TEROSON MS Series. Elastic Sealing, Bonding and Coating for Industrial Applications

Transcription

1 Elastic Sealing, Bonding and Coating for Industrial Applications

2 Elastic Sealing, Bonding and Coating Solutions Excellent weathering and aging resistant adhesives, specifically engineered to withstand high mechanical stress in elastic bonding applications. The use of TEROSON MS elastic sealing, bonding and coating solutions opens up new applications as they satisfy high modern design and cost- efficiency demands. These reliable adhesives can be applied in many different areas of industrial manufacturing and assembly. The TEROSON MS line is based on silane-modified polymers (SMP). Products incorporating this technology are moisture-curing and react to form high-performance elastomers. They contain a built-in adhesion promoter (primer). This gives an extremely broad adhesion spectrum, making them compatible with different substrates in many cases they can be applied without an additional primer. Benefits > > Primerless adhesion > > Wide application spectrum > > Broad range (sealants, adhesives, coatings) for standard and tailor-made solutions > > High quality grades TEROSON MS Solutions Product Features > > Solvent-free > > Good ageing properties > > High UV and weather stability > > Wide adhesion spectrum on metals, paints, plastics and mineral substrates > > Low shrinkage during curing > > Elastic behaviour > > Flame retardant (special formulations) AUTOMoTIVE INDUSRTY > > Passenger cars > > Buses & coaches > > Trucks > > Sub-suppliers Elastic Sealing Elastic Bonding Elastic Coating Definition Elastic, adherent, thixotropic or self leveling sealing of seams, cross joints, overlap joints, connecting joints for indoor and outdoor applications Application Areas > > Sealing of seams, sheet metal overlaps and border joints in metal, plastic, silo and container construction > > Sealing of flanged joints > > Cars, vans and buses Advantages > > Elastic > > Wide, primerless adhesion on many substrates > > Fast curing > > Low volume shrinkage during curing > > Mould resistant > > Easy processing > > Good UV and weather resistance > > Thixotropic or self leveling Bonding of materials with same or different elongation coefficients. Possible tensions can be compensated by TEROSON MS products which also absorb oscillations and vibrations > > Bonding of planking, lining, sheet plates > > Fixing of plastic or metal ledges, plates or structural elements on housings > > Bonding of sandwich and insulation plates > > Bonding of photovoltaic modules > > Bonding of profiles for wind craft generators > > Elastic > > Wide, primerless adhesion on many substrates > > Fast curing > > Low volume shrinkage during curing > > Easy processing > > Good UV and weather resistance > > No contact corrosion > > Replacement of screws and welding wires Elastic and resilient coating for surface protection > > Protective coating on metals (aluminium, steel, others), ceramics, foam glass and plastics > > Container design and repair > > Corrosion protection of riveted joints or screw joints > > Car repair > > Elastic > > Wide, primerless adhesion on many substrates > > Fast curing > > Low volume shrinkage during curing > > Easy processing > > Good UV and weather resistance > > High impact strength

3 TEROSON MS Product Range Product Application Area Color Consistency Density [g/cm 3 ] Hardness Shore A [ISO 868, Durometer A] Teroson MS 500 Bonding White, Black Pasty, high holding force Teroson MS 9360 Bonding Black Pasty, Thixotropic 1.4 > 50 Teroson MS 937 Bonding White, Grey, Black Pasty, Thixotropic Teroson MS 939 Bonding White, Off-White, Grey, Black Pasty, Thixotropic Teroson MS 939 FR Bonding Black Pasty, Thixotropic 1.45 > 50 Teroson MS 9399 *) Bonding White, Black Pasty, Thixotropic Teroson MS 9320 UBC Coating, Sealing Black Sprayable, non-sagging Teroson MS 931 Coating, Sealing White, Grey, Black Self Leveling Teroson MS 930 Sealing White, Grey, Black Pasty, Thixotropic Teroson MS 9304 Sealing Grey, Anthracite Pasty, Thixotropic Teroson MS 9307 LD Sealing Grey Pasty, Thixotropic Teroson MS Sealing Transparent Pasty, Thixotropic Teroson MS 935 Sealing White, Grey, Black Pasty, Thixotropic Teroson MS 222 Sealing Beige Pasty, low viscous Teroson MS 9320 SF Sealing Grey, Ochre, Black Pasty, low viscous *) 2 c adhesive **) not practicable as 2 c ***) unopened original packaging Processing Equipment Specialised application guns from Henkel Softpress Gun 570 > > For 1 c adhesives > > Pneumatic aluminium gun > > For all 310 ml cartridges and 600 ml foil packs Telescopic Multi-Press Gun > > For 1 c adhesives > > Pneumatic plastic gun with telescope mechanism > > For bead application and spraying > > For all 310 ml aluminium and plastic cartridges Cox Gun VBA-200 A > > For 2 c adhesives > > Double chamber pneumatic plastic gun (mixing ratio 1:1) > > For all 400 ml plastic cartridges

