UDDEHOLM IMPAX SUPREME

UDDEHOLM IMPAX SUPREME

Uddeholm Impax Supreme is a premium prehardened mould steel with very good polishing and texturing properties. Uddeholm Impax Supreme is available in a very wide dimensional range, where even the largest dimensions show a very uniform hardness profile all through the cross section. The delivery hardness of ~310 HB, makes the steel suitable for a many different applications like: Moulds for plastic injection moulding Moulds for blow moulding Dies for plastic extrusion General constructional parts, like machine components requiring improved fatigue strength and reliability This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty of specific properties of the products described or a warranty for fitness for a particular purpose. Classified according to EU Directive 1999/45/EC For further information see our Material Safety Data Sheets. Edition 7, 09.2011 The latest revised edition of this brochure is the English version, which is always published on our web site www.uddeholm.com SS-EN ISO 9001 SS-EN ISO 14001

General Uddeholm Impax Supreme is a premiumquality vacuum-degassed Cr-Ni-Mo-alloyed steel which is supplied in the hardened and tempered condition, offering the following benefits: No hardening risks No hardening costs Time saving, e.g. no waiting for heat treatment Lower tool cost (e.g. no distortion to rectify) Modifications easily carried out Can be subsequently nitrided to increase surface wear resistance or locally flame hardened to reduce surface damage Uddeholm Impax Supreme is manufactured to consistently high quality standards with a very low sulphur content, giving a steel with the following characteristics: Good polishing and photo-etching properties Good machinability High purity and good homogeneity Uniform hardness Note: Uddeholm Impax Supreme is 100% ultrasonic tested. Heavier sections are supplied premachined which offers the following advantages compared with un-machined material: Saving of weight Non-decarburized surface Exact nominal size (plus tolerance) Less machining Absence of scale minimizes machine and tool wear Approx. analysis % Standard spec. Delivery condition Colour code AISI P20 modified Applications C Si Mn Cr Ni Mo 0.37 0.3 1.4 2.0 1.0 0.2 Hardened and tempered to 290 330 HB Yellow/green Injection moulds for thermoplastics Extrusion dies for thermoplastics Blow moulds Forming tools, press-brake dies (possibly flame hardened or nitrided) Aluminium die casting prototype dies Structural components, shafts Properties Physical data Hardened and tempered to 310 HB. Temperature 20 C 200 C (68 F) (390 F) Density, kg/m 3 7 800 7 750 lbs/in 3 0.282 0.280 Coefficient of thermal expansion per C from 20 12.7 x 10-6 per F from 68 F 7.0 x 10-6 Thermal conductivity W/m C 28 Btu in/ft 2 h F 194 Modulus of elasticity N/mm 2 205 000 200 000 tsi 13 280 12 960 psi 29.7 x 10 6 29.0 x 10 6 Specific heat capacity J/kg C 460 Btu/lb F 0.110 Mechanical properties Impact strength, tensile strength and the compressive strength depends on the hardness in the delivered condition. IMPACT STRENGTH The energy absorption at impact testing depends on the test material (bar size and delivered hardness), testing temperature and the specimen (type, location, and orientation in the bar). The graph below shows how the impact energy changes as a function of the test temperature and hardness variation within the delivery hardness range. Impact energy, J (Charpy V) 100 90 80 70 60 50 40 30 20 10 0 100 50 0 50 100 150 C 148 58 32 122 212 302 F Temperature 3

