ÇOK KATMANLI AMBALAJ FİLMLERİ ve TEKNİK ÖZELLİKLERİ Muharrem DEMiR www.apack.com.tr
2 KATMANLI PA 30 microns PE 70 microns PA=Polyamide (substrate film) PA/PE 30/70 PE=Polyethylene (sealing layer) 5 KATMANLI PA HV EVOH HV PE = Polyamide = Tie layer = Gas barrier = Tie layer = Polyethylene 7 KATMANLI PE = Polyethylene HV = Tie layer PA = Polyamide EVOH = Gas barrier HV = Tie layer PA = Polyamide HV = Tie layer PE = Polyethylene Yukarıda gösterilen 5 ve 7 katmanlı filmler stadart coextrude filmlerdir. Bunlar Bloom veya Chill Roll yöntemleriyle üretilebilirler.
Çok Katmanlı Lamine Edilmiş Filmler PETP = Polyester Adhesive Aliminium foil Adhesive PE = Polyethylene Kalıpta çekilerek lamine edilen çok katmanlı kaplama filmler Kağıt (with primer) Bağlama Katmanı* = Ğolyethylene hamuru Aluminyum folyo, 9 mikron PE kaplama Surlyn kaplama Mono filmler gibi, çok katmanlı kombinasyonlar genellikle zemin veya kapak üretiminde kullanılır. PVC, PETP, PS, OPS, PAN, PP ya da PC gibi sert filmler ağırlıklı olarak monofilm üretiminde kullanılır. 100% e yakın esneklik derecesinde olan filmler ise çok katlı kombinasyonlarda kullanılmaktadır.
Coextrusion Blown film or cast film from a chill rol unit Lamination Adhesive or extrusion lamination Coating Extrusion coating or coextrusion coating Coating (solution/dispersion) HS lacquer, hotmelt, PVdC, Cold seal lacquer
Adhesive laminaation LAMİNASYON This line can also be used to produce combinations like PETP/Al/PE
Extrusion laminaation LAMİNASYON In this laminating process, PE in melt form is used as teh laminating agent.
KAPLAMA In the coating process, the PE is cast from the slot die onto the substrate material that is to be coated. The quality od teh combination is inferior to an adhesive laminate in every respect. Production is, however, less expensive
COEXTRUSION YÖNTEMİYLE KAPLAMA When low sealing temperatures are required to use a cheap PE as a basis and a thin Layer of expensive Surlyn as an agent that seals at low temperatures.
PP/EVOH/PP, PS/PE, PS/EVOH/PE, PS/PETP PA/PE, PE/PA/PE, PA/EVOH/PA/PE 20 to 2000 microns Coextrusion Chill Roll Süreci Coextrusion line for multilayer films from e.g. 500 to 1200 mic. (for sterilisable meal trays etc.) or flexible multilayer films made from PA, EVOH, PE, 100-300 micron
Only flexible multilayer films PA/PE, PE/PA/PE, PA/EVOH/PA/PE Combinations PA/EVOH/PA, PE/EVOH/PE Blown Film Coextrusion
Printing of Film Flexo Printing Gravure Printing Photocell point: register-printed Flexo printing has always been less expensive, particularly with runs of less than 50.000 metres. A further distinction is made between surface printing and reverse printing. Reverse printing is more common. Surface printing is only used for monofilms such as PVC and for multilayer films that have been coextruded, PA/PE. - Surface printing, where the ink is on the out side of the pack - Reverse printing is normally applied to an inner layer, so that it is protected against all external influences - The colours are also given greater depth when the printing is covered by the transparent outer layer of the film - In reverse printing the colour that is on top in the print motif is printed first and the white background is only added at the end.
Flexo Printing Printing of Film
Gravure Printing Printing of Film
MONOFİLMLERİN ÖZELLİKLERİ
MONOFİLMLERİN ÖZELLİKLERİ Water vapour transmission Gas barrier (O 2, CO 2 and N 2 ) Protection against aroma loss Light barrier Resistance of chamicals etc. Temperature resistance - Feezing - Pasteurisation (95 ºC) - Boiling - Sterilisation (121 ºC)
NEM GEÇİRGENLİĞİ Water vapour transmission is expressed in g/m2/24h with a difference in relative humidity of 85% to 0% Table comparing water vapour transmission; according to DIN 53122 (individual films) With a thickness of 40 mic 100 mic 500 mic PA 20 10 OPA 15 mic 20 Amorphous PETP 5 2 0,4 Oriented PETP 12 mic 5 PS 30 12 2,5 PVC 5,5 2,5 0,5 PP 1,5 0,5 0,1 OPP 20 mic 1 PE 2 1 Alu 12 mic 0 Cellulose film NC lacquer 35 gr 25 Cellulose film PVdC lacquer 35 gr 2,5
GAZ BARİYERİ (Co-extruded) Barrier Films Gas permeability is expressed in cm3/m2/bar/24h Table comparing Oxygen permeability; according to DIN 53380 (individual films) With a thickness of 40 mic 100 mic 500 mic PA 25 10 OPA 15 mic 30 Amorphous PETP 45 20 3,5 Oriented PETP 12 mic 80 PS 3000 1500 300 PVC 100 40 8 PP 1500 500 125 OPP 20 mic 1500 PE 3000 1500 300 Alu 12 mic 0 Cellulose film NC lacquer 35 gr 125 Cellulose film PVdC lacquer 35 gr 10
Development Priorities (Coated) Barrier Films Another way of achieving a barrier effect is by coating films with certain barrier materials. The following techniques are used to achieve this: Metalization Coating / vaporizing with inorganic materials (such as SiOX or Al2O3) Plasma polymerization Coating with PVDC Coating with organic-inorganic hybrid polymers Furthermore, NORDENIA TECHNOLOGIES GmbH has developed a barrier coating based on PVOH. It has an excellent aroma and oxygen barrier (O2 permeability at 23 C and 50 % relative humidity: 1-1.5 cm³/m²*24h*bar). PVOH contains (in contrast to PVDC) no chlorine. The coating is highly transparent, is printable and can be laminated, so that it may also be used in laminate composites. This coating, which is expensive compared to other barrier materials, was primarily developed for niche and special applications, as it can be applied, for example, to the whole surface or as a printed pattern that repeats itself.
Material Choice Before choosing a package for a product one must consider a number of factors: Product protection Oxidation Moisture gain or loss Aromatic gain or loss fat penetration Light Product influence Mechanical protection Information requirements Packaging machines Consumer demands Costs Acidic or fat products Aromatic oils Detergents Shock absorption Freeze or heat resistance Moisture resistance Handling endurance Print quality Print scope Company colours Fit chain material-machine-product capacity Manpower Easy opening, re-closing Handling endurance Shelf adaptation Environment Per unit Totally, with transport, etc.