4 Cure Rate in [mm/24h] Skin Formation time in [min] Tensile Strength (ISO 37) in [MPa] Elongation at Break (ISO 37) in [%] Service Temperature Range in [ C] Shelf Life *** in [month] up to up to up to up to up to ** 30 (Black) 20 (White) up to up to up to up to up to up to up to up to > up to up to Customised equipment alternatives for pails and drums MM15 Meter Mix Dispensing System > > For 1 or 2 c adhesives > > For bead application and spraying > > For manual or automatic applications > > For 20 L pails or 200 L drums

5 TEROSON MS Series Curing Mechanism of TEROSON MS Adhesives TEROSON MS adhesives are available as pastes with varying degrees of viscosity. They cross-link via a chemical reaction to form a rubber-elastic final product. The factors involved in this chemical reaction are important parameters for the speed of cross-linking. Elastic TEROSON MS adhesives fall into two categories: 1 c TEROSON MS Adhesives > > Cross-linking to form a rubber-elastic final product is triggered by the penetration of water in the form of atmospheric moisture > > Curing speed depends on the level of humidity in the air, the temperature and the size of the contact area > > Preferably used in designs where the bond line is neither too deep nor wide and there is a relatively large surface area exposed to atmospheric moisture 2 c TEROSON MS Adhesives > > Cross-linking to form a rubber-elastic final product takes place independently of atmospheric moisture and begins immediately after component B has been thoroughly mixed with component A > > Curing time does not depend on atmospheric moisture and progresses > > Significantly higher bond strengths after short reaction times > > Suitable for designs with little or no contact with atmospheric moisture, or where the application calls for highly fast and reliable processing Sustainability: Primerless adhesion on most industrial substrates; solvent-free Cost Efficiency: Wide application spectrum; application in many cases without primer Process Optimisation: Various processing equipment is available

6 Europe Germany Henkel AG & Co. KGaA (Headquarters) Henkelstraße Düsseldorf Germany Phone: (+49) Asia-Pacific China Henkel (China) Co. Ltd. No. 928 Zhang Heng Road Pu Dong Shanghai China Phone: (+86) Japan Henkel Japan Ltd. Asia Pacific Technical Center 27-7, Shin Isogo-cho Isogo-ku, Yokohama Japan Phone: (+81) Americas U.S.A. Henkel Corporation Madison Heights Stephenson Highway Madison Heights, MI United States Phone: (+1) Brazil Henkel Itapevi Avenida Professor Vernon Krieble, 91 CEP: Itapevi - SP Brazil Phone: (+55) México Henkel Mexicana, S.A. de C.V. Boulevard Magnocentro No. 8 Piso 2 Centro Urbano Interlomas Huixquilucan, Estado de México México Phone: (+52) The data contained herein are intended as reference only. Please contact Henkel AG & Co. KGaA for assistance and recommendation on specifi cations for these products. designates a trademark of Henkel AG & Co. KGaA or its affiliates, registered in Germany and elsewhere Henkel AG & Co. KGaA, 2013 AT