TENSILE STRENGTH Approx. values. Samples were taken from a flat bar, 90 x 300 mm (3.5" x 11.8"). Hardness: 325 HB. Testing temperature 20 C 200 C (68 F) (390 F) Ultimate tensile strength Rm N/mm 2 1020 930 Yield strength Rp0.2 N/mm 2 900 800 COMPRESSIVE STRENGTH Compressive yield strength Rc0.2 N/mm 2 850 1000 Heat treatment Uddeholm Impax Supreme is intended for use in the hardened and tempered condition, i.e. the delivery condition. When, however, the steel is to be heat treated to a higher hardness or case hardened, the following instructions may be helpful. Quenching media High speed gas/circulating atmosphere (Only suitable for small dimensions) Oil (60 80 C/140 175 F) Martempering bath 300 C (570 F) max. 4 minutes, then air Note: Temper immediately tool reaches 50 70 C (120 160 F). Tempering Choose the tempering temperature according to the hardness required by reference to the tempering graph. Temper twice with intermediate cooling to room temperature. Lowest tempering temperature 180 C (360 F) for small inserts, but preferred minimum is 250 C (480 F). Holding time at temperature minimum 2 hours. TEMPERING GRAPH The diagram is valid for small samples 15 x 15 x 40 mm (0.6 x 0.6 x 1.6 in.) austenitized 30 min. at 850 C (1560 F), quenched in air and tempered 2 + 2 hours. Soft annealing Protect the steel and heat through to 700 C (1300 F). Then cool in the furnace at 10 C (50 F) per hour to 600 C (1110 F), then freely in air. Stress relieving After rough machining the tool should be heated through to 550 C (1020 F), holding time 2 hours. Cool slowly to room temperature. Hardness HRC 55 50 45 40 35 30 HB 600 550 500 450 400 350 300 250 200 100 200 300 400 500 600 700 C 210 390 570 750 930 1110 1290 F Tempering temperature Hardening Note: The steel should be fully soft annealed before hardening. Preheating temperature: 500 600 C (930 1110 F). Austenitizing temperature: 850 C (1560 F). The steel should be heated through to the austenitizing temperature and held at temperature for 30 minutes. Flame and induction hardening Uddeholm Impax Supreme can be flame or induction hardened to a hardness of approx. 50 HRC. Cooling in air is preferable. Further information can be obtained from the Uddeholm Technical Services Report Flame hardening of Uddeholm Impax Supreme. Protect the tool against decarburization and oxidation during the hardening process. 4

Nitriding and nitrocarburizing Nitriding gives a hard surface which is very resistant to wear and erosion. A nitrided surface also increases the corrosion resistance. For best result the following steps should be followed: 1. Rough machining 2. Stress tempering at 550 C (1020 F) 3. Grinding 4. Nitriding Following surface hardness and nitriding depths will be achieved after nitriding: The cutting data below are to be considered as guiding values which must be adapted to existing local conditions. More information can be found in our technical information Cutting data recommendations. Temperature Surface Depth of case Time hardness C F h HV 1 mm inch Gas 525 977 20 650 0.30 0.012 nitriding 525 977 30 650 0.35 0.013 Ion- 480 896 24 700 0.30 0.012 nitriding 480 896 48 700 0.40 0.016 Nitrocarburizing 570 1058 2 700 0.10 0.004 Cutting data recommendations Turning Turning Turning with carbide with high speed steel Cutting data Rough Fine Fine parameters turning turning turning Cutting speed, (v c ) m/min 120 170 170 220 15 20 f.p.m. 394 558 558 722 49 66 Feed, (f) mm/r 0.2 0.4 0.05 0.2 0.05 0.3 i.p.r. 0.008 0.016 0.002 0.008 0.002 0.012 Depth of cut, (a p ) mm 2 4 0.5 2 0.5 3 inch 0.08 0.16 0.02 0.08 0.02 0.12 Drilling HIGH SPEED STEEL TWIST DRILL Drill diameter Cutting speed, (v c ) Feed, (f) mm inch m/min f.p.m. mm/r i.p.r. 5 3/16 14 16* 46 52 0.08 0.15 0.003 0.006 5 10 3/16 3/8 14 16* 46 52 0.15 0.25 0.006 0.010 10 15 3/8 5/8 14 16* 46 52 0.25 0.30 0.010 0.012 15 20 5/8 3/4 14 16* 46 52 0.30 0.35 0.012 0.014 * For coated high speed steel drill v c = 24 26 m/min (79 85 f.p.m.) CARBIDE DRILL Milling Type of drill Cutting data Indexable Solid Carbide parameters insert carbide tip 1) Cutting speed, (v c ) m/min 180 200 120 150 60 80 f.p.m. 600 656 394 492 197 262 Feed, (f) mm/r 0.05 0.15 2) 0.08 0.20 3) 0.15 0.25 4) i.p.r. 0.002 0.006 2) 0.003 0.008 3) 0.006 0.01 4) 1) Drill with replaceable or brazed carbide tip 2) Feed rate for drill diameter 20 40 mm (0.8 1.6 ) 3) Feed rate for drill diameter 5 20 mm (0.2 0.8 ) 4) Feed rate for drill diameter 10 20 mm (0.4 0.8 ) FACE AND SQUARE SHOULDER MILLING Cutting data Milling with carbide parameters Rough milling Fine milling Cutting speed, (v c ) m/min 80 150 150 190 f.p.m. 265 492 492 623 Feed, (f z ) mm/tooth 0.2 0.4 0.1 0.2 inch/tooth 0.008 0.016 0.004 0.008 Depth of cut, (a p ) mm 2 4 2 inch 0.08 0.16 0.08 Carbide designation ISO P20 P40 P10 P20 Coated Coated carbide carbide or Cermet Carbide designation, ISO P20 P30 P10 Coated Coated carbide carbide or Cermet 5

