTING INTO SILICON RUBBER MOULDS. Matej BEZNÁK, Martin BAJČIČÁK, Roland ŠUBA

Multicrystalline solar silicon production for development of photovoltaic industry

Start the Design Study!

Effect of Heat Treatment on Microstructure and Mechanical Properties of SAE 1025 Steel: Analysis by one-way ANOVA

ALLOY 6022 SHEET. Higher Strength with Improved Formability SUPPLYING THE WORLD S BEST

THE MICROSTRUCTURE AND PROPERTIES OF HOT PRESSED IRON BRONZE POWDERS. BOROWIECKA-JAMROZEK Joanna

Iron Alloys. Iron castings are produced by a variety

The atomic packing factor is defined as the ratio of sphere volume to the total unit cell volume, or APF = V S V C. = 2(sphere volume) = 2 = V C = 4R

SALT SPRAY AND IMMERSION CORROSION TESTING OF PM STAINLESS STEEL MATERIALS. W. Brian James Hoeganaes Corporation. Cinnaminson, NJ 08077

CENTRIFUGAL CASTING.

LABORATORY EXPERIMENTS TESTING OF MATERIALS

North American Stainless

North American Stainless

UNIT (2) ATOMS AND ELEMENTS

How to read your Oil Analysis Report

% Si Fe Cu Mn Mg Cr Zn Ti Others Others. Europe USA Spain France Germany G.B. Italy Sweden Switzerland Japan. ALMgSi H30

Drill Pipe Hard-facing

Effect of Small Additions of Boron on the Mechanical Properties and Hardenability of Sintered P/M Steels

Heat Treatment of Steel

STUDY OF SHIELDING GASES FOR MAG WELDING

Experiment: Heat Treatment - Quenching & Tempering

Transcription:

Materials Transactions, Vol. 44, No. 7 (2003) pp. 1419 to 1424 #2003 The Japan Institute of Metals Influence of Scrap on Microstructure and Mechanical Properties of Spheroidal Graphite Cast Iron Sadato Hiratsuka 1, Hiroshi Horie 1, Toshinori Kowata 1, Katsumi Koike 2 and Kazumichi Shimizu 3 1 Department of Materials Science and Technology, Faculty of Engineering, Iwate University, Morioka 020-8551, Japan 2 Industrial Research Institute of Tochigi Prof., Kanuma 322-0011, Japan 3 Department of Computer and Control Engineering, Oita National College of Technology, Oita 870-0152, Japan In this research, the spheroidal graphite cast iron melt was produced by using 7 kinds of steel scraps, the shredder scrap, the surface treated steel sheets, the magnetic steel sheets, the high strength steel and others. The influences of the steel scraps on microstructures and mechanical properties were studied. Zinc, chromium, antimony, nickel, aluminum and manganese were contained in the steel scraps respectively. Using the steel scrap of the used car (shredder scrap), zinc is contained in the iron castings. The antimony included in the magnetic steel sheet was found to be a powerful pearlite stabilizer. The tensile strength and the hardness of cast iron increased with the increasing pearlite percent. Also chromium included in the surface treated steel sheet and manganese in the high strength steel increase the pearlite in the matrix of cast iron. (Received November 21, 2002; Accepted May 8, 2003) Keywords: steel scrap, spheroidal graphite cast iron, microstructure, tensile strength, Brinell hardness 1. Introduction The production of iron and steel in Japan exceeded 100 million tons in 1973, and then the production of them has hardly increased. On the other hand, the proportion of electric furnace steel produced in Japan has grown by nearly 1% every year. The production of steel has reached 104 million tons in 1997. It is considered that steel scraps tend to increase year by year. scrap generated from machine parts, automobiles, construction materials and so forth. The consumption of surface treated steel sheets in the automobile industry has conspicuously increased. It is also the shredder scrap made from a used car. The consumption of magnetic steel sheets in the household electric product industry has also increased. The production of iron castings has continued to increase and the amount of steel scrap used has increased more. Accordingly hereafter, it is inevitable that these steel sheets will be used more and more in the iron casting industry. The main raw material for iron castings has recently changed from pig iron to steel scraps. In order to save materials and energy, the importance of steel scraps as a raw material for cast iron have been increasing in recent years. scraps containing alloy elements (Zn, Al, Cu, Cr, Pb, etc.), such as surface treated steel, high strength steel and other special steel, are particularly increasing. However, these types of steel scraps have many problems for use. In particular, a large amount of zinc produces the pinhole porosity in iron castings 1,2) and the addition of a small amount of lead in cast iron causes abnormality in graphite morphology. 3 6) Thereupon, in this research, for the purpose of determining the influences of steel scraps on the microstructure and mechanical properties (i.e., hardness, elongation and tensile strength), the following experiments were carried out. 2. Experimental Procedure A high frequency induction furnace with a 12 kw, 3 khz motor generator unit was utilized to prepare 5 kg of experimental cast iron melt. The chemical compositions of steel scraps used for these experiments are shown in Table 1. The 7 kinds of steel scrap were used as the experimental material. In order to make a commercial ductile iron (FCD450), high purity pig iron was used. Carburizer and pure silicon was also used to adjust the carbon and silicon contents and ferro manganese, ferro phosphorus and iron sulphide were used so that the contents of manganese, phosphorus and sulfur would be the same in every melt. The melt was superheated to 1803 K and then nodularising treatment was carried out in a crucible using 1.6 mass% of iron silicon (45%)-magnesium (8%) alloy. After the nodularising reaction subsided, the melt was post-inoculated with 0.4% ferro silicon (75% silicon) and poured in a CO 2 process sand mold at 1673 K. The size of specimen was 30 mm 250 mm. After the tensile test, the nodule count and the pearlite, ferrite, graphite and carbide contents and the nodularity of the tensile test specimens were measured with computerized image analyzer. 3. Results and Discussion 3.1 Chemical compositions of specimens The chemical compositions of typical specimens are shown in Table 2. An analysis of chemical compositions of specimens reveals that the content of trace elements lowered in the cast iron when the electrolytic iron is used as a raw material. Using the shredder scrap (A) or the surface treated steel sheets (C) (zinc coated steel sheets), zinc is contained in the cast iron. The yield rate of zinc is about 50%. During melting in furnace, 50% of zinc became a zinc oxide. Using another surface treated steel sheet scrap (B), the chromium content becomes higher. The magnetic steel scrap (D) enhances the aluminum and the antimony contents in cast iron, since some magnetic steel was treated by antimony or AlN to get a fine ferrite structure. The yield rate of aluminum is about 30%. The cast iron prepared with the carbon steel (E) or the high

