Aerospace series Aluminium alloy AL-P7175- Al Zn5,5MgCu(B) - T73511 Extruded bar and section a or D 150 mm

Transcription

1 AECMA STANDARD NORME AECMA AECMA NORM pren 4293 Edition P 2 July 2010 PUBLISHED BY THE EUROPEAN ASSOCIATION OF AEROSPACE INDUSTRIES (AECMA) Gulledelle 94 B-1200 BRUXELLES Tel. (+32) Fax. (+32) ICS: Descriptors: ENGLISH VERSION Aerospace series Aluminium alloy AL-P7175- Al Zn5,5MgCu(B) Extruded bar and section a or D 150 mm Série aérospatiale Alliage d'aluminium AL-P7175- Al Zn5,5MgCu(B) Barres et profilés filés a ou D 150 mm Luft- und Raumfahrt Aluminiumlegierung AL-P7175- Al Zn5,5MgCu(B) Stranggepreβte Stangen und Profile a oder D 150 mm This "Aerospace Series" Prestandard has been drawn up under the responsibility of AECMA (The European Association of Aerospace Industries). It is published on green paper for the needs of AECMA-Members. It has been technically approved by the experts of the concerned Technical Committee following comment by the Member countries. Subsequent to the publication of this Prestandard, the technical content shall not be changed to an extent that interchangeability is affected, physically or functionally, without re-identification of the standard. After examination and signature of the AECMA Standard Checking Centre (NPS) and formal agreement of the Official Services of the Member countries it will be submitted as a draft European Standard to CEN (European Committee for Standardization) for formal vote.

2 Page 2 Blank page

3 Page 3 0 Introduction This standard is part of the series of EN metallic material standards for aerospace applications. The general organization of this series is described in EN This standard has been prepared in accordance with EN Scope This standard specifies the requirements relating to: for aerospace applications. Aluminium alloy AL-P7175- Al Zn5,5MgCu(B) Extruded bar and section a or D 150 mm 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 2043 EN EN 4258 EN Aerospace series - Metallic materials - General requirements for semi-finished product qualification (excluding forgings and castings) 1) Aerospace series - Aluminium and aluminium alloy wrought products - Technical Specification - Part 3: Bar and section Aerospace series - Metallic materials - General organization of standardization - Links between types of EN standards and their use 1) Aerospace series - Metallic materials - Rules for drafting and presentation of material standards - Part 2: Specific rules for aluminium, aluminium alloys and magnesium alloys 1) 1) Published as AECMA Prestandard at the date of publication of this standard

4 Page 4 1 Material designation Aluminium alloy AL-P7175- Al Zn5,5MgCu(B) 2 Chemical Element Si Fe Cu Mn Mg Cr Zn Ti Others Al Each Total composition min. 1,2 2,1 0,18 5,1 % max. 0,15 0,20 2,0 0,10 2,9 0,28 6,1 0,10 0,05 0,15 3 Method of melting 4.1 Form Bar and section 4.2 Method of production Extruded 4.3 Limit dimension(s) mm a or D Technical specification EN Base 6.1 Delivery condition T73511 Heat treatment 455 C θ 475 C / WQ θ 40 C + 1 % controlled stretched 3 % + minor straightening C θ 125 C / 6 h t 24 h C θ 182 C / 6 h t 16 h 6.2 Delivery condition code U 7 Use condition T73511 Heat treatment Delivery condition Characteristics 8.1 Test sample(s) See EN Test piece(s) See EN Heat treatment Use condition 9 Dimensions concerned mm a or D < a or D < a or D < a or D < a or D < a or D Thickness of cladding on each face % 11 Direction of test piece L L L L L L 12 Temperature θ C Ambient Ambient Ambient Ambient Ambient Ambient 13 Proof stress R p 0,2 MPa T Strength R m MPa Elongation A % 8 1) Reduction of area Z % 17 Hardness 18 Shear strength R c MPa 19 Bending k 20 Impact strength 21 Temperature θ C 22 Time h 23 Stress σ a MPa 24 C Elongation a % 25 Rupture stress σ R MPa 26 Elongation at rupture A % 27 Notes (see line 98) 1)

5 Page 5 32 Electrical conductivity See EN Measurement on the surface of the sample from which tensile specimens are taken. 7 γ 23 MS/m Acceptable 22 MS/m γ < 23 MS/m Acceptable if Rp0,2 L Rp0,2 min. L + 85 MPa or if stress corrosion test acceptable γ < 22 MS/m Non acceptable 39 Stress corrosion See EN For qualification 3 a or D > 25 mm 6 σ = 70 % R p0,2 min. L 7 t = 20 days 40 Fracture toughness See EN (K IC ) 7 Dimensions (mm) For qualification 40 a or D External defects See EN T - L MPa m 51 Macrostructure See EN Internal defects See EN Batch uniformity See EN Electrical conductivity or T73511 Hardness γ MS/m See EN HB 140 (typical value) δ 20 per product 95 marking inspection See EN Δ 30 per batch 96 Dimensional inspection See EN Notes 1) or A 50mm 7% 99 Typical use

6 Page Product qualification See EN Qualification programme to be agreed between manufacturer and purchaser.