END MILLING Milling cutter Carbide Cutting data Solid indexable High speed parameters carbide insert steel Cutting speed, (v c ) m/min 70 110 80 120 15 20 1) f.p.m. 230 361 262 394 49 66 1) Feed, (f z ) mm/tooth 0.03 0.20 2) 0.08 0.20 2) 0.05 0.35 2) inch/tooth 0.001 0.008 2) 0.003 0.008 2) 0.002 0.014 2) Carbide designation, ISO P20 P40 1) For coated high speed steel end mill v c = 35 40 m/min (115 131 f.p.m.) 2) Depending on radial depth of cut and cutter diameter Grinding A general grinding wheel recommendation is given below. More information can be found in the Uddeholm brochure Grinding of Tool Steel. Type of grinding Face grinding straight wheel Face grinding segments Cylindrical grinding Internal grinding Profile grinding Welding Wheel recommendation A 46 HV A 24 GV A 60 KV A 46 JV A 100 KV Good results when welding tool steel can be achieved if proper precautions are taken during welding (elevated working temperature, joint prep-aration, choice of consumables and welding procedure). If the tool is to be polished or photo-etched, it is necessary to work with an electrode type of matching composition. Welding method TIG MMA (SMAW) Working 200 250 C 200 250 C temperature (390 480 F) (390 480 F) IMPAX Consumables TIG-WELD IMPAX WELD Hardness after welding 300 330 HB 300 330 HB Further information is given in the Uddeholm brochures Welding of Tool Steel and Uddeholm Impax Weld/TIG-Weld. Electrical-discharge machining If spark-erosion, EDM, is performed in the as delivered condition, the tool should then be given an additional temper at approx. 550 C (1020 F). If the steel has been rehardened, the additional tempering temperature should be 25 C (50 F) lower than the last tempering temperature used. Further information can be obtained from the Uddeholm brochure EDM of tool steel. Hard-chromium-plating After hard-chromium-plating, the tool should be tempered for approx. 4 hours at 180 C (350 F) within 4 hours of plating in order to avoid hydrogen embrittlement. Photo-etching Uddeholm Impax Supreme is particularly suitable for texturing by the photo-etching process. Its very low sulphur content ensures accurate and consistent pattern reproduction. For heavy sections an extra tempering at 550 C (1020 F) before photo-etching is recommended. Polishing Uddeholm Impax Supreme has good polishability in the hardened and tempered condition. After grinding, polishing is undertaken with aluminium oxide or diamond paste. Note: Each steel grade has an optimum polishing time which largely depends on hardness and polishing technique. Overpolishing can lead to a poor surface finish (e.g. an orange peel effect). Further information is given in the Uddeholm publication Polishing of mould steel. Further information Contact your local Uddeholm office for further information on the selection, heat treatment, application and availability of Uddeholm tool steels, including the publication Steels for moulds. 6

Network of excellence UDDEHOLM is present on every continent. This ensures you high-quality Swedish tool steel and local support wherever you are. ASSAB is our wholly-owned subsidiary and exclusive sales channel, representing Uddeholm in the Asia Pacific area. Together we secure our position as the world s leading supplier of tooling materials. www.assab.com www.uddeholm.com

UDDEHOLM 110902.200 / TRYCKERI KNAPPEN, KARLSTAD 201109254 UDDEHOLM is the world s leading supplier of tooling materials. This is a position we have reached by improving our customers everyday business. Long tradition combined with research and product development equips Uddeholm to solve any tooling problem that may arise. It is a challenging process, but the goal is clear to be your number one partner and tool steel provider. Our presence on every continent guarantees you the same high quality wherever you are. ASSAB is our wholly-owned subsidiary and exclusive sales channel, representing Uddeholm in the Asia Pacific area. Together we secure our position as the world s leading supplier of tooling materials. We act worldwide, so there is always an Uddeholm or ASSAB representative close at hand to give local advice and support. For us it is all a matter of trust in long-term partnerships as well as in developing new products. Trust is something you earn, every day. For more information, please visit www.uddeholm.com, www.assab.com or your local website.