1420 S. Hiratsuka, H. Horie, T. Kowata, K. Koike and K. Shimizu Table 1 Chemical composition of steel scraps and pig iron. (mass%) C Si Mn P S Cu Cr Ni Mo Sn Ti Al Pb Zn A,Shredder Scrap 0.014 0.037 0.102 0.014 0.001 0.008 0.019 0.017 0.006 0.001 0.018 0.023 0.003 0.635 B,Surface treated 0.041 0.08 0.22 0.026 0.008 0.020 0.059 0.030 0.030 0.001 0.001 0.035 0.003 0.00 steel C,Surface treated 0.01 0.01 0.14 0.009 0.007 0.015 0.035 0.024 0.004 0.002 0.015 0.034 0.003 42 56 steel g/mm 2 D,Magnetic 0.006 0.549 0.312 0.030 0.006 0.01 0.04 0.014 0.005 0.002 <0:001 0.275 0.002 0.001 E,Carbon 0.23 0.19 0.34 0.019 0.008 0.01 0.11 0.020 <0:001 0.001 <0:001 0.020 0.002 F,Carbon steel 0.086 0.208 0.521 0.017 0.003 <0:005 0.081 0.017 <0:005 0.010 0.002 0.023 <0:01 <0:005 scrap G,Electroly -tic iron 0.0022 <0:0005 0.0005 <0:005 0.0001 0.0013 <0:001 <0:001 <0:001 <0:001 0.000 0.008 <0:001 H,Pig iron 3.95 0.01 0.08 0.008 0.006 0.04 0.016 0.011 0.001 0.001 0.000 0.001 0.001 Table 2 Chemical composition of spheroidal graphite cast iron. (mass%) C Si Mn P S Cu Cr Zn Al Pb Ti Sn Sb Ni Mo Mg CE A,Shredder Scrap 3.53 2.62 0.32 0.044 0.008 0.01 0.019 0.023 0.002 0.002 0.015 0.001 0.000 0.009 0.002 0.037 4.35 B,Surface treated 3.66 2.77 0.44 0.087 0.008 0.01 0.060 0.000 0.020 0.002 0.002 0.001 0.000 0.011 0.002 0.043 4.54 steel C,Surface treated 3.65 2.64 0.32 0.043 0.008 0.02 0.032 0.042 0.021 0.001 0.011 0.002 0.000 0.015 0.004 0.040 4.45 steel D,Magnetic 3.74 3.08 0.55 0.077 0.007 0.01 0.040 0.000 0.083 0.003 0.003 0.002 0.020 0.007 0.002 0.052 4.71 E,Carbon 3.88 2.84 0.53 0.054 0.011 0.01 0.113 0.000 0.020 0.003 0.002 0.001 0.000 0.012 0.002 0.042 4.77 F,Carbon steel 3.89 2.88 0.74 0.057 0.014 0.01 0.085 0.000 0.023 0.004 0.002 0.008 0.000 0.017 0.005 0.046 4.78 scrap G,Electroly -tic iron 3.68 2.59 0.21 0.036 0.003 0.00 0.016 0.000 0.007 0.000 0.002 0.001 0.000 0.000 0.001 0.043 4.49 H,Pig iron 3.65 2.60 0.21 0.035 0.007 0.01 0.016 0.000 0.017 0.000 0.002 0.001 0.000 0.006 0.001 0.041 4.46 CE = C% + 0.31%Si 0.027%Mn + 0.33%P + 0.4%S strength carbon steel scrap (F) contains higher levels of chromium, manganese and tin. The yield rate of manganese and chromium is about 98% and 100% respectively. 3.2 Microstructure Observations Figure 1 shows the microstructures of cast iron specimens in Table 2. The base iron (H) without steel scrap exhibits well-formed spheroidal graphite and a nodule count of 160 counts/mm 2 with a matrix of 74% ferrite. Using the electrolytic iron, a typical Bulls-eye structure is formed. The shredder scrap and the surface treated steel sheets (zinc coated steel sheets) scrap deteriorated the morphology of spheroidal graphite. Nodule count is significantly dropped from 160 to 130 counts/mm 2, and the matrix of cast iron changes to about 31% ferrite, as illustrated in Fig. 1(A). The surface treated steel sheets and the carbon steel scraps increase the amount of pearlite. This is due to the high content of pearlite-stabilizing elements (chromium and manganese) in the material. 7,8) There is clear agreement that a chromium, tin and manganese addition to spheroidal

Influence of Scrap on Microstructure and Mechanical Properties of Spheroidal Graphite Cast Iron 1421 Fig. 1 Microstructure of specimens using steel scraps as a raw material. graphite cast iron promotes the stability of pearlite. Using the magnetic steel was sufficient to convert the structure of the predominantly ferrite base casting to 87% pearlite. Antimony included in the magnetic steel scrap exhibited a pronounced pearlite stabilizing influence. 9 11) As the antimony deteriorates the morphology of spheroidal graphite, the formation of aggregated graphite was observed at austenite shell boundary. The magnetic steel scrap also produced a few star-shaped graphite. The total nodule counts slightly increased to 178/ mm 2. 3.3 Tensile strength, elongation and hardness The effects of each steel scraps on the tensile strength were investigated on ductile iron specimens with CE4.3-4.85. As shown in Fig. 2, the tensile strength of the base iron (H) with CE 4.5 was 516 MPa. Tensile strength increases from 516 to 579 MPa with decreasing CE value from 4.5 to 4.3. Tensile strength of all specimens produced with steel scraps was generally higher than the strength of the base iron. For example, the strength of cast iron (CE 4.4) prepared with surface treated steel sheet scrap (B) was 629 MPa. In the case of the carbon steel scrap (F) and the magnetic steel sheet scrap (D) was 689 MPa and 695 MPa respectively. The increase in strength is a result of an increase in the amount of pearlite in the matrix. The effects of steel scraps on the elongation values of ductile iron are shown in Fig. 3. Elongation value of the base iron (H) increases from 16 to 24% with increasing CE value from 4.3 to 4.5. Elongation values of all specimens using steel scraps as a raw material were generally lower than the elongation of the base iron. For example, the elongation value of the specimen made of surface treated steel sheets (B) was 10.6% at CE 4.4. Using the magnetic steel sheet (D), the elongation values were in 4.1 5.3%. The elongation was reduced as a result of the increased amount of pearlite. The improved tensile strength and corresponding reductions in ductility produced by antimony in the magnetic steel sheet is readily understood in terms of its effect on microstructure. The effects of steel scraps on the hardness of ductile iron are shown in Fig. 4. Brinell hardness of the base iron (H) increased from 157HB to 187HB with decreasing CE values from 4.5 to 4.3. The Brinell hardness of every specimen prepared with steel scraps was generally higher than the hardness of the base iron. For example, the hardness of surface treated steel sheets (B) used was 197HB. In the case of the carbon steel scrap (F) and the magnetic steel sheet (D) was 229HB and 277HB respectively. Using the magnetic steel sheet (D), the amount of pearlite and the hardness were the highest in specimens. Figure 5 shows relation between the area fraction of pearlite values and Brinell hardness. The increase in hardness is a result of an increase in the amount of pearlite in the matrix.

1422 S. Hiratsuka, H. Horie, T. Kowata, K. Koike and K. Shimizu Fig. 2 Relation between tensile strength and carbon equivalent. Fig. 3 Relation between elongation values and carbon equivalent. Fig. 4 Relation between Brinell hardness and carbon equivalent. Fig. 5 Relation between area fraction of pearlite and Brinell hardness.

Influence of Scrap on Microstructure and Mechanical Properties of Spheroidal Graphite Cast Iron 1423 Elongation: ln ð%þ ¼5:02 0:013 HB RGð%Þ ¼ð t = n Þ100 ð2þ ð3þ Fig. 6 Relation between tensile strength, elongation values and Brinell hardness. Figure 6 shows relations between tensile strength, elongation values and Brinell hardness. A linear relationship between tensile strength and Brinell hardness was obtained. The elongation values deceased oppositely. The results can be expressed as: Tensile strength: (N/mm 2 ) ¼ 47:1 þ 2:7 HB ð1þ t : the standard tensile strength n : the actual tensile strength RG, 12) the reifegard, means the degree of normality. The concept of reifegrad is widely used for estimating the quality of flake graphite cast iron. According to this concept, quality is expressed by the comparison of the actual tensile strength with the standard tensile strength of the same carbon equivalent. Because the Brinell hardness properly expresses the state of matrix structure, the comparison of the actual tensile properties and standard properties for same Brinell hardness is considered to be reifegrad of spheroidal graphite cast iron. Most specimens are RG100% excepting the cast iron prepared with the magnetic steel sheet scrap. The antimony in the magnetic steel scrap deteriorates the morphology of spheroidal graphite. Therefore, tensile strength decreased in the same hardness due to morphological changes of spheroidal graphite. The quality of castings may be defined, in general, as the capability of the parts to meet the microstructure and mechanical properties specifications with maintaining a high level of consistency for these properties. The results, herein described and discussed, confirm the influence of the steel scrap as a law charge material on the quality of spheroidal graphite cast iron. Through extended laboratory tests, they demonstrate that variation in chemical composition that appear meaningless, at first sight, may have significant effect on the microstructure and the mechanical properties. When a materials property of cast iron is examined, it is important that the relation among tensile strength, elongation and hardness is clarified. Generally, the tensile strength increases with increasing the hardness value. A cast iron should be not hard from the machine processing side though the tensile strength should be high. From the experimental results, the tensile strength of all specimens was 450 MPa or more. The tensile strength, the elongation and the hardness are evaluated synthetically; the specimens are classified into three grades, FCD450, FCD500 and FCD600. In the case of the magnetic steel sheet (D) is classified into FCD600 and the carbon steel scrap (F) is classified into FCD500 according to a JIS standard. In consideration of material properties for iron castings to be demanded, it is important to understand the kind of scrap and the trace element of steel scrap. The stronger pearlite forming tendency of magnetic steel scrap based materials is due to the content of 0.2% antimony in the castings. Also the carbon steel scrap (high strength carbon steel) containing manganese and tin based materials are sufficient to favor pearlite formation. The results of this study supported the beneficial role of materials in the charge to stabilize the concentration of pearlite-promoting elements and, thus, to improve the consistency of characteristic of the pearlitic castings.

1424 S. Hiratsuka, H. Horie, T. Kowata, K. Koike and K. Shimizu 4. Conclusions Based on the results obtained in this study, the following conclusions may be reached. (1) The shredder scrap and zinc coated steel scrap deteriorated the morphology of spheroidal graphite, hence they lowered the tensile strength of cast iron in specimens. (2) The yield rate of zinc is about 50%. During melting in furnace, 50% of zinc became a zinc oxide. (3) The magnetic steel sheets containing antimony produced considerable pearlite and resulted in significant increases in tensile strength with corresponding reductions in ductility. (4) The carbon steel scrap and high strength steel scrap containing chromium, tin and manganese also produced considerable pearlite and resulted in significant increases in tensile strength. (5) There are the casting prepared with surface treated steel sheet scrap to correspond the Japanese JIS FCD450 standard and the casting prepared with magnetic steel sheets not satisfied in the specimens. It is important for a sound cast iron to understand the kind of scrap and the trace element of steel scrap. REFERENCES 1) A. Chida: Proceedings of AFS symposium (1980) 99. 2) K. H. Capers: Giesseri 63 (1973) 679. 3) H. Morrougt: AFS Trans. 60 (1952) 439. 4) C. K. Donoho: Modern Castings 46 (1964) 608. 5) E. N. Pan, C. N. Lin and H. S. Chiou: AFS Trans. 103 (1995) 265 273. 6) H. Nakae, T. Kanno and B. Y. Kim: Proceedings, 2nd AFC (1994) 1 10. 7) M. F. Nikolai, A. Javaid, M. P. Arvedson, C. Vaidyanathan and C. R. Loper. Jr.: AFS Trans. 102 (1994) 781 787. 8) M. Gagne: AFS Trans. 92 (1984) 387 393. 9) H. Horie: J. Japan Foundry Engineering 48 (1976) 629-634. 10) H. Morrougt: AFS Trans. 60 (1952) 439. 11) E. N. Pan and C. N. Lin: AFS Trans. 104 (1996) 845 858. 12) K. Ikawa: J. Japan Foundry Engineering 68 (1995) 883 890.